Key Differences
| Product Type |
|
|
| Mixed Viscosity | 650 cps | 11,000 cps |
| Mix Ratio By Volume | N/A (gram scale required) | 1A:1B |
| Pot Life | 60 minutes | 3 minutes |
| Cure Time | 24 hours | 20 minutes |
| Shore D Hardness | 80 | — |
| Shore A Hardness | — | 20 |
| Color | Clear | Translucent Green |
Disclaimer
Although we do our best to ensure accuracy, Smooth-On offers no warranties, promises, and/or representations of any kind, either expressed or implied, as to the accuracy, completeness, or reliability of the information contained on this Compare Tool, nor suitability of the information contained herein to your particular circumstances. Smooth-On assumes no liability for losses or damages of whatever nature (direct, indirect, consequential or other) associated with your use, or inability to use, the Compare Tool, or from your use (or failure to use) the information contained herein. Other useful tools include product technical bulletins and our extensive FAQ section. You can also contact our technical support team.All Technical Data
| EpoxAmite™ HT | EZ-Spray™ Silicone 20 | |
|---|---|---|
| Product Type |
|
|
| Mixed Viscosity | 650 cps | 11,000 cps |
| Mix Ratio By Volume | — | 1A:1B |
| Mix Ratio By Weight | 100A:33B | — |
| Pot Life | 60 minutes | 3 minutes |
| Thin Film Working Time | 180 minutes | — |
| Cure Time | 24 hours | 20 minutes |
| Shore D Hardness | 80 | — |
| Shore A Hardness | — | 20 |
| Specific Gravity | 1.10 g/cc | 1.08 g/cc |
| Specific Volume | 25.2 cu. in./lb. | 25.6 cu. in./lb. |
| Color | Clear | Translucent Green |
| Die B Tear Strength | — | 100 pli |
| Tensile Strength | — | 495 psi |
| Tensile Modulus | 342,000 psi | — |
| Ultimate Tensile | 6,500 psi | — |
| Tensile Elongation | 2.3 % | — |
| Elongation @ Break | — | 470 % |
| 100% Modulus | — | 47 psi |
| Compressive Strength | 16,600 psi | — |
| Compressive Modulus | 168,000 psi | — |
| Flexural Strength | 12,325 psi | — |
| Flexural Modulus | 429,000 psi | — |
| Shrinkage | — | <.001 in. / in. |
| Useful Temperature (min) | — | -65 °F |
| Useful Temperature (max) | — | 500 °F |
| Flexural Modulus on 6 ply / 10 oz. Laminate | 2,216,000 psi | — |
| Flexural Strength on 6 ply / 10 oz. Laminate | 20,700 psi | — |
| Heat Deflection With Post Cure | 300 °F | — |
| Tensile Modulus on 6 ply / 10 oz. Laminate | 2,150,000 psi | — |
| Ultimate Tensile on 6 ply / 10 oz. Laminate | 32,100 psi | — |
Product Description
EpoxAmite™ HT
EpoxAmite™ HT High Temperature Laminating Epoxy is a water clear, UV resistant laminating epoxy that resists high temperatures up to 300°F / 149°C when properly cured. Pot life is 1 hour and cure time is 24 hours at 73°F / 23°C (post cure required – see post cure schedule). Ultra-low viscosity ensures uniform wetting out and fast penetration of reinforcement materials during hand lay-up or vacuum infusion processes. Cured resin offers superior physical properties.
EpoxAmite™ HT High Temp Laminating Epoxy can be used with S-Glass, E-Glass, Kevlar and carbon fibers for making composite tooling or parts. Applications include making high temperature pre-preg parts, bonding fixtures, vacuum form molds and prototype injection molds.
Use as a backup laminating resin for EpoxAcoat™ HT high temperature surface coat epoxy.
› Click here for more EpoxAmite™ resin products.
EZ-Spray™ Silicone 20
EZ~Spray™ Silicone 20 is a sprayable silicone which cures quickly to soft rubbers with high elongation and tear strength. Liquid silicone is sprayed through the EZ~Spray™ Junior Cartridge System which is an economical alternative to expensive spray equipment. After a suitable thickness is attained, EZ~Spray™ Silicone 20 cures in about 20 minutes. EZ~Spray™ Silicone cures with negligible shrinkage to strong, durable silicone rubbers good for production casting of polyester, epoxy or urethane resins, gypsum, concrete and other materials.