Ecoflex™ 5

Mold Max™ 60 vs. Ecoflex™ 5

Super-Soft, Addition Cure Silicone Rubber

 View Product

Vs.
remove

Mold Max™ 60

Mold Max™ 60 vs. Ecoflex™ 5Ecoflex™ 5

High Heat Resistance Silicone Mold Rubber

 View Product

Add Material to Compare

start over

Key Differences

Product Type
  • Silicone Rubber - Platinum Cure
  • Silicone Rubber - Tin Cure
Mixed Viscosity13,000 cps20,000 cps
Mix Ratio By Volume1A:1BN/A (gram scale required)
Pot Life1 minute40 minutes
Cure Time5 minutes24 hours
Shore A Hardness560
Specific Volume25.8 cu. in./lb.19.1 cu. in./lb.
ColorTranslucentRed
Elongation @ Break1,000 %132 %
100% Modulus15 psi331 psi
Disclaimer
Although we do our best to ensure the accuracy of this Compare Tool, Smooth-On offers no warranty either expressed or implied as to the reliability of the information contained herein. Smooth-On assumes no liability for loss or damage associated with use of the Compare Tool. If this is a critical project, we encourage you to review all of the technical data below and contact our Technical Service department with any questions or concerns.

All Technical Data

Ecoflex™ 5Mold Max™ 60
Product Type
  • Silicone Rubber - Platinum Cure
  • Silicone Rubber - Tin Cure
Mixed Viscosity13,000 cps20,000 cps
Mix Ratio By Volume1A:1B
Mix Ratio By Weight1A:1B100A:3B
Pot Life1 minute40 minutes
Cure Time5 minutes24 hours
Shore A Hardness560
Specific Gravity1.07 g/cc1.45 g/cc
Specific Volume25.8 cu. in./lb.19.1 cu. in./lb.
ColorTranslucentRed
Die B Tear Strength75 pli63 pli
Tensile Strength350 psi398 psi
Elongation @ Break1,000 %132 %
100% Modulus15 psi331 psi
Shrinkage<.001 in. / in.0.0015 in. / in.
Useful Temperature (min)-65 °F-65 °F
Useful Temperature (max)450 °F560 °F
Volume Resistivity9.000000E+14 ohm/cm
Dielectric Strength>500 volts/mil
Dissipation Factor, 100Hz0.02
Dielectric Constant, 100Hz3.4
Thermal Conductivity0.347 W/M*K

Product Description

Ecoflex™ 5

Ecoflex™ rubbers are platinum-catalyzed silicones that are versatile and easy to use. Ecoflex™ rubbers are mixed 1A:1B by weight or volume and cured at room temperature with negligible shrinkage.  Low viscosity ensures easy mixing and de-airing. Dispense using our convenient dispensing cartridges. Cured rubber is very soft, very strong and very “stretchy”, stretching many times its original size without tearing and will rebound to its original form without distortion.

Read More

Mold Max™ 60

Mold Max™ 60 is a Shore 60A tin catalyzed silicone mold rubber formulated for applications requiring high heat resistance (up to 560°F/294°C). It features a low mixed viscosity and cured rubber exhibits very low linear shrinkage. Parts A & B are mixed 100A & 3B by weight. Pot life is 40 minutes and cure time is 24 hours. Applications include making foundry patterns, flat pattern reproductions and casting low-melt metal alloys such as tin and pewter.

Read More

Select a Material from a Category Below

Silicone Rubber - Tin Cure ›

Silicone Rubber - Platinum Cure ›

Urethane Rubber ›

Polysulfide Rubber ›

Urethane Resins ›

Epoxy Casting and Laminating Resins ›

Epoxy Putties ›

Epoxy and Urethane Coatings ›

Mix and Pour Expanding Foams ›

Adhesives ›

Lifecasting Materials ›

Skin Safe FX Materials ›

Polymer Modifiers for Concrete and Gypsum ›