Key Differences
| Product Type |
|
|
| Mixed Viscosity | 7,000 cps | 25,000 cps |
| Pot Life | 90 minutes | 45 minutes |
| Cure Time | 4 hours | 24 hours |
| Barcol 935 Hardness | 93 | — |
| Shore A Hardness | — | 20 |
| Specific Volume | 18.22 cu. in./lb. | 23.5 cu. in./lb. |
| Color | Black | Light Pink |
Disclaimer
Although we do our best to ensure accuracy, Smooth-On offers no warranties, promises, and/or representations of any kind, either expressed or implied, as to the accuracy, completeness, or reliability of the information contained on this Compare Tool, nor suitability of the information contained herein to your particular circumstances. Smooth-On assumes no liability for losses or damages of whatever nature (direct, indirect, consequential or other) associated with your use, or inability to use, the Compare Tool, or from your use (or failure to use) the information contained herein. Other useful tools include product technical bulletins and our extensive FAQ section. You can also contact our technical support team.All Technical Data
| EpoxAcast™ 650 BLACK + 102 Hardener | Mold Max™ 20 | |
|---|---|---|
| Product Type |
|
|
| Mixed Viscosity | 7,000 cps | 25,000 cps |
| Mix Ratio By Weight | 100A:13B | 100A:10B |
| Pot Life | 90 minutes | 45 minutes |
| Cure Time | 4 hours | 24 hours |
| Barcol 935 Hardness | 93 | — |
| Shore A Hardness | — | 20 |
| Specific Gravity | 1.52 g/cc | 1.18 g/cc |
| Specific Volume | 18.22 cu. in./lb. | 23.5 cu. in./lb. |
| Color | Black | Light Pink |
| Die B Tear Strength | — | 110 pli |
| Tensile Strength | — | 555 psi |
| Tensile Modulus | 1,503,000 psi | — |
| Ultimate Tensile | 6,000 psi | — |
| Tensile Elongation | 0.42 % | — |
| Elongation @ Break | — | 512 % |
| 100% Modulus | — | 49 psi |
| Compressive Strength | 16,350 psi | — |
| Compressive Modulus | 142,600 psi | — |
| Flexural Strength | 5,890 psi | — |
| Flexural Modulus | 710,000 psi | — |
| Shrinkage | 0.001 in. / in. | 0.001 in. / in. |
| Heat Deflection Temp | 129 °F | — |
| Useful Temperature (min) | — | -65 °F |
| Useful Temperature (max) | — | 400 °F |
| Dielectric Constant, 100Hz | — | 3.29 |
| Dielectric Strength | — | 330 volts/mil |
| Dissipation Factor, 100Hz | — | 0.005 |
| Volume Resistance | — | 8.29E+11 ohm |
| Volume Resistivity | — | 5.83E+13 ohm/cm |
Product Description
EpoxAcast™ 650 BLACK + 102 Hardener
EpoxAcast™ 650 Black is a mineral filled general purpose casting epoxy that is low cost and versatile. It features a low mixed viscosity for minimal bubble entrapment.
Mold Max™ 20
Mold Max™ Silicones are tin-cured silicone rubber compounds that have exceptional working properties and library life. Mold Max™ Silicones feature Smooth-On’s exclusive “Libra™” catalyst for long library life. Mold Max™ silicones can be pigmented with Silc Pig™ silicone colorants. Pot life for the pourable silicones is 45 minutes and they cure overnight at room temperature.
Vacuum degassing mixed material using a vacuum pump and chamber to remove entrapped air is recommended.