| Mold Max™ 60 | |
|---|---|
| Product Type |
|
| Mixed Viscosity | 20,000 cps |
| Mix Ratio By Weight | 100A:3B |
| Pot Life | 40 minutes |
| Cure Time | 24 hours |
| Shore A Hardness | 60 |
| Specific Gravity | 1.45 g/cc |
| Specific Volume | 19.1 cu. in./lb. |
| Color | Red |
| Die B Tear Strength | 63 pli |
| Tensile Strength | 398 psi |
| Elongation @ Break | 132 % |
| 100% Modulus | 331 psi |
| Shrinkage | 0.0015 in. / in. |
| Useful Temperature (min) | -65 °F |
| Useful Temperature (max) | 560 °F |
| Dielectric Constant, 100Hz | 3.4 |
| Dielectric Strength | >500 volts/mil |
| Dissipation Factor, 100Hz | 0.02 |
| Thermal Conductivity | 0.347 W/M*K |
| Volume Resistivity | 9.000000E+14 ohm/cm |
Product Description
Mold Max™ 60
Mold Max™ 60 is a Shore 60A tin catalyzed silicone mold rubber formulated for applications requiring high heat resistance (up to 560°F/294°C). It features a low mixed viscosity and cured rubber exhibits very low linear shrinkage. Parts A & B are mixed 100A & 3B by weight. Pot life is 40 minutes and cure time is 24 hours. Applications include making foundry patterns, flat pattern reproductions and casting low-melt metal alloys such as tin and pewter.