Key Differences
| Product Type |
|
|
| Mixed Viscosity | 4,250 cps | 7,000 cps |
| Mix Ratio By Volume | 1A:1B | N/A (gram scale required) |
| Pot Life | 15 minutes | 90 minutes |
| Cure Time | 75 minutes | 4 hours |
| Barcol 935 Hardness | — | 93 |
| Shore A Hardness | 25 | — |
| Color | Light Blue | Black |
| Shrinkage | 0.0025 in. / in. | 0.001 in. / in. |
Disclaimer
Although we do our best to ensure accuracy, Smooth-On offers no warranties, promises, and/or representations of any kind, either expressed or implied, as to the accuracy, completeness, or reliability of the information contained on this Compare Tool, nor suitability of the information contained herein to your particular circumstances. Smooth-On assumes no liability for losses or damages of whatever nature (direct, indirect, consequential or other) associated with your use, or inability to use, the Compare Tool, or from your use (or failure to use) the information contained herein. Other useful tools include product technical bulletins and our extensive FAQ section. You can also contact our technical support team.All Technical Data
| OOMOO™ 25 | EpoxAcast™ 650 BLACK + 102 Hardener | |
|---|---|---|
| Product Type |
|
|
| Mixed Viscosity | 4,250 cps | 7,000 cps |
| Mix Ratio By Volume | 1A:1B | — |
| Mix Ratio By Weight | 100A:130B | 100A:13B |
| Pot Life | 15 minutes | 90 minutes |
| Cure Time | 75 minutes | 4 hours |
| Barcol 935 Hardness | — | 93 |
| Shore A Hardness | 25 | — |
| Specific Gravity | 1.34 g/cc | 1.52 g/cc |
| Specific Volume | 20.6 cu. in./lb. | 18.22 cu. in./lb. |
| Color | Light Blue | Black |
| Die B Tear Strength | 40 pli | — |
| Tensile Strength | 240 psi | — |
| Tensile Modulus | — | 1,503,000 psi |
| Ultimate Tensile | — | 6,000 psi |
| Tensile Elongation | — | 0.42 % |
| Elongation @ Break | 250 % | — |
| 100% Modulus | 100 psi | — |
| Compressive Strength | — | 16,350 psi |
| Compressive Modulus | — | 142,600 psi |
| Flexural Strength | — | 5,890 psi |
| Flexural Modulus | — | 710,000 psi |
| Shrinkage | 0.0025 in. / in. | 0.001 in. / in. |
| Heat Deflection Temp | — | 129 °F |
| Useful Temperature (min) | -65 °F | — |
| Useful Temperature (max) | 400 °F | — |
Product Description
OOMOO™ 25
No Vacuuming – No Scale – Easy To Use . . . OOMOO™ 25 is an easy to use tin cure silicone rubber compound that features a convenient one-to-one by volume mix ratio (no scale necessary). It has a low viscosity for easy mixing and pouring . . . vacuum degassing is not necessary. This product cures at room temperature with negligible shrinkage. OOMOO™ 25 has a 15-minute pot life and 75-minute cure time.
For The Novice Mold Maker - OOMOO™ silicones do not have great tear strength. They are good for making simple one or two-piece block molds. If you require a high tear strength silicone, Mold Max™ silicones are recommended.
OOMOO™ 25 is suitable for a variety of art-related and industrial applications including making one and two-piece block molds for sculpture and prototype reproduction, casting plaster, resins and wax. OOMOO™ silicones are also suitable for electrical potting and encapsulation applications.
EpoxAcast™ 650 BLACK + 102 Hardener
EpoxAcast™ 650 Black is a mineral filled general purpose casting epoxy that is low cost and versatile. It features a low mixed viscosity for minimal bubble entrapment.