Key Differences
| Product Type |
|
|
| Mixed Viscosity | 20,000 cps | 370 cps |
| Pot Life | 40 minutes | 12 hours |
| Shore D Hardness | — | 80 |
| Shore A Hardness | 60 | — |
| Specific Volume | 19.1 cu. in./lb. | 25.7 cu. in./lb. |
| Color | Red | Clear |
| Shrinkage | 0.0015 in. / in. | 0.007 in. / in. |
Disclaimer
Although we do our best to ensure accuracy, Smooth-On offers no warranties, promises, and/or representations of any kind, either expressed or implied, as to the accuracy, completeness, or reliability of the information contained on this Compare Tool, nor suitability of the information contained herein to your particular circumstances. Smooth-On assumes no liability for losses or damages of whatever nature (direct, indirect, consequential or other) associated with your use, or inability to use, the Compare Tool, or from your use (or failure to use) the information contained herein. Other useful tools include product technical bulletins and our extensive FAQ section. You can also contact our technical support team.All Technical Data
| Mold Max™ 60 | EpoxAcast™ 692 Deep Pour | |
|---|---|---|
| Product Type |
|
|
| Mixed Viscosity | 20,000 cps | 370 cps |
| Mix Ratio By Weight | 100A:3B | 100A:40B |
| Pot Life | 40 minutes | 12 hours |
| Cure Time | 24 hours | — |
| Shore D Hardness | — | 80 |
| Shore A Hardness | 60 | — |
| Specific Gravity | 1.45 g/cc | 1.08 g/cc |
| Specific Volume | 19.1 cu. in./lb. | 25.7 cu. in./lb. |
| Color | Red | Clear |
| Die B Tear Strength | 63 pli | — |
| Tensile Strength | 398 psi | — |
| Tensile Modulus | — | 378,000 psi |
| Ultimate Tensile | — | 4,585 psi |
| Tensile Elongation | — | 3.1 % |
| Elongation @ Break | 132 % | — |
| 100% Modulus | 331 psi | — |
| Compressive Strength | — | 5,777 psi |
| Compressive Modulus | — | 82,000 psi |
| Flexural Strength | — | 6,780 psi |
| Flexural Modulus | — | 203,000 psi |
| Shrinkage | 0.0015 in. / in. | 0.007 in. / in. |
| Heat Deflection Temp | — | 100 °F |
| Useful Temperature (min) | -65 °F | — |
| Useful Temperature (max) | 560 °F | — |
| Dielectric Constant, 100Hz | 3.4 | — |
| Dielectric Strength | >500 volts/mil | — |
| Dissipation Factor, 100Hz | 0.02 | — |
| Index of Refraction at 20°C | — | 1.5372 |
| Thermal Conductivity | 0.347 W/M*K | — |
| Volume Resistivity | 9.000000E+14 ohm/cm | — |
Product Description
Mold Max™ 60
Mold Max™ 60 is a Shore 60A tin catalyzed silicone mold rubber formulated for applications requiring high heat resistance (up to 560°F/294°C). It features a low mixed viscosity and cured rubber exhibits very low linear shrinkage. Parts A & B are mixed 100A & 3B by weight. Pot life is 40 minutes and cure time is 24 hours. Applications include making foundry patterns, flat pattern reproductions and casting low-melt metal alloys such as tin and pewter.
EpoxAcast™ 692 Deep Pour
EpoxAcast™ 692 Deep Pour is an UV resistant clear casting epoxy resins suitable for a variety of industrial and art related projects requiring a rigid, clear finished casting. EpoxAcast™ 692 features a very low viscosity for easy mixing and minimal bubble entrapment. Castings cure with negligible shrinkage and are very hard and strong. Resin can be colored with UVO™ or IGNITE™ colorants. Cast Magic™ and Glow Worm™ powders can also be added to create amazing casting effects.