Ecoflex™ 5

Ecoflex™ 5 vs. FOAM-iT!™ 26 vs. Epsilon™ PRO

Super-Soft, Addition Cure Silicone Rubber

 View Product

Vs.
remove

Epsilon™ PRO

Ecoflex™ 5 vs. FOAM-iT!™ 26 vs. Epsilon™ PROEcoflex™ 5

High Performance Impact Resistant EPS Foam Coating

 View Product

Vs.
remove

FOAM-iT!™ 26

Ecoflex™ 5 vs. FOAM-iT!™ 26 vs. Epsilon™ PROEcoflex™ 5 versus Epsilon™ PRO

Rigid Urethane Expanding Foams

 View Product

Add Material to Compare

start over

Key Differences

Product Type
  • Silicone Rubber - Platinum Cure
  • Epoxy and Urethane Coatings
  • Mix and Pour Expanding Foams
Mixed Viscosity13,000 cps4,000 cps500 cps
Pot Life1 minute22 minutes1.5 minutes
Cure Time5 minutes16 hours2 hours
Shore D Hardness65
Shore A Hardness5
Specific Volume25.8 cu. in./lb.25.0 cu. in./lb.60 cu. in./lb.
ColorTranslucentClear AmberWhite
Disclaimer
Although we do our best to ensure the accuracy of this Compare Tool, Smooth-On offers no warranty either expressed or implied as to the reliability of the information contained herein. Smooth-On assumes no liability for loss or damage associated with use of the Compare Tool. If this is a critical project, we encourage you to review all of the technical data below and contact our Technical Service department with any questions or concerns.

All Technical Data

Ecoflex™ 5Epsilon™ PROFOAM-iT!™ 26
Product Type
  • Silicone Rubber - Platinum Cure
  • Epoxy and Urethane Coatings
  • Mix and Pour Expanding Foams
Mixed Viscosity13,000 cps4,000 cps500 cps
Mix Ratio By Volume1A:1B2A:1B1A:1B
Mix Ratio By Weight1A:1B100A:44B100A:90B
Pot Life1 minute22 minutes1.5 minutes
Thin Film Working Time35 minutes
Thin Film Recoat Time3 hours
Tack Free Time20 minutes
Cure Time5 minutes16 hours2 hours
Shore D Hardness65
Shore A Hardness5
Expansion (approximate)2 times
Foam Density26 lb/ft³
Specific Gravity1.07 g/cc1.11 g/cc0.42 g/cc
Specific Volume25.8 cu. in./lb.25.0 cu. in./lb.60 cu. in./lb.
ColorTranslucentClear AmberWhite
Die B Tear Strength75 pli
Tensile Strength350 psi
Elongation @ Break1,000 %
100% Modulus15 psi
Shrinkage<.001 in. / in.
Useful Temperature (min)-65 °F
Useful Temperature (max)450 °F

Product Description

Ecoflex™ 5

Ecoflex™ rubbers are platinum-catalyzed silicones that are versatile and easy to use. Ecoflex™ rubbers are mixed 1A:1B by weight or volume and cured at room temperature with negligible shrinkage.  Low viscosity ensures easy mixing and de-airing. Dispense using our convenient dispensing cartridges. Cured rubber is very soft, very strong and very “stretchy”, stretching many times its original size without tearing and will rebound to its original form without distortion.

Read More

Epsilon™ PRO

Epsilon™ PRO is a thixotropic epoxy coating that self-thickens for brushing onto a variety of surfaces.  Compared to original Epsilon™, Epsilon™ PRO offers a longer working time and cured epoxy is semi-rigid, offering better impact resistance.  Mix ratio for Epsilon™ PRO is 2A:1B by volume (100A:44B by weight).  A gram scale is not needed to use this product.

Applied in thin layers, mixed material holds a vertical surface without sagging or slumping. Material wets out uniformly over different surfaces.  Pot life is 22 minutes, with a re-coat time of 3 hours.  All layers should be allowed to cure for 16 hours at 73° F / 23° C and can be accelerated with mild heat.  Epsilon™ PRO is clear and can be easily colored using Ignite™ or UVO™ colorants.  Cured coating has a gloss finish and can be sanded, primed and painted.

Applications: Epsilon™ PRO is suitable for use as a protective, impact resistant coating for EPS or polyurethane foam. It can also be applied to plaster, concrete, wood and fabrics. This product is not sensitive to moisture / humidity and contains no VOC’s. 

Read More

FOAM-iT!™ 26

Smooth-On’s FOAM-iT!™ Series are two-component water blown rigid foams that are versatile and easy to use. FOAM-iT!™ products are available in 3lb., 4 lb., 5 lb., 8 lb., 10 lb.,15 lb. or 26 lb. per cubic foot densities. Parts A and B are measured and mixed in equal amounts by volume. The mixture is then poured into a mold or other form (apply release agent if necessary). The mixture will expand many times original volume (depending on which FOAM-iT!™ product you are using) and develop a uniform cell structure. FOAM-IT!™ 26 is tack-free in about 4 - 6.5 minutes, developing handling strength in 20 minutes and full cure in 2 hours. FOAM-iT!™ 26 can be cast in blocks as a machinable prototype modeling board.

All FOAM-iT!™ products can be used as a straight casting material, backfill material for hollow castings (adds structural strength) or as an encapsulation material, etc. They can be color pigmented with SO-Strong™, UVO™ or IGNITE™ colorants and are used for a variety of art/ craft, industrial design and special effects applications.

Read More

Select a Material from a Category Below

Silicone Rubber - Tin Cure ›

Silicone Rubber - Platinum Cure ›

Urethane Rubber ›

Polysulfide Rubber ›

Urethane Resins ›

Epoxy Casting and Laminating Resins ›

Epoxy Putties ›

Epoxy and Urethane Coatings ›

Mix and Pour Expanding Foams ›

Adhesives ›

Lifecasting Materials ›

Skin Safe FX Materials ›

Polymer Modifiers for Concrete and Gypsum ›