Product Type |
|
|
Mixed Viscosity | 1,100 cps | 30,000 cps |
Mix Ratio By Volume | 1A:1B | N/A (gram scale required) |
Pot Life | 4 minutes | 40 minutes |
Cure Time | 48 hours | 24 hours |
Shore A Hardness | 60 | 30 |
Color | White | Blue |
Tensile Strength | 990 psi | 550 psi |
100% Modulus | 312 psi | 95 psi |
Simpact™ 60A | Mold Max™ XLS™ II | |
---|---|---|
Product Type |
|
|
Mixed Viscosity | 1,100 cps | 30,000 cps |
Mix Ratio By Volume | 1A:1B | — |
Mix Ratio By Weight | 100A:94B | 100A:10B |
Pot Life | 4 minutes | 40 minutes |
Handling Time | 2 hours | — |
Cure Time | 48 hours | 24 hours |
Shore A Hardness | 60 | 30 |
Specific Gravity | 1.08 g/cc | 1.22 g/cc |
Specific Volume | 25.7 cu. in./lb. | 22.7 cu. in./lb. |
Color | White | Blue |
Die B Tear Strength | — | 110 pli |
Die C Tear Strength | 142 pli | — |
Tensile Strength | 990 psi | 550 psi |
Elongation @ Break | 400 % | 375 % |
100% Modulus | 312 psi | 95 psi |
Shrinkage | <.007 in. / in. | 0.001 in. / in. |
Useful Temperature (min) | — | -65 °F |
Useful Temperature (max) | — | 400 °F |
Dielectric Constant, 100Hz | — | 3.4 |
Dielectric Strength | — | >360 volts/mil |
Dissipation Factor, 100Hz | — | 0.002 |
Thermal Conductivity | — | 0.24 W/M*K |
Volume Resistivity | — | 9.000000E+15 ohm/cm |
Simpact™ 60A urethane is a low odor, fast-setting urethane elastomer which offers very high tear strength, impact resistance and wear resistance. Simpact™ urethanes are phthalate free, mercury free and MOCA free. Simpact™ urethanes pour easily. Working time is 4 minutes, handling time is 2 hours and full cure time is 48 hours at room temperature.
Cured rubber has exceptional performance characteristics and dimensional stability. Simpact™ urethanes can be colored with SO-Strong™, UVO™ or Ignite™ colorants. Simpact™ urethanes are suitable for making impact resistant props, prototypes and display pieces.
This material may congeal if exposed to cold temperatures. To reconstitute, Part A & B must be heated to 90°F (33°C) then thoroughly mixed to an even consistency.
Mold Max™ XLS™ II is a Shore 30A tin-catalyzed silicone mold rubber that exhibits very low long-term shrinkage. XLS™ II molds last longer than other silicones in production when casting chemically harsh resins such as epoxies and polyesters as well as urethane foams.
Mix ratio is 100A:10B by weight. Pot life is 40 minutes and cure time is 24 hours at room temperature. Mold Max™ XLS™ II silicone will reproduce the finest detail and is suitable for a variety of industrial and art related applications including making production molds for, reproducing prototypes, furniture, sculpture and architectural elements. Mold Max™ XLS™ II can be thickened with THI‑VEX™ additive for brush-on applications.
Vacuum degassing mixed material using a vacuum pump and chamber to remove entrapped air is recommended.