Product Type |
|
|
Mixed Viscosity | Variable | Paste |
Cure Time | 90 minutes | 24 hours |
Barcol 935 Hardness | — | 75 |
Color | White | Black |
Matrix Dryve™ | PC-3™ | |
---|---|---|
Product Type |
|
|
Mixed Viscosity | Variable | Paste |
Mix Ratio By Volume | 3 Parts Powder : 1 Part Water By Volume | 1A:1B |
Mix Ratio By Weight | 100 Parts Powder : 27 Parts Water by Weight | 1A:1B |
Pot Life | 20 minutes | 20 minutes |
Handling Time | — | 2 hours |
Cure Time | 90 minutes | 24 hours |
Barcol 935 Hardness | — | 75 |
Specific Gravity | — | 1.4 g/cc |
Specific Volume | 17.45 cu. in./lb. | 20 cu. in./lb. |
Color | White | Black |
Tensile Strength | 3300 - 5500 psi | 3,000 psi |
Compressive Strength | 6500 - 9500 psi | — |
Flexural Strength | — | 5,000 psi |
Shrinkage | — | 0.003 in. / in. |
Useful Temperature (max) | 200 °F | — |
Compressive Yield Strength | — | 5,000 psi |
Density | 99 lbs lb/ft³ | — |
Flexural Strength on 6 ply / 10 oz. Laminate | 7500 - 9800 psi | — |
Freeze / Thaw Resistance | 300 cycles | — |
Impact Resistance | 175 in lb / in² | — |
Water Absorption | 0.5 ‰ after 24 hour water soak | — |
Matrix Dryve™ is a versatile all-powder polymer modified gypsum system that has superior physical and performance properties compared to regular gypsum products. It is an “all-powder” alternative to our original Matrix™ NEO powder/liquid system.
Smooth-On PC-3™ Laboratory Table Top Cement is a two-component, black epoxy resin compound designed to join, bond and caulk sections of laboratory counters and tables. This epoxy resin cement is heavily filled and will adhere to vertical surfaces without sagging. It cures at room temperature with extremely low shrinkage.