| Mold Max™ 29NV | |
|---|---|
| Product Type |
|
| Mixed Viscosity | 10,000 cps |
| Mix Ratio By Weight | 100A:10B |
| Pot Life | 40 minutes |
| Cure Time | 6 hours |
| Shore A Hardness | 29 |
| Specific Gravity | 1.17 g/cc |
| Specific Volume | 23.7 cu. in./lb. |
| Color | Yellow |
| Die B Tear Strength | 96 pli |
| Tensile Strength | 417 psi |
| Elongation @ Break | 361 % |
| 100% Modulus | 54 psi |
| Shrinkage | 0.002 in. / in. |
| Useful Temperature (min) | -65 °F |
| Useful Temperature (max) | 400 °F |
| Dielectric Constant, 100Hz | 3.29 |
| Dielectric Strength | 330 volts/mil |
| Dissipation Factor, 100Hz | 0.005 |
| Thermal Conductivity | 0.21 W/M*K |
| Volume Resistance | 8.29E+11 ohm |
| Volume Resistivity | 5.83E+13 ohm/cm |
Product Description
Mold Max™ 29NV
Mold Max™ 29NV is a Shore 29A tin-catalyzed silicone mold rubber that offers low viscosity, fast cure and long library life.
Mold Max™ 29NV does not require vacuum degassing. Mix ratio is 100A:10B by weight. Working time is 45 minutes and cure time is 6 hours at room temperature.
Mold Max™ 29NV will reproduce the finest detail and is suitable for a variety of industrial and art related applications including making molds for reproducing prototypes, furniture, sculpture and architectural elements. Cure time can be reduced with Accel-T™ cure accelerator. Mold Max™ 29NV can be used to cast a variety of materials including wax, gypsum, low melt alloys/metals and urethane, epoxy or polyester resins. Important: Do not cast concrete into rubber molds made with this product. Concrete will not cure properly and inhibition will result.
Important; you must weigh Part A & B components using a gram scale to be successful with Mold Max™ 29NV.