Product Type |
|
|
Mixed Viscosity | 1,100 cps | 1,500 cps |
Pot Life | 4 minutes | 30 minutes |
Cure Time | 48 hours | 16 hours |
Shore A Hardness | 60 | 30 |
Color | White | Off White |
Die C Tear Strength | 142 pli | 82 pli |
Tensile Strength | 990 psi | 450 psi |
Elongation @ Break | 400 % | 1,000 % |
100% Modulus | 312 psi | 67 psi |
Simpact™ 60A | ReoFlex™ 30 | |
---|---|---|
Product Type |
|
|
Mixed Viscosity | 1,100 cps | 1,500 cps |
Mix Ratio By Volume | 1A:1B | 1A:1B |
Mix Ratio By Weight | 100A:94B | 1A:1B |
Pot Life | 4 minutes | 30 minutes |
Handling Time | 2 hours | — |
Cure Time | 48 hours | 16 hours |
Shore A Hardness | 60 | 30 |
Specific Gravity | 1.08 g/cc | 1.01 g/cc |
Specific Volume | 25.7 cu. in./lb. | 27.5 cu. in./lb. |
Color | White | Off White |
Die C Tear Strength | 142 pli | 82 pli |
Tensile Strength | 990 psi | 450 psi |
Elongation @ Break | 400 % | 1,000 % |
100% Modulus | 312 psi | 67 psi |
Shrinkage | <.007 in. / in. | <.001 in. / in. |
Simpact™ 60A urethane is a low odor, fast-setting urethane elastomer which offers very high tear strength, impact resistance and wear resistance. Simpact™ urethanes are phthalate free, mercury free and MOCA free. Simpact™ urethanes pour easily. Working time is 4 minutes, handling time is 2 hours and full cure time is 48 hours at room temperature.
Cured rubber has exceptional performance characteristics and dimensional stability. Simpact™ urethanes can be colored with SO-Strong™, UVO™ or Ignite™ colorants. Simpact™ urethanes are suitable for making impact resistant props, prototypes and display pieces.
This material may congeal if exposed to cold temperatures. To reconstitute, Part A & B must be heated to 90°F (33°C) then thoroughly mixed to an even consistency.
ReoFlex™ urethane rubbers offer superior physical and performance properties for production casting of wax, plasters, and resins. ReoFlex™ urethanes are available in 20A, 30A, 40A, 50A and 60A Shore hardnesses and feature convenient one-to-one by volume mix ratios. Vacuum degassing is not necessary and ReoFlex™ rubbers cure with negligible shrinkage to a durable rubber that will last in production. ReoFlex™ “Wet” rubbers will shrink somewhat over time vs. “Dry” formulations.
ReoFlex™ mold rubbers are used for a variety of applications including making molds to reproduce sculpture and architectural elements, as well as for making special effects, toys and prototypes. Vibrant colors can be achieved by adding So-Strong™ Color Tints, available from Smooth-On.
Casting Concrete? Look into the VytaFlex™ series of urethane mold rubbers. VytaFlex™ urethanes were formulated specifically for casting concrete / pigmented concrete and feature Smooth-On’s exclusive ‘V-Polymer™’ technology.