Product Type |
|
|
Mixed Viscosity | Brushable | Variable |
Mix Ratio By Volume | 1A:1B | N/A (gram scale required) |
Pot Life | 20 minutes | 30 minutes |
Cure Time | 16 hours | 24 hours |
Shore D Hardness | — | 75 |
Shore A Hardness | 50 | — |
Color | Off White | Beige |
Brush-On™ 50 | EPSILON™ + 102 Hardener | |
---|---|---|
Product Type |
|
|
Mixed Viscosity | Brushable | Variable |
Mix Ratio By Volume | 1A:1B | — |
Mix Ratio By Weight | 100A:125B | 100A:25B |
Pot Life | 20 minutes | 30 minutes |
Thin Film Working Time | — | 120 minutes |
Thin Film Recoat Time | — | 180 minutes |
Tack Free Time | — | 5 hours |
Cure Time | 16 hours | 24 hours |
Shore D Hardness | — | 75 |
Shore A Hardness | 50 | — |
Specific Gravity | 1.17 g/cc | 1.14 g/cc |
Specific Volume | 23.7 cu. in./lb. | 24.3 cu. in./lb. |
Color | Off White | Beige |
Die C Tear Strength | 80 pli | — |
Tensile Strength | 500 psi | — |
Elongation @ Break | 400 % | — |
Shrinkage | <.001 in. / in. | — |
Smooth-On’s Brush-On™ Series of mold rubbers are extremely versatile and are famous for their abrasion resistance and high tear strength. They have the convenience of a one-to-one mix ratio and are easy to mix and apply with a brush or spatula.
EPSILON™ is a thixotropic epoxy coating that self thickens for brushing onto a variety of surfaces without sagging. Parts A and B mix together easily, and the mixture wets out uniformly. This product is not sensitive to moisture or humidity. EPSILON™ cures at room temperature to an impact resistant plastic which exhibits good compressive and flexural strength.