Key Differences
| Product Type |
|
|
| Pot Life | 60 minutes | 4.5 hours |
| Cure Time | 24 hours | 7 days |
Disclaimer
Although we do our best to ensure accuracy, Smooth-On offers no warranties, promises, and/or representations of any kind, either expressed or implied, as to the accuracy, completeness, or reliability of the information contained on this Compare Tool, nor suitability of the information contained herein to your particular circumstances. Smooth-On assumes no liability for losses or damages of whatever nature (direct, indirect, consequential or other) associated with your use, or inability to use, the Compare Tool, or from your use (or failure to use) the information contained herein. Other useful tools include product technical bulletins and our extensive FAQ section. You can also contact our technical support team.All Technical Data
| EpoxAmite™ HT | Crystal Clear™ 206 | |
|---|---|---|
| Product Type |
|
|
| Mixed Viscosity | 650 cps | 600 cps |
| Mix Ratio By Weight | 100A:33B | 100A:90B |
| Pot Life | 60 minutes | 4.5 hours |
| Thin Film Working Time | 180 minutes | — |
| Cure Time | 24 hours | 7 days |
| Shore D Hardness | 80 | 80 |
| Specific Gravity | 1.10 g/cc | 1.036 g/cc |
| Specific Volume | 25.2 cu. in./lb. | 26.7 cu. in./lb. |
| Color | Clear | Clear |
| Tensile Strength | — | 2,500 psi |
| Tensile Modulus | 342,000 psi | 73,200 psi |
| Ultimate Tensile | 6,500 psi | — |
| Tensile Elongation | 2.3 % | — |
| Elongation @ Break | — | 10 % |
| Compressive Strength | 16,600 psi | 6,385 psi |
| Compressive Modulus | 168,000 psi | 40,000 psi |
| Flexural Strength | 12,325 psi | 10,650 psi |
| Flexural Modulus | 429,000 psi | 200,000 psi |
| Shrinkage | — | 0.002 in. / in. |
| Heat Deflection Temp | — | 120 °F |
| Flexural Modulus on 6 ply / 10 oz. Laminate | 2,216,000 psi | — |
| Flexural Strength on 6 ply / 10 oz. Laminate | 20,700 psi | — |
| Heat Deflection With Post Cure | 300 °F | — |
| Index of Refraction at 20°C | — | 1.49962 |
| Index of Refraction at 25°C | — | 1.49894 |
| Tensile Modulus on 6 ply / 10 oz. Laminate | 2,150,000 psi | — |
| Ultimate Tensile on 6 ply / 10 oz. Laminate | 32,100 psi | — |
Product Description
EpoxAmite™ HT
EpoxAmite™ HT High Temperature Laminating Epoxy is a water clear, UV resistant laminating epoxy that resists high temperatures up to 300°F / 149°C when properly cured. Pot life is 1 hour and cure time is 24 hours at 73°F / 23°C (post cure required – see post cure schedule). Ultra-low viscosity ensures uniform wetting out and fast penetration of reinforcement materials during hand lay-up or vacuum infusion processes. Cured resin offers superior physical properties.
EpoxAmite™ HT High Temp Laminating Epoxy can be used with S-Glass, E-Glass, Kevlar and carbon fibers for making composite tooling or parts. Applications include making high temperature pre-preg parts, bonding fixtures, vacuum form molds and prototype injection molds.
Use as a backup laminating resin for EpoxAcoat™ HT high temperature surface coat epoxy.
› Click here for more EpoxAmite™ resin products.
Crystal Clear™ 206
Crystal Clear™ 206 is a water white clear and made specifically for applications that require clarity. These rigid urethane casting resins differ only in working and demold times. Low viscosity ensures easy mixing and pouring. Crystal Clear™ resins cure at room temperature* with negligible shrinkage.
CAUTION: NOT FOR HOME USE. THIS PRODUCT IS FOR INDUSTRIAL USE ONLY. With adequate local exhaust ventilation, respiratory protection is not normally required when using this product. Where risk assessment shows air-purifying respirators are appropriate, follow OSHA respirator regulations and European Standards EN 141, 143 and 371. Protective clothing (gloves and long sleeves) is required to minimize the risk of dermal sensitization. If breathing is affected or a dermal rash develops, immediately cease using this product and seek medical attention. Read SDS before using.