Product Type |
|
|
Mixed Viscosity | 2,000 cps | Brushable |
Pot Life | 45 minutes | 18 minutes |
Cure Time | 4 hours | 16 hours |
Shore A Hardness | 00-45 | 40 |
Color | Water Clear Translucent | Grey |
Tensile Strength | 315 psi | 420 psi |
Elongation @ Break | 980 % | 577 % |
Ecoflex™ 00-45 Near Clear™ | EZ-Mix™ 40 | |
---|---|---|
Product Type |
|
|
Mixed Viscosity | 2,000 cps | Brushable |
Mix Ratio By Volume | 1A:1B | 1A:1B |
Mix Ratio By Weight | — | 100A:95B |
Pot Life | 45 minutes | 18 minutes |
Thin Film Recoat Time | — | 60 minutes |
Cure Time | 4 hours | 16 hours |
Shore A Hardness | 00-45 | 40 |
Specific Gravity | 1.06 g/cc | 1.025 g/cc |
Specific Volume | 26.2 cu. in./lb. | 27 cu. in./lb. |
Color | Water Clear Translucent | Grey |
Die B Tear Strength | 50 pli | — |
Die C Tear Strength | — | 67 pli |
Tensile Strength | 315 psi | 420 psi |
Elongation @ Break | 980 % | 577 % |
100% Modulus | 12 psi | — |
Shrinkage | <.001 in. / in. | <.001 in. / in. |
Useful Temperature (min) | -65 °F | — |
Useful Temperature (max) | 450 °F | — |
Ecoflex™ 00-45 Near Clear™ is a very soft, platinum silicone that is clearer than other Ecoflex™ silicones. Versatile and easy to use, Ecoflex™ 00-45 Near Clear™ rubber is mixed 1A:1B by weight or volume and cures at room temperature with negligible shrinkage. Low viscosity ensures easy mixing and de-airing. Cured material is skin safe and certified by an independent laboratory.
EZ~MIX™ 40 is a brushable polyurethane rubber mold compound that mixes and applies easily. Two liquids (Part A and Part B) are measured and combined in equal amounts by volume (no scale is necessary). After a few minutes of mixing, EZ~MIX™ 40 is ready to be applied to a vertical surface with a brush. After a suitable thickness is attained (multiple layers), EZ~MIX™ 40 cures overnight with negligible shrinkage to a flexible, durable mold rubber. Following the application of a support shell, a rubber mold made with EZ~MIX™ 40 is suitable for casting a variety of materials including wax, gypsum, urethane/epoxy resins, concrete, cement, etc.