Key Differences
| Product Type |
|
|
| Mixed Viscosity | 10,000 cps | 800 cps |
| Pot Life | 40 minutes | 3 minutes |
| Cure Time | 6 hours | 20 minutes |
| Shore D Hardness | — | 50 |
| Shore A Hardness | 29 | — |
| Color | Yellow | Black |
| Tensile Strength | 417 psi | 1,800 psi |
| Elongation @ Break | 361 % | 125 % |
| Shrinkage | 0.002 in. / in. | 0.005 in. / in. |
Disclaimer
Although we do our best to ensure accuracy, Smooth-On offers no warranties, promises, and/or representations of any kind, either expressed or implied, as to the accuracy, completeness, or reliability of the information contained on this Compare Tool, nor suitability of the information contained herein to your particular circumstances. Smooth-On assumes no liability for losses or damages of whatever nature (direct, indirect, consequential or other) associated with your use, or inability to use, the Compare Tool, or from your use (or failure to use) the information contained herein. Other useful tools include product technical bulletins and our extensive FAQ section. You can also contact our technical support team.All Technical Data
| Mold Max™ 29NV | TASK™ 13 | |
|---|---|---|
| Product Type |
|
|
| Mixed Viscosity | 10,000 cps | 800 cps |
| Mix Ratio By Weight | 100A:10B | 100A:120B |
| Pot Life | 40 minutes | 3 minutes |
| Cure Time | 6 hours | 20 minutes |
| Shore D Hardness | — | 50 |
| Shore A Hardness | 29 | — |
| Specific Gravity | 1.17 g/cc | 1.15 g/cc |
| Specific Volume | 23.7 cu. in./lb. | 24.1 cu. in./lb. |
| Color | Yellow | Black |
| Die B Tear Strength | 96 pli | — |
| Tensile Strength | 417 psi | 1,800 psi |
| Elongation @ Break | 361 % | 125 % |
| 100% Modulus | 54 psi | — |
| Shrinkage | 0.002 in. / in. | 0.005 in. / in. |
| Useful Temperature (min) | -65 °F | — |
| Useful Temperature (max) | 400 °F | — |
| Dielectric Constant, 100Hz | 3.29 | — |
| Dielectric Strength | 330 volts/mil | — |
| Dissipation Factor, 100Hz | 0.005 | — |
| Thermal Conductivity | 0.21 W/M*K | — |
| Volume Resistance | 8.29E+11 ohm | — |
| Volume Resistivity | 5.83E+13 ohm/cm | — |
Product Description
Mold Max™ 29NV
Mold Max™ 29NV is a Shore 29A tin-catalyzed silicone mold rubber that offers low viscosity, fast cure and long library life.
Mold Max™ 29NV does not require vacuum degassing. Mix ratio is 100A:10B by weight. Working time is 45 minutes and cure time is 6 hours at room temperature.
Mold Max™ 29NV will reproduce the finest detail and is suitable for a variety of industrial and art related applications including making molds for reproducing prototypes, furniture, sculpture and architectural elements. Cure time can be reduced with Accel-T™ cure accelerator. Mold Max™ 29NV can be used to cast a variety of materials including wax, gypsum, low melt alloys/metals and urethane, epoxy or polyester resins. Important: Do not cast concrete into rubber molds made with this product. Concrete will not cure properly and inhibition will result.
Important; you must weigh Part A & B components using a gram scale to be successful with Mold Max™ 29NV.
TASK™ 13
TASK™ 13 is a fast setting two-component urethane that cures quickly to black semi-rigid plastic. TASK™ 13 has a pot life of 3 minutes and demold time of 20 minutes.
With a Shore value of 50D, these semi-rigid plastics are used for a variety of industrial applications including fast mold making, fast model duplication, prototyping, durable miniatures, black props and special effects, or making parts that are impact resistant. Fully cured castings are tough, durable and chemical resistant.
For Best Results… Do not cast TASK™ 13 into platinum cure (addition cure) silicone molds.