Key Differences
| Product Type |
|
|
| Mixed Viscosity | 1,800 cps | 5,400 cps |
| Pot Life | 50 minutes | 3.5 minutes |
| Cure Time | 16 hours | 2.5 hours |
| Shore A Hardness | 60 | 85 |
| Color | Off White | Black |
| Die C Tear Strength | 132 pli | 175 pli |
| Tensile Strength | 782 psi | 3,400 psi |
| Elongation @ Break | 581 % | 121 % |
Disclaimer
Although we do our best to ensure accuracy, Smooth-On offers no warranties, promises, and/or representations of any kind, either expressed or implied, as to the accuracy, completeness, or reliability of the information contained on this Compare Tool, nor suitability of the information contained herein to your particular circumstances. Smooth-On assumes no liability for losses or damages of whatever nature (direct, indirect, consequential or other) associated with your use, or inability to use, the Compare Tool, or from your use (or failure to use) the information contained herein. Other useful tools include product technical bulletins and our extensive FAQ section. You can also contact our technical support team.All Technical Data
| ReoFlex™ 60 | Black Panther™ 85 | |
|---|---|---|
| Product Type |
|
|
| Mixed Viscosity | 1,800 cps | 5,400 cps |
| Mix Ratio By Volume | 1A:1B | 1A:1B |
| Mix Ratio By Weight | 1A:1B | 100A:92B |
| Pot Life | 50 minutes | 3.5 minutes |
| Cure Time | 16 hours | 2.5 hours |
| Shore A Hardness | 60 | 85 |
| Specific Gravity | 1.04 g/cc | 1.11 g/cc |
| Specific Volume | 26.7 cu. in./lb. | 25 cu. in./lb. |
| Color | Off White | Black |
| Die C Tear Strength | 132 pli | 175 pli |
| Tensile Strength | 782 psi | 3,400 psi |
| Elongation @ Break | 581 % | 121 % |
| 100% Modulus | 256 psi | — |
| Shrinkage | <.001 in. / in. | 0.0038 in. / in. |
| Modulus of Elasticity in Tension | — | 700 psi |
Product Description
ReoFlex™ 60
ReoFlex™ urethane rubbers offer superior physical and performance properties for production casting of wax, plasters, and resins. ReoFlex™ urethanes are available in 20A, 30A, 40A, 50A and 60A Shore hardnesses and feature convenient one-to-one by volume mix ratios. Vacuum degassing is not necessary and ReoFlex™ rubbers cure with negligible shrinkage to a durable rubber that will last in production. ReoFlex™ “Wet” rubbers will shrink somewhat over time vs. “Dry” formulations.
ReoFlex™ mold rubbers are used for a variety of applications including making molds to reproduce sculpture and architectural elements, as well as for making special effects, toys and prototypes. Vibrant colors can be achieved by adding So-Strong™ Color Tints, available from Smooth-On.
Casting Concrete? Look into the VytaFlex™ series of urethane mold rubbers. VytaFlex™ urethanes were formulated specifically for casting concrete / pigmented concrete and feature Smooth-On’s exclusive ‘V-Polymer™’ technology.
FOR COMMERCIAL/INDUSTRIAL USE ONLY
› Click here for more ReoFlex™ rubber products.
Black Panther™ 85
Black Panther™ 85 is a two-component, fast curing liquid adhesive for repairing holes, tears and splits in steel / fabric corded rubber conveyor belts, providing high wear and abrasion resistance.
It also provides a strong, flexible bond between a variety of substrates including plaster, wood, cement, stone, glass, hard plastics and a variety of metals.
Working time is 3.5 minutes and cure time is 2.5 hours at room temperature (73° F / 23° C).