Product Type |
|
|
Mixed Viscosity | 2,000 cps | 45,000 cps |
Mix Ratio By Volume | 1A:1B | N/A (gram scale required) |
Cure Time | 4 hours | 24 hours |
Shore A Hardness | 00-45 | 40 |
Color | Water Clear Translucent | Mint Green |
Die B Tear Strength | 50 pli | 120 pli |
Tensile Strength | 315 psi | 550 psi |
Elongation @ Break | 980 % | 250 % |
100% Modulus | 12 psi | 190 psi |
Ecoflex™ 00-45 Near Clear™ | Mold Max™ 40 | |
---|---|---|
Product Type |
|
|
Mixed Viscosity | 2,000 cps | 45,000 cps |
Mix Ratio By Volume | 1A:1B | — |
Mix Ratio By Weight | — | 100A:10B |
Pot Life | 45 minutes | 45 minutes |
Cure Time | 4 hours | 24 hours |
Shore A Hardness | 00-45 | 40 |
Specific Gravity | 1.06 g/cc | 1.14 g/cc |
Specific Volume | 26.2 cu. in./lb. | 24.3 cu. in./lb. |
Color | Water Clear Translucent | Mint Green |
Die B Tear Strength | 50 pli | 120 pli |
Tensile Strength | 315 psi | 550 psi |
Elongation @ Break | 980 % | 250 % |
100% Modulus | 12 psi | 190 psi |
Shrinkage | <.001 in. / in. | 0.004 in. / in. |
Useful Temperature (min) | -65 °F | -65 °F |
Useful Temperature (max) | 450 °F | 400 °F |
Dielectric Constant, 100Hz | — | 3.29 |
Dielectric Strength | — | 330 volts/mil |
Dissipation Factor, 100Hz | — | 0.005 |
Volume Resistance | — | 8.29E+11 ohm |
Volume Resistivity | — | 5.83E+13 ohm/cm |
Ecoflex™ 00-45 Near Clear™ is a very soft, platinum silicone that is clearer than other Ecoflex™ silicones. Versatile and easy to use, Ecoflex™ 00-45 Near Clear™ rubber is mixed 1A:1B by weight or volume and cures at room temperature with negligible shrinkage. Low viscosity ensures easy mixing and de-airing. Cured material is skin safe and certified by an independent laboratory.
Mold Max™ Silicones are tin-cured silicone mold rubber compounds that have exceptional working properties and library life. Mold Max™ Silicones feature Smooth-On’s exclusive “Libra™” catalyst for long library life. Mold Max™ silicones can be pigmented with Silc Pig™ silicone colorants. Pot life for the pourable silicones is 45 minutes and they cure overnight at room temperature.
Vacuum degassing mixed material using a vacuum pump and chamber to remove entrapped air is recommended.