| Product Type |
|
|
| Mixed Viscosity | 4,250 cps | Light Paste |
| Mix Ratio By Volume | 1A:1B | N/A (gram scale required) |
| Pot Life | 15 minutes | 40 minutes |
| Cure Time | 75 minutes | 24 hours |
| Shore D Hardness | — | 85 |
| Shore A Hardness | 25 | — |
| Color | Light Blue | Dark Red |
Disclaimer
Although we do our best to ensure accuracy, Smooth-On offers no warranties, promises, and/or representations of any kind, either expressed or implied, as to the accuracy, completeness, or reliability of the information contained on this Compare Tool, nor suitability of the information contained herein to your particular circumstances. Smooth-On assumes no liability for losses or damages of whatever nature (direct, indirect, consequential or other) associated with your use, or inability to use, the Compare Tool, or from your use (or failure to use) the information contained herein. Other useful tools include product technical bulletins and our extensive FAQ section. You can also contact our technical support team.All Technical Data
| OOMOO™ 25 | EpoxAcoat™ HT | |
|---|---|---|
| Product Type |
|
|
| Mixed Viscosity | 4,250 cps | Light Paste |
| Mix Ratio By Volume | 1A:1B | — |
| Mix Ratio By Weight | 100A:130B | 100A:18B |
| Pot Life | 15 minutes | 40 minutes |
| Thin Film Working Time | — | 75 minutes |
| Thin Film Recoat Time | — | 4 hours |
| Cure Time | 75 minutes | 24 hours |
| Shore D Hardness | — | 85 |
| Shore A Hardness | 25 | — |
| Specific Gravity | 1.34 g/cc | — |
| Specific Volume | 20.6 cu. in./lb. | — |
| Color | Light Blue | Dark Red |
| Die B Tear Strength | 40 pli | — |
| Tensile Strength | 240 psi | — |
| Elongation @ Break | 250 % | — |
| 100% Modulus | 100 psi | — |
| Shrinkage | 0.0025 in. / in. | — |
| Heat Deflection Temp | — | 133 °F |
| Useful Temperature (min) | -65 °F | — |
| Useful Temperature (max) | 400 °F | — |
| Heat Deflection With Post Cure | — | 284 °F |
Product Description
OOMOO™ 25
No Vacuuming – No Scale – Easy To Use . . . OOMOO™ 25 is an easy to use tin cure silicone rubber compound that features a convenient one-to-one by volume mix ratio (no scale necessary). It has a low viscosity for easy mixing and pouring . . . vacuum degassing is not necessary. This product cures at room temperature with negligible shrinkage. OOMOO™ 25 has a 15-minute pot life and 75-minute cure time.
For The Novice Mold Maker - OOMOO™ silicones do not have great tear strength. They are good for making simple one or two-piece block molds. If you require a high tear strength silicone, Mold Max™ silicones are recommended.
OOMOO™ 25 is suitable for a variety of art-related and industrial applications including making one and two-piece block molds for sculpture and prototype reproduction, casting plaster, resins and wax. OOMOO™ silicones are also suitable for electrical potting and encapsulation applications.
EpoxAcoat™ HT
EpoxAcoat™ HT is a slightly thixotropic epoxy gel coat that offers high heat resistance (post cure required). Cured epoxy is tough and offers exceptional abrasion resistance. This surface coat will wet out well over a variety of surfaces with good sag resistance. Applications include laminating, precision tooling, master and pattern making, core boxes and fixtures.
Use as a surface coat for EpoxAmite™ HT high temperature laminating epoxy.