Key Differences
| Product Type |
|
|
| Mixed Viscosity | 650 cps | 1,500 cps |
| Mix Ratio By Volume | N/A (gram scale required) | 1A:1B |
| Pot Life | 60 minutes | 30 minutes |
| Cure Time | 24 hours | 16 hours |
| Shore D Hardness | 80 | — |
| Shore A Hardness | — | 30 |
| Color | Clear | Off White |
Disclaimer
Although we do our best to ensure accuracy, Smooth-On offers no warranties, promises, and/or representations of any kind, either expressed or implied, as to the accuracy, completeness, or reliability of the information contained on this Compare Tool, nor suitability of the information contained herein to your particular circumstances. Smooth-On assumes no liability for losses or damages of whatever nature (direct, indirect, consequential or other) associated with your use, or inability to use, the Compare Tool, or from your use (or failure to use) the information contained herein. Other useful tools include product technical bulletins and our extensive FAQ section. You can also contact our technical support team.All Technical Data
| EpoxAmite™ HT | ReoFlex™ 30 | |
|---|---|---|
| Product Type |
|
|
| Mixed Viscosity | 650 cps | 1,500 cps |
| Mix Ratio By Volume | — | 1A:1B |
| Mix Ratio By Weight | 100A:33B | 1A:1B |
| Pot Life | 60 minutes | 30 minutes |
| Thin Film Working Time | 180 minutes | — |
| Cure Time | 24 hours | 16 hours |
| Shore D Hardness | 80 | — |
| Shore A Hardness | — | 30 |
| Specific Gravity | 1.10 g/cc | 1.01 g/cc |
| Specific Volume | 25.2 cu. in./lb. | 27.5 cu. in./lb. |
| Color | Clear | Off White |
| Die C Tear Strength | — | 82 pli |
| Tensile Strength | — | 450 psi |
| Tensile Modulus | 342,000 psi | — |
| Ultimate Tensile | 6,500 psi | — |
| Tensile Elongation | 2.3 % | — |
| Elongation @ Break | — | 1,000 % |
| 100% Modulus | — | 67 psi |
| Compressive Strength | 16,600 psi | — |
| Compressive Modulus | 168,000 psi | — |
| Flexural Strength | 12,325 psi | — |
| Flexural Modulus | 429,000 psi | — |
| Shrinkage | — | <.001 in. / in. |
| Flexural Modulus on 6 ply / 10 oz. Laminate | 2,216,000 psi | — |
| Flexural Strength on 6 ply / 10 oz. Laminate | 20,700 psi | — |
| Heat Deflection With Post Cure | 300 °F | — |
| Tensile Modulus on 6 ply / 10 oz. Laminate | 2,150,000 psi | — |
| Ultimate Tensile on 6 ply / 10 oz. Laminate | 32,100 psi | — |
Product Description
EpoxAmite™ HT
EpoxAmite™ HT High Temperature Laminating Epoxy is a water clear, UV resistant laminating epoxy that resists high temperatures up to 300°F / 149°C when properly cured. Pot life is 1 hour and cure time is 24 hours at 73°F / 23°C (post cure required – see post cure schedule). Ultra-low viscosity ensures uniform wetting out and fast penetration of reinforcement materials during hand lay-up or vacuum infusion processes. Cured resin offers superior physical properties.
EpoxAmite™ HT High Temp Laminating Epoxy can be used with S-Glass, E-Glass, Kevlar and carbon fibers for making composite tooling or parts. Applications include making high temperature pre-preg parts, bonding fixtures, vacuum form molds and prototype injection molds.
Use as a backup laminating resin for EpoxAcoat™ HT high temperature surface coat epoxy.
› Click here for more EpoxAmite™ resin products.
ReoFlex™ 30
ReoFlex™ urethane rubbers offer superior physical and performance properties for production casting of wax, plasters, and resins. ReoFlex™ urethanes are available in 20A, 30A, 40A, 50A and 60A Shore hardnesses and feature convenient one-to-one by volume mix ratios. Vacuum degassing is not necessary and ReoFlex™ rubbers cure with negligible shrinkage to a durable rubber that will last in production. ReoFlex™ “Wet” rubbers will shrink somewhat over time vs. “Dry” formulations.
ReoFlex™ mold rubbers are used for a variety of applications including making molds to reproduce sculpture and architectural elements, as well as for making special effects, toys and prototypes. Vibrant colors can be achieved by adding So-Strong™ Color Tints, available from Smooth-On.
Casting Concrete? Look into the VytaFlex™ series of urethane mold rubbers. VytaFlex™ urethanes were formulated specifically for casting concrete / pigmented concrete and feature Smooth-On’s exclusive ‘V-Polymer™’ technology.
FOR COMMERCIAL/INDUSTRIAL USE ONLY