Product Type |
|
|
Pot Life | 45 minutes | 25 minutes |
Cure Time | 4 hours | 48 hours |
Shore A Hardness | 00-45 | 80 |
Color | Water Clear Translucent | Light Amber |
Tensile Strength | 315 psi | 900 psi |
Elongation @ Break | 980 % | 750 % |
100% Modulus | 12 psi | 400 psi |
Ecoflex™ 00-45 Near Clear™ | PMC™-780 DRY | |
---|---|---|
Product Type |
|
|
Mixed Viscosity | 2,000 cps | 2,000 cps |
Mix Ratio By Volume | 1A:1B | 2A:1B |
Mix Ratio By Weight | — | 2A:1B |
Pot Life | 45 minutes | 25 minutes |
Cure Time | 4 hours | 48 hours |
Shore A Hardness | 00-45 | 80 |
Specific Gravity | 1.06 g/cc | 1.02 g/cc |
Specific Volume | 26.2 cu. in./lb. | 27.2 cu. in./lb. |
Color | Water Clear Translucent | Light Amber |
Die B Tear Strength | 50 pli | — |
Die C Tear Strength | — | 200 pli |
Tensile Strength | 315 psi | 900 psi |
Elongation @ Break | 980 % | 750 % |
100% Modulus | 12 psi | 400 psi |
Shrinkage | <.001 in. / in. | <.001 in. / in. |
Useful Temperature (min) | -65 °F | — |
Useful Temperature (max) | 450 °F | — |
Ecoflex™ 00-45 Near Clear™ is a very soft, platinum silicone that is clearer than other Ecoflex™ silicones. Versatile and easy to use, Ecoflex™ 00-45 Near Clear™ rubber is mixed 1A:1B by weight or volume and cures at room temperature with negligible shrinkage. Low viscosity ensures easy mixing and de-airing. Cured material is skin safe and certified by an independent laboratory.
PMC™-780 is a premium performance urethane rubber that offers exceptional strength, durability and abrasion resistance. PMC™-780 DOES NOT CONTAIN MOCA – a known cancer causing agent and hazard. Mixed two parts A to one part B by weight or volume, PMC™-780 urethane pours easily and cures at room temperature with negligible shrinkage to a solid Shore 80A rubber.
Pick The One Best Suited For Your Application: Original PMC™-780 Dry does not exude oil. New PMC™-780 Wet contains a built in release agent to aid in demolding concrete. (Note: “wet” rubber has a higher net shrinkage value over time vs. “dry “ rubber.)