Key Differences
| Product Type |
|
|
| Mixed Viscosity | 12,000 cps | 350 cps |
| Mix Ratio By Volume | N/A (gram scale required) | 2A:1B |
| Pot Life | 4 hours | 10 minutes |
| Shore D Hardness | 90 | 80 |
| Specific Volume | 16.5 cu. in./lb. | 25.1 cu. in./lb. |
| Color | Grey | Clear (Slightly Yellow In Thick Sections) |
Disclaimer
Although we do our best to ensure accuracy, Smooth-On offers no warranties, promises, and/or representations of any kind, either expressed or implied, as to the accuracy, completeness, or reliability of the information contained on this Compare Tool, nor suitability of the information contained herein to your particular circumstances. Smooth-On assumes no liability for losses or damages of whatever nature (direct, indirect, consequential or other) associated with your use, or inability to use, the Compare Tool, or from your use (or failure to use) the information contained herein. Other useful tools include product technical bulletins and our extensive FAQ section. You can also contact our technical support team.All Technical Data
| EpoxAcast™ 655 + HT Hardener | XTC-3D™ | |
|---|---|---|
| Product Type |
|
|
| Mixed Viscosity | 12,000 cps | 350 cps |
| Mix Ratio By Volume | — | 2A:1B |
| Mix Ratio By Weight | 100A:8B | 100A:42B |
| Pot Life | 4 hours | 10 minutes |
| Thin Film Working Time | — | 20 minutes |
| Thin Film Recoat Time | — | 90 minutes |
| Tack Free Time | — | 2 hours |
| Cure Time | Twenty Four Hours Followed By Post Cures | 3.5 hours |
| Shore D Hardness | 90 | 80 |
| Specific Gravity | 1.64 g/cc | 1.09 g/cc |
| Specific Volume | 16.5 cu. in./lb. | 25.1 cu. in./lb. |
| Color | Grey | Clear (Slightly Yellow In Thick Sections) |
| Tensile Modulus | 7,200,000 psi | — |
| Ultimate Tensile | 6,000 psi | — |
| Tensile Elongation | 0.50 % | — |
| Compressive Strength | 15,700 psi | — |
| Compressive Modulus | 270,000 psi | — |
| Shrinkage | 0.001 in. / in. | — |
| Heat Deflection Temp | 225 °F | — |
| Thermal Conductivity | 0.675 W/M*K | — |
Product Description
EpoxAcast™ 655 + HT Hardener
EpoxAcast™ 655 (formerly Metalset™ A-30) is a versatile aluminum filled castable epoxy resin that is very hard and strong. It is dimensionally stable, even when mass cast up to 512 in³ / 8,390 cm³. Maximum heat resistance is achieved using HT HIGH TEMP hardener (up to 225°F/108°C).
XTC-3D™
XTC-3D™ is a protective coating for smoothing and finishing 3D printed parts. Two liquids are mixed together and brushed onto any 3D print. Coating self-levels and wets out uniformly without leaving brush strokes. Working time is 10 minutes and cure time is about 4 hours (depending on mass and temperature). XTC-3D™ cures to a hard, impact resistant coating that can be sanded, primed and painted. Adding colors and metal effects is easy.