Key Differences
| Product Type |
|
|
|
|
| Mixed Viscosity | 13,000 cps | 7,000 cps | Light Paste | 1,000 cps |
| Mix Ratio By Volume | 1A:1B | N/A (gram scale required) | N/A (gram scale required) | 1A:2B |
| Pot Life | 1 minute | 90 minutes | 40 minutes | 35 seconds |
| Cure Time | 5 minutes | 4 hours | 24 hours | 2 hours |
| Barcol 935 Hardness | — | 93 | — | — |
| Shore D Hardness | — | — | 85 | — |
| Shore A Hardness | 5 | — | — | — |
| Color | Translucent | Off White | Dark Red | White |
Disclaimer
Although we do our best to ensure accuracy, Smooth-On offers no warranties, promises, and/or representations of any kind, either expressed or implied, as to the accuracy, completeness, or reliability of the information contained on this Compare Tool, nor suitability of the information contained herein to your particular circumstances. Smooth-On assumes no liability for losses or damages of whatever nature (direct, indirect, consequential or other) associated with your use, or inability to use, the Compare Tool, or from your use (or failure to use) the information contained herein. Other useful tools include product technical bulletins and our extensive FAQ section. You can also contact our technical support team.All Technical Data
| Ecoflex™ 5 | EpoxAcast™ 650 + 102 Hardener | EpoxAcoat™ HT | FlexFoam-iT!™ VIII Pillow Soft | |
|---|---|---|---|---|
| Product Type |
|
|
|
|
| Mixed Viscosity | 13,000 cps | 7,000 cps | Light Paste | 1,000 cps |
| Mix Ratio By Volume | 1A:1B | — | — | 1A:2B |
| Mix Ratio By Weight | 1A:1B | 100A:13B | 100A:18B | 52.6A:100B |
| Pot Life | 1 minute | 90 minutes | 40 minutes | 35 seconds |
| Thin Film Working Time | — | — | 75 minutes | — |
| Thin Film Recoat Time | — | — | 4 hours | — |
| Handling Time | — | — | — | 25 minutes |
| Cure Time | 5 minutes | 4 hours | 24 hours | 2 hours |
| Barcol 935 Hardness | — | 93 | — | — |
| Shore D Hardness | — | — | 85 | — |
| Shore A Hardness | 5 | — | — | — |
| Expansion (approximate) | — | — | — | 7 times |
| Foam Density | — | — | — | 8 lb/ft³ |
| Specific Gravity | 1.07 g/cc | 1.52 g/cc | — | 0.13 g/cc |
| Specific Volume | 25.8 cu. in./lb. | 18.22 cu. in./lb. | — | 194 cu. in./lb. |
| Color | Translucent | Off White | Dark Red | White |
| Die B Tear Strength | 75 pli | — | — | — |
| Tensile Strength | 350 psi | — | — | — |
| Tensile Modulus | — | 1,503,000 psi | — | — |
| Ultimate Tensile | — | 6,000 psi | — | — |
| Tensile Elongation | — | 0.42 % | — | — |
| Elongation @ Break | 1,000 % | — | — | — |
| 100% Modulus | 15 psi | — | — | — |
| Compressive Strength | — | 16,350 psi | — | — |
| Compressive Modulus | — | 142,600 psi | — | — |
| Flexural Strength | — | 5,890 psi | — | — |
| Flexural Modulus | — | 710,000 psi | — | — |
| Shrinkage | <.001 in. / in. | 0.001 in. / in. | — | — |
| Heat Deflection Temp | — | 129 °F | 133 °F | — |
| Useful Temperature (min) | -65 °F | — | — | — |
| Useful Temperature (max) | 450 °F | — | — | — |
| Heat Deflection With Post Cure | — | — | 284 °F | — |
Product Description
Ecoflex™ 5
Ecoflex™ rubbers are platinum-catalyzed silicones that are versatile and easy to use. Ecoflex™ rubbers are mixed 1A:1B by weight or volume and cured at room temperature with negligible shrinkage. Low viscosity ensures easy mixing and de-airing. Dispense using our convenient dispensing cartridges. Cured rubber is very soft, very strong and very “stretchy”, stretching many times its original size without tearing and will rebound to its original form without distortion.
EpoxAcast™ 650 + 102 Hardener
EpoxAcast™ 650 is a mineral filled general purpose casting epoxy resin that is low cost and versatile. It features a low mixed viscosity for minimal bubble entrapment.
EpoxAcoat™ HT
EpoxAcoat™ HT is a slightly thixotropic epoxy gel coat that offers high heat resistance (post cure required). Cured epoxy is tough and offers exceptional abrasion resistance. This surface coat will wet out well over a variety of surfaces with good sag resistance. Applications include laminating, precision tooling, master and pattern making, core boxes and fixtures.
Use as a surface coat for EpoxAmite™ HT high temperature laminating epoxy.
› Click here for more EpoxAcoat™ resin products.
FlexFoam-iT!™ VIII Pillow Soft
FlexFoam-iT!™ Series foams are premium quality water blown flexible foams that can be used for a variety of industrial, special effects and art & crafts and projects. With several to choose from, uses include making theatrical props (swords, knives, hammers, etc.), industrial gaskets, custom padding and cushioning, and more. SO-Strong™, UVO™ or IGNITE™ colorants can be added for color effects.
Part A and B liquids are combined, mixed and poured into a mold or other form (apply release agent if necessary). Mixture will rise and cure quickly to a solid, flexible foam. Foams vary by density and offer good physical properties.