Key Differences
| Product Type |
|
|
| Mixed Viscosity | Paste | 2,000 cps |
| Pot Life | 20 minutes | 50 minutes |
| Cure Time | 24 hours | 16 hours |
| Barcol 935 Hardness | 75 | — |
| Shore A Hardness | — | 50 |
| Specific Volume | 20 cu. in./lb. | 27.4 cu. in./lb. |
| Color | Black | Off White |
| Tensile Strength | 3,000 psi | 580 psi |
Disclaimer
Although we do our best to ensure accuracy, Smooth-On offers no warranties, promises, and/or representations of any kind, either expressed or implied, as to the accuracy, completeness, or reliability of the information contained on this Compare Tool, nor suitability of the information contained herein to your particular circumstances. Smooth-On assumes no liability for losses or damages of whatever nature (direct, indirect, consequential or other) associated with your use, or inability to use, the Compare Tool, or from your use (or failure to use) the information contained herein. Other useful tools include product technical bulletins and our extensive FAQ section. You can also contact our technical support team.All Technical Data
| PC-3™ | ReoFlex™ 50 | |
|---|---|---|
| Product Type |
|
|
| Mixed Viscosity | Paste | 2,000 cps |
| Mix Ratio By Volume | 1A:1B | 1A:1B |
| Mix Ratio By Weight | 1A:1B | 1A:1B |
| Pot Life | 20 minutes | 50 minutes |
| Handling Time | 2 hours | — |
| Cure Time | 24 hours | 16 hours |
| Barcol 935 Hardness | 75 | — |
| Shore A Hardness | — | 50 |
| Specific Gravity | 1.4 g/cc | 1.01 g/cc |
| Specific Volume | 20 cu. in./lb. | 27.4 cu. in./lb. |
| Color | Black | Off White |
| Die C Tear Strength | — | 120 pli |
| Tensile Strength | 3,000 psi | 580 psi |
| Elongation @ Break | — | 435 % |
| 100% Modulus | — | 152 psi |
| Flexural Strength | 5,000 psi | — |
| Shrinkage | 0.003 in. / in. | <.001 in. / in. |
| Compressive Yield Strength | 5,000 psi | — |
Product Description
PC-3™
Smooth-On PC-3™ Laboratory Table Top Cement is a two-component, black epoxy resin compound designed to join, bond and caulk sections of laboratory counters and tables. This epoxy resin cement is heavily filled and will adhere to vertical surfaces without sagging. It cures at room temperature with extremely low shrinkage.
ReoFlex™ 50
ReoFlex™ urethane rubbers offer superior physical and performance properties for production casting of wax, plasters, and resins. ReoFlex™ urethanes are available in 20A, 30A, 40A, 50A and 60A Shore hardnesses and feature convenient one-to-one by volume mix ratios. Vacuum degassing is not necessary and ReoFlex™ rubbers cure with negligible shrinkage to a durable rubber that will last in production. ReoFlex™ “Wet” rubbers will shrink somewhat over time vs. “Dry” formulations.
ReoFlex™ mold rubbers are used for a variety of applications including making molds to reproduce sculpture and architectural elements, as well as for making special effects, toys and prototypes. Vibrant colors can be achieved by adding So-Strong™ Color Tints, available from Smooth-On.