Ecoflex™ 5

FMC™ 200 vs. Ecoflex™ 5 vs. EpoxAcast™ 650 + 102 Hardener

Super-Soft, Addition Cure Silicone Rubber

 View Product

Vs.
remove

EpoxAcast™ 650 + 102 Hardener

FMC™ 200 vs. Ecoflex™ 5 vs. EpoxAcast™ 650 + 102 HardenerEcoflex™ 5

Mineral Filled General Purpose Casting Epoxy

 View Product

Vs.

Add Material to Compare

start over

Key Differences

Product Type
  • Silicone Rubber - Platinum Cure
  • Epoxy Casting and Laminating Resins
  • Polysulfide Rubber
Mixed Viscosity13,000 cps7,000 cps6,000 cps
Mix Ratio By Volume1A:1BN/A (gram scale required)N/A (gram scale required)
Pot Life1 minute90 minutes50 minutes
Cure Time5 minutes4 hours16 hours
Barcol 935 Hardness93
Shore A Hardness520
Specific Volume25.8 cu. in./lb.18.22 cu. in./lb.20.5 cu. in./lb.
ColorTranslucentOff WhiteBlack
Disclaimer
Although we do our best to ensure the accuracy of this Compare Tool, Smooth-On offers no warranty either expressed or implied as to the reliability of the information contained herein. Smooth-On assumes no liability for loss or damage associated with use of the Compare Tool. If this is a critical project, we encourage you to review all of the technical data below and contact our Technical Service department with any questions or concerns.

All Technical Data

Ecoflex™ 5EpoxAcast™ 650 + 102 HardenerFMC™ 200
Product Type
  • Silicone Rubber - Platinum Cure
  • Epoxy Casting and Laminating Resins
  • Polysulfide Rubber
Mixed Viscosity13,000 cps7,000 cps6,000 cps
Mix Ratio By Volume1A:1B
Mix Ratio By Weight1A:1B100A:13B100A:12B
Pot Life1 minute90 minutes50 minutes
Cure Time5 minutes4 hours16 hours
Barcol 935 Hardness93
Shore A Hardness520
Specific Gravity1.07 g/cc1.52 g/cc1.35 g/cc
Specific Volume25.8 cu. in./lb.18.22 cu. in./lb.20.5 cu. in./lb.
ColorTranslucentOff WhiteBlack
Die B Tear Strength75 pli
Tensile Strength350 psi157 psi
Tensile Modulus1,503,000 psi
Ultimate Tensile6,000 psi
Elongation @ Break1,000 %700 %
100% Modulus15 psi29 psi
Compressive Strength16,350 psi
Compressive Modulus142,600 psi
Flexural Strength5,890 psi
Flexural Modulus710,000 psi
Shrinkage<.001 in. / in.0.001 in. / in.negligible in. / in.
Heat Deflection Temp129 °F
Useful Temperature (min)-65 °F
Useful Temperature (max)450 °F

Product Description

Ecoflex™ 5

Ecoflex™ rubbers are platinum-catalyzed silicones that are versatile and easy to use. Ecoflex™ rubbers are mixed 1A:1B by weight or volume and cured at room temperature with negligible shrinkage.  Low viscosity ensures easy mixing and de-airing. Dispense using our convenient dispensing cartridges. Cured rubber is very soft, very strong and very “stretchy”, stretching many times its original size without tearing and will rebound to its original form without distortion.

Read More

EpoxAcast™ 650 + 102 Hardener

EpoxAcast™ 650 is a mineral filled general purpose casting epoxy that is low cost and versatile. It features a low mixed viscosity for minimal bubble entrapment.

Read More

FMC™ 200

FMC™-200 is a polysulfide rubber mold compound with high tear strength that cures overnight with negligible shrinkage. Molds made of FMC™-200 are very durable and will perform in production. The mix ratio is 100 parts of Part A to 12 parts of Part B by weight. FMC™-200 cures to a Shore hardness of 20 A.

FMC™-200 is ideal for those applications that require capturing intricate detail from a variety of model surfaces. Unlike polyurethanes, FMC™-200 is not sensitive to moisture and can be poured directly over wet plaster or water/sulfur based clays. Common applications include molds for foundry and pattern work, sculpture (lost wax process), casting various gypsum products and waxes.

Read More

Select a Material from a Category Below

Silicone Rubber - Tin Cure ›

Silicone Rubber - Platinum Cure ›

Urethane Rubber ›

Polysulfide Rubber ›

Urethane Resins ›

Epoxy Casting and Laminating Resins ›

Epoxy Putties ›

Epoxy and Urethane Coatings ›

Mix and Pour Expanding Foams ›

Adhesives ›

Lifecasting Materials ›

Skin Safe FX Materials ›

Polymer Modifiers for Concrete and Gypsum ›