C
mpare
T
l
Key Differences
| Product Type |
|
|
| Mixed Viscosity | 1,800 cps | 23,000 cps |
| Mix Ratio By Volume | 1A:1B | N/A (gram scale required) |
| Pot Life | 50 minutes | 30 minutes |
| Cure Time | 16 hours | 3 hours |
| Shore D Hardness | — | 90 |
| Shore A Hardness | 60 | — |
| Specific Volume | 26.7 cu. in./lb. | 16.7 cu. in./lb. |
| Color | Off White | Grey |
Disclaimer
Although we do our best to ensure accuracy, Smooth-On offers no warranties, promises, and/or representations of any kind, either expressed or implied, as to the accuracy, completeness, or reliability of the information contained on this Compare Tool, nor suitability of the information contained herein to your particular circumstances. Smooth-On assumes no liability for losses or damages of whatever nature (direct, indirect, consequential or other) associated with your use, or inability to use, the Compare Tool, or from your use (or failure to use) the information contained herein. Other useful tools include product technical bulletins and our extensive FAQ section. You can also contact our technical support team.All Technical Data
| ReoFlex™ 60 | EpoxAcast™ 655 + 101 Hardener | |
|---|---|---|
| Product Type |
|
|
| Mixed Viscosity | 1,800 cps | 23,000 cps |
| Mix Ratio By Volume | 1A:1B | — |
| Mix Ratio By Weight | 1A:1B | 100A:10B |
| Pot Life | 50 minutes | 30 minutes |
| Cure Time | 16 hours | 3 hours |
| Shore D Hardness | — | 90 |
| Shore A Hardness | 60 | — |
| Specific Gravity | 1.04 g/cc | 1.66 g/cc |
| Specific Volume | 26.7 cu. in./lb. | 16.7 cu. in./lb. |
| Color | Off White | Grey |
| Die C Tear Strength | 132 pli | — |
| Tensile Strength | 782 psi | — |
| Tensile Modulus | — | 2,040,000 psi |
| Ultimate Tensile | — | 4,810 psi |
| Tensile Elongation | — | 0.54 % |
| Elongation @ Break | 581 % | — |
| 100% Modulus | 256 psi | — |
| Compressive Strength | — | 12,500 psi |
| Compressive Modulus | — | 125,500 psi |
| Flexural Strength | — | 7,660 psi |
| Flexural Modulus | — | 1,403,000 psi |
| Shrinkage | <.001 in. / in. | 0.0006 in. / in. |
| Heat Deflection Temp | — | 135 °F |
| Thermal Conductivity | — | 0.675 W/M*K |
Product Description
ReoFlex™ 60
ReoFlex™ urethane rubbers offer superior physical and performance properties for production casting of wax, plasters, and resins. ReoFlex™ urethanes are available in 20A, 30A, 40A, 50A and 60A Shore hardnesses and feature convenient one-to-one by volume mix ratios. Vacuum degassing is not necessary and ReoFlex™ rubbers cure with negligible shrinkage to a durable rubber that will last in production. ReoFlex™ “Wet” rubbers will shrink somewhat over time vs. “Dry” formulations.
ReoFlex™ mold rubbers are used for a variety of applications including making molds to reproduce sculpture and architectural elements, as well as for making special effects, toys and prototypes. Vibrant colors can be achieved by adding So-Strong™ Color Tints, available from Smooth-On.
Casting Concrete? Look into the VytaFlex™ series of urethane mold rubbers. VytaFlex™ urethanes were formulated specifically for casting concrete / pigmented concrete and feature Smooth-On’s exclusive ‘V-Polymer™’ technology.
FOR COMMERCIAL/INDUSTRIAL USE ONLY
› Click here for more ReoFlex™ rubber products.
EpoxAcast™ 655 + 101 Hardener
EpoxAcast™ 655 (formerly Metalset™ A-30) is a versatile aluminum filled castable epoxy resin that is very hard and strong. It is dimensionally stable, even when mass cast up to 512 in³ / 8,390 cm³.