Product Type |
|
|
Mixed Viscosity | 2,000 cps | 1,000 cps |
Pot Life | 60 minutes | 11 minutes |
Cure Time | 16 hours | 8 hours |
Shore D Hardness | — | 84 |
Shore A Hardness | 50 | — |
Color | Off-White | Clear Yellow |
VytaFlex™ 50 | EpoxAmite™ 101 | |
---|---|---|
Product Type |
|
|
Mixed Viscosity | 2,000 cps | 1,000 cps |
Mix Ratio By Volume | 1A:1B | 4A:1B |
Mix Ratio By Weight | 1A:1B | 100A:24B |
Pot Life | 60 minutes | 11 minutes |
Thin Film Working Time | — | 30 minutes |
Cure Time | 16 hours | 8 hours |
Shore D Hardness | — | 84 |
Shore A Hardness | 50 | — |
Specific Gravity | 1.04 g/cc | 1.13 g/cc |
Specific Volume | 26.7 cu. in./lb. | 24.5 cu. in./lb. |
Color | Off-White | Clear Yellow |
Die C Tear Strength | 102 pli | — |
Tensile Strength | 588 psi | — |
Tensile Modulus | — | 445,000 psi |
Ultimate Tensile | — | 7,930 psi |
Tensile Elongation | — | 2.45 % |
Elongation @ Break | 400 % | — |
100% Modulus | 215 psi | — |
Compressive Strength | — | 11,550 psi |
Compressive Modulus | — | 121,400 psi |
Flexural Strength | — | 13,660 psi |
Flexural Modulus | — | 468,000 psi |
Shrinkage | <.001 in. / in. | — |
Heat Deflection Temp | — | 133 °F |
Flexural Strength on 6 ply / 10 oz. Laminate | — | 30,700 psi |
Ultimate Tensile on 6 ply / 10 oz. Laminate | — | 35,100 psi |
Using Smooth-On’s exclusive “V-Polymer™” technology, VytaFlex™ urethane rubbers offer superior physical and performance properties for casting concrete. VytaFlex™ urethanes are available in 10A, 20A, 30A, 40A, 45A, 50A and 60A Shore hardness’s and feature convenient one-to-one by volume mix ratios.
Vacuum degassing is not necessary and VytaFlex™ rubbers cure with negligible shrinkage to a durable rubber that will last in production.
VytaFlex™ mold rubbers work especially well for casting pigmented / colored concrete. Molds made with VytaFlex™ Series urethanes will render accurate and uniform colored castings.
FOR COMMERCIAL/INDUSTRIAL USE ONLY
EpoxAmite™ 101 is an easy-to-use liquid epoxy system formulated for a wide variety of fabrication applications. EpoxAmite™ 101 includes the EpoxAmite™ 100 Base and the EpoxAmite™ 101 FAST Hardener. EpoxAmite™ 101 is unfilled, low in viscosity, odorless and cures at room temperature. Cured epoxy displays exceptional physical and performance properties. It can be sanded, shaped, machined, drilled, tapped and painted.
EpoxAmite™ 101 can be used with reinforcements such as S-Glass, E-Glass, Kevlar and Carbon fibers for lay-up applications or composite parts. EpoxAmite™ 101 can also be mixed with fillers such as fumed silica for gel coat applications. Urefil™ 3, Urefil™ 7 and other fillers can be added for fairing, filleting or bonding applications.
Applications: Wet Lay-Up Lamination, General Bonding & Repair, Clear Coating - Gel Coating, Barrier Coating, Thin-Section Casting, Water Proofing, Patching & Small Laminates
Also available: EpoxAmite™ 102 MEDIUM SET and EpoxAmite™ 103 SLOW SET