Key Differences
| Product Type |
|
|
| Mixed Viscosity | 2,000 cps | 650 cps |
| Pot Life | 20 minutes | 60 minutes |
| Cure Time | 16 hours | 24 hours |
| Shore D Hardness | 60 | 80 |
| Color | Translucent White | Clear |
Disclaimer
Although we do our best to ensure accuracy, Smooth-On offers no warranties, promises, and/or representations of any kind, either expressed or implied, as to the accuracy, completeness, or reliability of the information contained on this Compare Tool, nor suitability of the information contained herein to your particular circumstances. Smooth-On assumes no liability for losses or damages of whatever nature (direct, indirect, consequential or other) associated with your use, or inability to use, the Compare Tool, or from your use (or failure to use) the information contained herein. Other useful tools include product technical bulletins and our extensive FAQ section. You can also contact our technical support team.All Technical Data
| TASK™ 11 | EpoxAmite™ HT | |
|---|---|---|
| Product Type |
|
|
| Mixed Viscosity | 2,000 cps | 650 cps |
| Mix Ratio By Weight | 100A:100B | 100A:33B |
| Pot Life | 20 minutes | 60 minutes |
| Thin Film Working Time | — | 180 minutes |
| Cure Time | 16 hours | 24 hours |
| Shore D Hardness | 60 | 80 |
| Specific Gravity | 1.12 g/cc | 1.10 g/cc |
| Specific Volume | 24.7 cu. in./lb. | 25.2 cu. in./lb. |
| Color | Translucent White | Clear |
| Tensile Strength | 2,500 psi | — |
| Tensile Modulus | — | 342,000 psi |
| Ultimate Tensile | — | 6,500 psi |
| Tensile Elongation | — | 2.3 % |
| Elongation @ Break | 100 % | — |
| Compressive Strength | — | 16,600 psi |
| Compressive Modulus | — | 168,000 psi |
| Flexural Strength | — | 12,325 psi |
| Flexural Modulus | — | 429,000 psi |
| Shrinkage | 0.0024 in. / in. | — |
| Flexural Modulus on 6 ply / 10 oz. Laminate | — | 2,216,000 psi |
| Flexural Strength on 6 ply / 10 oz. Laminate | — | 20,700 psi |
| Heat Deflection With Post Cure | — | 300 °F |
| Tensile Modulus on 6 ply / 10 oz. Laminate | — | 2,150,000 psi |
| Ultimate Tensile on 6 ply / 10 oz. Laminate | — | 32,100 psi |
Product Description
TASK™ 11
TASK™ 11 urethane casting resin is a semi-rigid plastic (has some flexibility) that is strong and very tough. Originally developed for high impact tooling (drop hammer punch), TASK™ 11 also offers good abrasion and chemical resistance and is ideal for a variety of industrial applications.
This product is suitable for some FDA/USDA applications - dry food contact only.
TASK™ 11 applications include making abrasion resistant parts, foundry patterns, encapsulation, roller facings, metal bonding and vibration pads.
› Click here for more TASK™ resin products.
EpoxAmite™ HT
EpoxAmite™ HT High Temperature Laminating Epoxy is a water clear, UV resistant laminating epoxy that resists high temperatures up to 300°F / 149°C when properly cured. Pot life is 1 hour and cure time is 24 hours at 73°F / 23°C (post cure required – see post cure schedule). Ultra-low viscosity ensures uniform wetting out and fast penetration of reinforcement materials during hand lay-up or vacuum infusion processes. Cured resin offers superior physical properties.
EpoxAmite™ HT High Temp Laminating Epoxy can be used with S-Glass, E-Glass, Kevlar and carbon fibers for making composite tooling or parts. Applications include making high temperature pre-preg parts, bonding fixtures, vacuum form molds and prototype injection molds.
Use as a backup laminating resin for EpoxAcoat™ HT high temperature surface coat epoxy.