Simpact™ 60A

EpoxAcoat™ GREY vs. Simpact™ 60A

Tough, Fast Setting Urethane

 View Product

Vs.

Add Material to Compare

start over

Key Differences

Product Type
  • Urethane Rubber
  • Urethane Resins
  • Epoxy Casting and Laminating Resins
  • Epoxy and Urethane Coatings
Mixed Viscosity1,100 cpsLight Paste
Pot Life4 minutes20 minutes
Cure Time48 hours16 hours
Barcol 935 Hardness87
Shore D Hardness85
Shore A Hardness60
Specific Volume25.7 cu. in./lb.19.4 cu. in./lb.
ColorWhiteGrey
Disclaimer
Although we do our best to ensure accuracy, Smooth-On offers no warranties, promises, and/or representations of any kind, either expressed or implied, as to the accuracy, completeness, or reliability of the information contained on this Compare Tool, nor suitability of the information contained herein to your particular circumstances. Smooth-On assumes no liability for losses or damages of whatever nature (direct, indirect, consequential or other) associated with your use, or inability to use, the Compare Tool, or from your use (or failure to use) the information contained herein. Other useful tools include product technical bulletins and our extensive FAQ section. You can also contact our technical support team.

All Technical Data

Simpact™ 60AEpoxAcoat™ GREY
Product Type
  • Urethane Rubber
  • Urethane Resins
  • Epoxy Casting and Laminating Resins
  • Epoxy and Urethane Coatings
Mixed Viscosity1,100 cpsLight Paste
Mix Ratio By Volume1A:1B5A:1B
Mix Ratio By Weight100A:94B100A:15B
Pot Life4 minutes20 minutes
Thin Film Working Time40 minutes
Thin Film Recoat Time60 minutes
Tack Free Time4 hours
Handling Time2 hours
Cure Time48 hours16 hours
Barcol 935 Hardness87
Shore D Hardness85
Shore A Hardness60
Specific Gravity1.08 g/cc1.43 g/cc
Specific Volume25.7 cu. in./lb.19.4 cu. in./lb.
ColorWhiteGrey
Die C Tear Strength142 pli
Tensile Strength990 psi
Ultimate Tensile26,000 psi
Elongation @ Break400 %
100% Modulus312 psi
Compressive Strength24,000 psi
Flexural Strength30,000 psi
Shrinkage<.007 in. / in.0.00015 in. / in.
Heat Deflection Temp133 °F

Product Description

Simpact™ 60A

Simpact™ 60A urethane is a low odor, fast-setting urethane elastomer which offers very high tear strength, impact resistance and wear resistance. Simpact™ urethanes are phthalate free, mercury free and MOCA free. Simpact™ urethanes pour easily. Working time is 4 minutes, handling time is 2 hours and full cure time is 48 hours at room temperature.

Cured rubber has exceptional performance characteristics and dimensional stability. Simpact™ urethanes can be colored with SO-Strong™, UVO™ or Ignite™ colorants. Simpact™ urethanes are suitable for making impact resistant props, prototypes and display pieces.

This material may congeal if exposed to cold temperatures. To reconstitute, Part A & B must be heated to 90°F (33°C) then thoroughly mixed to an even consistency.

Click here for more Simpact™ products.

Read More

EpoxAcoat™ GREY

EpoxAcoat™ RED, GREY, WHITE and NEUTRAL are thixotropic epoxy gel coats which are widely used for hand laminating and tooling applications. They are tough and strong surface coat resins which cure at room temperature and offer exceptional abrasion resistance. EpoxAcoat™ NEUTRAL is formulated “color neutral” specifically for adding color pigments and fillers. For high temperature applications (to 284°F / 140°C) use EpoxAcoat HT™ (see separate technical bulletin).

Read More

Select a Material from a Category Below

Silicone Rubber - Tin Cure ›

Silicone Rubber - Platinum Cure ›

Silicone Expanding Foams - Platinum Cure ›

Urethane Rubber ›

Polysulfide Rubber ›

Urethane Resins ›

Urethane Expanding Foams ›

Epoxy Casting and Laminating Resins ›

Epoxy Putties ›

Epoxy and Urethane Coatings ›

Flame Rated Materials ›

Adhesives ›

Lifecasting Materials ›

Skin Safe FX Materials ›

Polymer Modifiers for Concrete and Gypsum ›