Compare Tool

Vs.
remove

PC-3®

XTC-3D™ vs. EZ-Spray® Silicone 22 vs. PC-3®EZ-Spray® Silicone 22

Laboratory Tabletop Epoxy Adhesive

 View Product

Vs.
remove

XTC-3D™

XTC-3D™ vs. EZ-Spray® Silicone 22 vs. PC-3®EZ-Spray® Silicone 22 versus PC-3®

High Performance 3D Print Coating

 View Product

Add Material to Compare

start over

Key Differences

Product Type
  • Silicone Rubber - Platinum Cure
  • Adhesives
  • Epoxy and Urethane Coatings
Mixed Viscosity11,000 cpsPaste350 cps
Barcol 935 Hardness75
Shore D Hardness80
Shore A Hardness22
Specific Volume25.6 cu. in./lb.20 cu. in./lb.25.1 cu. in./lb.
ColorTranslucent GreenBlackClear (Slightly Yellow In Thick Sections)
Disclaimer
Although we do our best to ensure the accuracy of this Compare Tool, Smooth-On offers no warranty either expressed or implied as to the reliability of the information contained herein. Smooth-On assumes no liability for loss or damage associated with use of the Compare Tool. If this is a critical project, we encourage you to review all of the technical data below and contact our Technical Service department with any questions or concerns.

All Technical Data

EZ-Spray® Silicone 22PC-3®XTC-3D™
Product Type
  • Silicone Rubber - Platinum Cure
  • Adhesives
  • Epoxy and Urethane Coatings
Mixed Viscosity11,000 cpsPaste350 cps
Mix Ratio By Volume1A:1B1A:1B2A:1B
Mix Ratio By Weight1A:1B100A:42B
Pot Life5 minutes20 minutes
Thin Film Working Time20 minutes
Thin Film Recoat Time90 minutes
Tack Free Time2 hours
Cure Time45 minutes24 hours
Barcol 935 Hardness75
Shore D Hardness80
Shore A Hardness22
Specific Gravity1.08 g/cc1.4 g/cc1.09 g/cc
Specific Volume25.6 cu. in./lb.20 cu. in./lb.25.1 cu. in./lb.
ColorTranslucent GreenBlackClear (Slightly Yellow In Thick Sections)
Die B Tear Strength102 pli
Tensile Strength490 psi3,000 psi
Elongation @ Break450 %
100% Modulus49 psi
Flexural Strength5,000 psi
Shrinkage<.001 in. / in.0.003 in. / in.
Useful Temperature (min)-65 °F
Useful Temperature (max)500 °F
Compressive Yield Strength5,000 psi

Product Description

EZ-Spray® Silicone 22

EZ~Spray® Silicone 22 are sprayable silicones which cure quickly to soft rubbers with high elongation and tear strength. Liquid silicone is sprayed through the EZ~Spray® Junior Cartridge System which is an economical alternative to expensive spray equipment. After a suitable thickness is attained, EZ~Spray® Silicone 22 cures in about 45 minutes. EZ~Spray® Silicone cures with negligible shrinkage to strong, durable silicone rubbers good for production casting of polyester, epoxy or urethane resins, gypsum, concrete and other materials.

Read More

PC-3®

Smooth-On PC-3® Laboratory Table Top Cement is a two-component, black epoxy resin compound designed to join, bond and caulk sections of laboratory counters and tables. This epoxy resin cement is heavily filled and will adhere to vertical surfaces without sagging. It cures at room temperature with extremely low shrinkage.

Read More

XTC-3D™

XTC-3D™ is a protective coating for smoothing and finishing 3D printed parts. Two liquids are mixed together and brushed onto any 3D print. Coating self-levels and wets out uniformly without leaving brush strokes. Working time is 10 minutes and cure time is about 4 hours (depending on mass and temperature). XTC-3D™ cures to a hard, impact resistant coating that can be sanded, primed and painted. Adding colors and metal effects is easy.

Read More

Select a Material from a Category Below

Silicone Rubber - Tin Cure ›

Silicone Rubber - Platinum Cure ›

Urethane Rubber ›

Polysulfide Rubber ›

Urethane Resins ›

Epoxy Casting and Laminating Resins ›

Epoxy Putties ›

Epoxy and Urethane Coatings ›

Mix and Pour Expanding Foams ›

Adhesives ›

Lifecasting Materials ›

Skin Safe FX Materials ›

Polymer Modifiers for Concrete and Gypsum ›