Product Type |
|
|
|
Mixed Viscosity | 13,000 cps | 3,000 cps | 7,000 cps |
Mix Ratio By Volume | 1A:1B | 1A:4B | N/A (gram scale required) |
Pot Life | 1 minute | 3 minutes | 90 minutes |
Cure Time | 5 minutes | 60 minutes | 4 hours |
Barcol 935 Hardness | — | — | 93 |
Shore D Hardness | — | 85 | — |
Shore A Hardness | 5 | — | — |
Specific Volume | 25.8 cu. in./lb. | 17.3 cu. in./lb. | 18.22 cu. in./lb. |
Color | Translucent | Beige | Off White |
Ecoflex™ 5 | Shell Shock™ FAST | EpoxAcast™ 650 + 102 Hardener | |
---|---|---|---|
Product Type |
|
|
|
Mixed Viscosity | 13,000 cps | 3,000 cps | 7,000 cps |
Mix Ratio By Volume | 1A:1B | 1A:4B | — |
Mix Ratio By Weight | 1A:1B | 1A:5B | 100A:13B |
Pot Life | 1 minute | 3 minutes | 90 minutes |
Cure Time | 5 minutes | 60 minutes | 4 hours |
Barcol 935 Hardness | — | — | 93 |
Shore D Hardness | — | 85 | — |
Shore A Hardness | 5 | — | — |
Specific Gravity | 1.07 g/cc | 1.60 g/cc | 1.52 g/cc |
Specific Volume | 25.8 cu. in./lb. | 17.3 cu. in./lb. | 18.22 cu. in./lb. |
Color | Translucent | Beige | Off White |
Die B Tear Strength | 75 pli | — | — |
Tensile Strength | 350 psi | 3,100 psi | — |
Tensile Modulus | — | 435,000 psi | 1,503,000 psi |
Ultimate Tensile | — | — | 6,000 psi |
Tensile Elongation | — | — | 0.42 % |
Elongation @ Break | 1,000 % | 0.4 % | — |
100% Modulus | 15 psi | — | — |
Compressive Strength | — | 9,000 psi | 16,350 psi |
Compressive Modulus | — | 500,000 psi | 142,600 psi |
Flexural Strength | — | 7,150 psi | 5,890 psi |
Flexural Modulus | — | 980,000 psi | 710,000 psi |
Shrinkage | <.001 in. / in. | 0.0006 in. / in. | 0.001 in. / in. |
Heat Deflection Temp | — | 135 °F | 129 °F |
Useful Temperature (min) | -65 °F | — | — |
Useful Temperature (max) | 450 °F | — | — |
Ecoflex™ rubbers are platinum-catalyzed silicones that are versatile and easy to use. Ecoflex™ rubbers are mixed 1A:1B by weight or volume and cured at room temperature with negligible shrinkage. Low viscosity ensures easy mixing and de-airing. Dispense using our convenient dispensing cartridges. Cured rubber is very soft, very strong and very “stretchy”, stretching many times its original size without tearing and will rebound to its original form without distortion.
Shell Shock™ FAST is a thixotropic plastic that self thickens when mixed and can be brushed onto a variety of surfaces or into rubber molds. When Parts A and B are mixed in proper proportion (1A:4B by volume or 1A:5B by weight), material cures at room temperature with virtually no shrinkage to a hard, durable plastic that exhibits good compressive and flexural strength. Fully cured castings are rigid and can be sanded, primed and painted. Color effects are possible by adding SO-Strong™ Color Tints.
EpoxAcast™ 650 is a mineral filled general purpose casting epoxy resin that is low cost and versatile. It features a low mixed viscosity for minimal bubble entrapment.