Product Type |
|
|
Mixed Viscosity | Dough | 3,500 cps |
Pot Life | 90 minutes | 2.5 minutes |
Cure Time | 16 hours | 5 minutes |
Shore D Hardness | 85 | — |
Shore A Hardness | — | 00-35 |
Specific Volume | 17.3 cu. in./lb. | 26.0 cu. in./lb. |
Color | Grey | Off-White Translucent |
Free Form™ Habitat™ Fire Safe™ | Ecoflex™ 00-35 FAST | |
---|---|---|
Product Type |
|
|
Mixed Viscosity | Dough | 3,500 cps |
Mix Ratio By Volume | 1A:1B | 1A:1B |
Mix Ratio By Weight | 1A:1B | — |
Pot Life | 90 minutes | 2.5 minutes |
Cure Time | 16 hours | 5 minutes |
Shore D Hardness | 85 | — |
Shore A Hardness | — | 00-35 |
Specific Gravity | 1.44 g/cc | 1.07 g/cc |
Specific Volume | 17.3 cu. in./lb. | 26.0 cu. in./lb. |
Color | Grey | Off-White Translucent |
Die B Tear Strength | — | 38 pli |
Tensile Strength | — | 200 psi |
Elongation @ Break | — | 900 % |
100% Modulus | — | 10 psi |
Shrinkage | — | <0.001 in. / in. |
Heat Deflection Temp | 160 °F | — |
Useful Temperature (min) | — | -65 °F |
Useful Temperature (max) | — | 450 °F |
Heat Deflection With Post Cure | 212 °F | — |
Free Form™ Habitat™ Fire Safe™ epoxy putty is a high density epoxy sculpting putty that is flame rated (E84, Class A). Habitat™ Fire Safe™ is solvent-free and contains no VOC’s. Working time is 90 minutes and cure time is 16 hours at room temperature (73° F/23° C). Epoxy cures to a very hard, flame and heat resistant material that is easily painted. Habitat™ Fire Safe™ does not contain any carcinogens (cancer causing agents).
Ecoflex™ 00-35 FAST is a soft, fast cure platinum-catalyzed silicone that is versatile and easy to use. Parts A and B are mixed 1:1 by weight or volume, pot life is about 2.5 minutes and rubber cures in about 5 minutes at room temperature with negligible shrinkage. Low viscosity ensures easy mixing and pouring. Rubber cures without "tacky" surface, is very soft, very strong and very "stretchy, stretching many times its original size. EcoFlex™ 00-35 FAST is off-white translucent and can be color pigmented using Silc Pig™ silicone color pigments.