Product Type |
|
|
Mixed Viscosity | 1,100 cps | 20,000 cps |
Pot Life | 4 minutes | 30 minutes |
Cure Time | 48 hours | 3.5 hours |
Shore A Hardness | 60 | 20 |
Color | White | Translucent Green |
Tensile Strength | 990 psi | 550 psi |
100% Modulus | 312 psi | 46 psi |
Simpact™ 60A | EZ-Brush™ Vac Bag Silicone | |
---|---|---|
Product Type |
|
|
Mixed Viscosity | 1,100 cps | 20,000 cps |
Mix Ratio By Volume | 1A:1B | 1A:1B |
Mix Ratio By Weight | 100A:94B | 1A:1B |
Pot Life | 4 minutes | 30 minutes |
Handling Time | 2 hours | — |
Cure Time | 48 hours | 3.5 hours |
Shore A Hardness | 60 | 20 |
Specific Gravity | 1.08 g/cc | 1.08 g/cc |
Specific Volume | 25.7 cu. in./lb. | 25.7 cu. in./lb. |
Color | White | Translucent Green |
Die B Tear Strength | — | 120 pli |
Die C Tear Strength | 142 pli | — |
Tensile Strength | 990 psi | 550 psi |
Elongation @ Break | 400 % | 364 % |
100% Modulus | 312 psi | 46 psi |
Shrinkage | <.007 in. / in. | <.001 in. / in. |
Simpact™ 60A urethane is a low odor, fast-setting urethane elastomer which offers very high tear strength, impact resistance and wear resistance. Simpact™ urethanes are phthalate free, mercury free and MOCA free. Simpact™ urethanes pour easily. Working time is 4 minutes, handling time is 2 hours and full cure time is 48 hours at room temperature.
Cured rubber has exceptional performance characteristics and dimensional stability. Simpact™ urethanes can be colored with SO-Strong™, UVO™ or Ignite™ colorants. Simpact™ urethanes are suitable for making impact resistant props, prototypes and display pieces.
This material may congeal if exposed to cold temperatures. To reconstitute, Part A & B must be heated to 90°F (33°C) then thoroughly mixed to an even consistency.
EZ-Brush™ Vac Bag Silicone is a brushable platinum cure silicone developed especially for making high performance, reusable vacuum bags. EZ-Brush™ Vac Bag Silicone is easy to mix and apply. Mix ratio is 1A:1B by volume and rubber can be applied with a brush or spatula to vertical surfaces without sagging.