EpoxAmite™ HT

EZ-Spray® Silicone 22 vs. EpoxAmite™ HTEZ-Spray® Silicone 22

High-Temp Laminating Epoxy

 View Product

Add Material to Compare

start over

Key Differences

Product Type
  • Silicone Rubber - Platinum Cure
  • Epoxy Casting and Laminating Resins
Mixed Viscosity11,000 cps650 cps
Mix Ratio By Volume1A:1BN/A (gram scale required)
Pot Life5 minutes60 minutes
Cure Time45 minutes24 hours
Shore D Hardness80
Shore A Hardness22
ColorTranslucent GreenClear
Disclaimer
Although we do our best to ensure the accuracy of this Compare Tool, Smooth-On offers no warranty either expressed or implied as to the reliability of the information contained herein. Smooth-On assumes no liability for loss or damage associated with use of the Compare Tool. If this is a critical project, we encourage you to review all of the technical data below and contact our Technical Service department with any questions or concerns.

All Technical Data

EZ-Spray® Silicone 22EpoxAmite™ HT
Product Type
  • Silicone Rubber - Platinum Cure
  • Epoxy Casting and Laminating Resins
Mixed Viscosity11,000 cps650 cps
Mix Ratio By Volume1A:1B
Mix Ratio By Weight100A:33B
Pot Life5 minutes60 minutes
Thin Film Working Time180 minutes
Cure Time45 minutes24 hours
Shore D Hardness80
Shore A Hardness22
Specific Gravity1.08 g/cc1.1 g/cc
Specific Volume25.6 cu. in./lb.25.2 cu. in./lb.
ColorTranslucent GreenClear
Die B Tear Strength102 pli
Tensile Strength490 psi
Tensile Modulus342,000 psi
Ultimate Tensile6,500 psi
Tensile Elongation2.3 %
Elongation @ Break450 %
100% Modulus49 psi
Compressive Strength16,600 psi
Compressive Modulus168,000 psi
Flexural Strength12,325 psi
Flexural Modulus429,000 psi
Shrinkage<.001 in. / in.
Useful Temperature (min)-65 °F
Useful Temperature (max)500 °F
Heat Deflection With Post Cure300 °F
Ultimate Tensile on 6 ply / 10 oz. Laminate32,100 psi
Flexural Strength on 6 ply / 10 oz. Laminate20,700 psi
Tensile Modulus on 6 ply / 10 oz. Laminate2,150,000 psi
Flexural Modulus on 6 ply / 10 oz. Laminate2,216,000 psi

Product Description

EZ-Spray® Silicone 22

EZ~Spray® Silicone 22 are sprayable silicones which cure quickly to soft rubbers with high elongation and tear strength. Liquid silicone is sprayed through the EZ~Spray® Junior Cartridge System which is an economical alternative to expensive spray equipment. After a suitable thickness is attained, EZ~Spray® Silicone 22 cures in about 45 minutes. EZ~Spray® Silicone cures with negligible shrinkage to strong, durable silicone rubbers good for production casting of polyester, epoxy or urethane resins, gypsum, concrete and other materials.

Read More

EpoxAmite™ HT

EpoxAmite™ HT High Temperature Laminating Epoxy is a water clear, UV resistant laminating epoxy that resists high temperatures up to 300°F / 149°C when properly cured. Pot life is 1 hour and cure time is 24 hours at 73°F / 23°C (post cure required – see post cure schedule). Ultra-low viscosity ensures uniform wetting out and fast penetration of reinforcement materials during hand lay-up or vacuum infusion processes. Cured resin offers superior physical properties.

EpoxAmite™ HT High Temp Laminating Epoxy can be used with S-Glass, E-Glass, Kevlar and carbon fibers for making composite tooling or parts.  Applications include making high temperature pre-preg parts, bonding fixtures, vacuum form molds and prototype injection molds.
Use as a backup laminating resin for EpoxAcoat™ HT high temperature surface coat epoxy.

Read More

Select a Material from a Category Below

Silicone Rubber - Tin Cure ›

Silicone Rubber - Platinum Cure ›

Urethane Rubber ›

Polysulfide Rubber ›

Urethane Resins ›

Epoxy Casting and Laminating Resins ›

Epoxy Putties ›

Epoxy and Urethane Coatings ›

Mix and Pour Expanding Foams ›

Adhesives ›

Lifecasting Materials ›

Skin Safe FX Materials ›

Polymer Modifiers for Concrete and Gypsum ›