|Mold Max™ 29NV|
|Mixed Viscosity||10,000 cps|
|Mix Ratio By Weight||100A:10B|
|Pot Life||40 minutes|
|Cure Time||6 hours|
|Shore A Hardness||29|
|Specific Gravity||1.17 g/cc|
|Specific Volume||23.7 cu. in./lb.|
|Die B Tear Strength||96 pli|
|Tensile Strength||417 psi|
|Elongation @ Break||361 %|
|100% Modulus||54 psi|
|Shrinkage||0.002 in. / in.|
|Useful Temperature (min)||-65 °F|
|Useful Temperature (max)||400 °F|
|Volume Resistivity||9.000000E+14 ohm/cm|
|Dielectric Constant, 100Hz||3.4|
|Dielectric Strength||>500 volts/mil|
|Dissipation Factor, 100Hz||0.02|
|Thermal Conductivity||0.21 W/M*K|
Mold Max™ 29NV is a Shore 29A tin-catalyzed silicone mold rubber that offers low viscosity, fast cure and long library life.
Mold Max™ 29NV does not require vacuum degassing. Mix ratio is 100A:10B by weight. Working time is 45 minutes and cure time is 6 hours at room temperature.
Mold Max™ 29NV will reproduce the finest detail and is suitable for a variety of industrial and art related applications including making molds for reproducing prototypes, furniture, sculpture and architectural elements. Cure time can be reduced with Accel-T™ cure accelerator. Mold Max™ 29NV can be used to cast a variety of materials including concrete, wax, gypsum, low melt alloys/metals and urethane, epoxy or polyester resins.
Important; you must weigh Part A & B components using a gram scale to be successful with Mold Max™ 29NV.