Ecoflex™ 5

Ecoflex™ 5 vs. PC-3® vs. EpoxAcast™ 655 + 102 Hardener

Super-Soft, Addition Cure Silicone Rubber

 View Product

Vs. Vs.
remove

PC-3®

Ecoflex™ 5 vs. PC-3® vs. EpoxAcast™ 655 + 102 HardenerEcoflex™ 5 versus EpoxAcast™ 655 + 102 Hardener

Laboratory Tabletop Epoxy Adhesive

 View Product

Add Material to Compare

start over

Key Differences

Product Type
  • Silicone Rubber - Platinum Cure
  • Epoxy Casting and Laminating Resins
  • Adhesives
Mixed Viscosity13,000 cps23,000 cpsPaste
Mix Ratio By Volume1A:1BN/A (gram scale required)1A:1B
Pot Life1 minute75 minutes20 minutes
Cure Time5 minutes9 hours24 hours
Barcol 935 Hardness75
Shore D Hardness90
Shore A Hardness5
Specific Volume25.8 cu. in./lb.16.7 cu. in./lb.20 cu. in./lb.
ColorTranslucentGreyBlack
Disclaimer
Although we do our best to ensure the accuracy of this Compare Tool, Smooth-On offers no warranty either expressed or implied as to the reliability of the information contained herein. Smooth-On assumes no liability for loss or damage associated with use of the Compare Tool. If this is a critical project, we encourage you to review all of the technical data below and contact our Technical Service department with any questions or concerns.

All Technical Data

Ecoflex™ 5EpoxAcast™ 655 + 102 HardenerPC-3®
Product Type
  • Silicone Rubber - Platinum Cure
  • Epoxy Casting and Laminating Resins
  • Adhesives
Mixed Viscosity13,000 cps23,000 cpsPaste
Mix Ratio By Volume1A:1B1A:1B
Mix Ratio By Weight1A:1B100A:11B1A:1B
Pot Life1 minute75 minutes20 minutes
Cure Time5 minutes9 hours24 hours
Barcol 935 Hardness75
Shore D Hardness90
Shore A Hardness5
Specific Gravity1.07 g/cc1.66 g/cc1.4 g/cc
Specific Volume25.8 cu. in./lb.16.7 cu. in./lb.20 cu. in./lb.
ColorTranslucentGreyBlack
Die B Tear Strength75 pli
Tensile Strength350 psi3,000 psi
Tensile Modulus2,040,000 psi
Ultimate Tensile4,810 psi
Elongation @ Break1,000 %
100% Modulus15 psi
Compressive Strength12,500 psi
Compressive Modulus125,500 psi
Flexural Strength7,660 psi5,000 psi
Flexural Modulus1,403,000 psi
Shrinkage<.001 in. / in.0.0006 in. / in.0.003 in. / in.
Heat Deflection Temp135 °F
Useful Temperature (min)-65 °F
Useful Temperature (max)450 °F
Compressive Yield Strength5,000 psi

Product Description

Ecoflex™ 5

Ecoflex™ rubbers are platinum-catalyzed silicones that are versatile and easy to use. Ecoflex™ rubbers are mixed 1A:1B by weight or volume and cured at room temperature with negligible shrinkage.  Low viscosity ensures easy mixing and de-airing. Dispense using our convenient dispensing cartridges. Cured rubber is very soft, very strong and very “stretchy”, stretching many times its original size without tearing and will rebound to its original form without distortion.

Read More

EpoxAcast™ 655 + 102 Hardener

EpoxAcast655 (formerly Metalset™ A-30) is a versatile aluminum filled castable epoxy that is very hard and strong. It is dimensionally stable, even when mass cast up to 512 in3 / 8,390 cm3.

Read More

PC-3®

Smooth-On PC-3® Laboratory Table Top Cement is a two-component, black epoxy resin compound designed to join, bond and caulk sections of laboratory counters and tables. This epoxy resin cement is heavily filled and will adhere to vertical surfaces without sagging. It cures at room temperature with extremely low shrinkage.

Read More

Select a Material from a Category Below

Silicone Rubber - Tin Cure ›

Silicone Rubber - Platinum Cure ›

Urethane Rubber ›

Polysulfide Rubber ›

Urethane Resins ›

Epoxy Casting and Laminating Resins ›

Epoxy Putties ›

Epoxy and Urethane Coatings ›

Mix and Pour Expanding Foams ›

Adhesives ›

Lifecasting Materials ›

Skin Safe FX Materials ›

Polymer Modifiers for Concrete and Gypsum ›