Key Differences
| Product Type |
|
|
| Mixed Viscosity | 2,000 cps | 4,000 cps |
| Cure Time | 48 hours | 16 hours |
| Shore D Hardness | — | 65 |
| Shore A Hardness | 80 | — |
| Color | Light Amber | Clear Amber |
Disclaimer
Although we do our best to ensure accuracy, Smooth-On offers no warranties, promises, and/or representations of any kind, either expressed or implied, as to the accuracy, completeness, or reliability of the information contained on this Compare Tool, nor suitability of the information contained herein to your particular circumstances. Smooth-On assumes no liability for losses or damages of whatever nature (direct, indirect, consequential or other) associated with your use, or inability to use, the Compare Tool, or from your use (or failure to use) the information contained herein. Other useful tools include product technical bulletins and our extensive FAQ section. You can also contact our technical support team.All Technical Data
| PMC™-780 WET | Epsilon™ PRO | |
|---|---|---|
| Product Type |
|
|
| Mixed Viscosity | 2,000 cps | 4,000 cps |
| Mix Ratio By Volume | 2A:1B | 2A:1B |
| Mix Ratio By Weight | 2A:1B | 100A:44B |
| Pot Life | 25 minutes | 22 minutes |
| Thin Film Working Time | — | 35 minutes |
| Thin Film Recoat Time | — | 3 hours |
| Tack Free Time | — | 4 hours |
| Cure Time | 48 hours | 16 hours |
| Shore D Hardness | — | 65 |
| Shore A Hardness | 80 | — |
| Specific Gravity | 1.02 g/cc | 1.11 g/cc |
| Specific Volume | 27.2 cu. in./lb. | 25.0 cu. in./lb. |
| Color | Light Amber | Clear Amber |
| Die C Tear Strength | 200 pli | — |
| Tensile Strength | 900 psi | — |
| Elongation @ Break | 750 % | — |
| 100% Modulus | 400 psi | — |
| Shrinkage | <.001 in. / in. | — |
Product Description
PMC™-780 WET
PMC™-780 is a premium performance urethane rubber that offers exceptional strength, durability and abrasion resistance. PMC™-780 DOES NOT CONTAIN MOCA – a known cancer causing agent and hazard. Mixed two parts A to one part B by weight or volume, PMC™-780 urethane pours easily and cures at room temperature with negligible shrinkage to a solid Shore 80A rubber.
Epsilon™ PRO
Epsilon™ PRO is a thixotropic epoxy coating that self-thickens for brushing onto a variety of surfaces. Compared to original Epsilon™, Epsilon™ PRO offers a longer working time and cured epoxy is semi-rigid, offering better impact resistance. Mix ratio for Epsilon™ PRO is 2A:1B by volume (100A:44B by weight). A gram scale is not needed to use this product.
Applied in thin layers, mixed material holds a vertical surface without sagging or slumping. Material wets out uniformly over different surfaces. Pot life is 22 minutes, with a re-coat time of 3 hours. All layers should be allowed to cure for 16 hours at 73° F / 23° C and can be accelerated with mild heat. Epsilon™ PRO is clear and can be easily colored using Ignite™ or UVO™ colorants. Cured coating has a gloss finish and can be sanded, primed and painted.
Applications: Epsilon™ PRO is suitable for use as a protective, impact resistant coating for EPS or polyurethane foam. It can also be applied to plaster, concrete, wood and fabrics. This product is not sensitive to moisture / humidity and contains no VOC’s.