Key Differences
| Product Type |
|
|
| Mixed Viscosity | 1,200 cps | 350 cps |
| Pot Life | 13 minutes | 10 minutes |
| Cure Time | 24 hours | 3.5 hours |
| Shore D Hardness | — | 80 |
| Shore A Hardness | 80 | — |
| Color | Translucent | Clear (Slightly Yellow In Thick Sections) |
Disclaimer
Although we do our best to ensure accuracy, Smooth-On offers no warranties, promises, and/or representations of any kind, either expressed or implied, as to the accuracy, completeness, or reliability of the information contained on this Compare Tool, nor suitability of the information contained herein to your particular circumstances. Smooth-On assumes no liability for losses or damages of whatever nature (direct, indirect, consequential or other) associated with your use, or inability to use, the Compare Tool, or from your use (or failure to use) the information contained herein. Other useful tools include product technical bulletins and our extensive FAQ section. You can also contact our technical support team.All Technical Data
| Econ™ 80 | XTC-3D™ | |
|---|---|---|
| Product Type |
|
|
| Mixed Viscosity | 1,200 cps | 350 cps |
| Mix Ratio By Volume | 1A:1B | 2A:1B |
| Mix Ratio By Weight | 100A:90B | 100A:42B |
| Pot Life | 13 minutes | 10 minutes |
| Thin Film Working Time | — | 20 minutes |
| Thin Film Recoat Time | — | 90 minutes |
| Tack Free Time | — | 2 hours |
| Handling Time | 6 hours | — |
| Cure Time | 24 hours | 3.5 hours |
| Shore D Hardness | — | 80 |
| Shore A Hardness | 80 | — |
| Specific Gravity | 1.06 g/cc | 1.09 g/cc |
| Specific Volume | 26.16 cu. in./lb. | 25.1 cu. in./lb. |
| Color | Translucent | Clear (Slightly Yellow In Thick Sections) |
| Die C Tear Strength | 77 pli | — |
| Tensile Strength | 955 psi | — |
| Elongation @ Break | 127 % | — |
| 100% Modulus | 670 psi | — |
| Shrinkage | 0.0014 in. / in. | — |
Product Description
Econ™ 80
Econ™ 80 is an economical Shore 80A urethane rubber suitable for a variety of mold making and industrial applications. It is a lower cost, faster cure alternative to our popular PMC™-780. Physical properties are lower vs. PMC™-780. This is a no odor system that features a 1A:1B mix ratio and a low viscosity for easy mixing and pouring. Working time is about 13 minutes at room temperature, handling time is 6 hours and rubber cures overnight. Econ™ 80 is translucent and easily colored with SO-Strong™ or Ignite™ colorants. Econ™ 80 is used to make short run molds for casting concrete and resins, concrete stamping pads, rubber mechanical parts, coating fabrics, pour-in-place gaskets for industrial equipment and burial vaults. Important: To minimize air bubbles in cured rubber, vacuum degassing is recommended.
FOR COMMERCIAL/INDUSTRIAL USE ONLY
XTC-3D™
XTC-3D™ is a protective coating for smoothing and finishing 3D printed parts. Two liquids are mixed together and brushed onto any 3D print. Coating self-levels and wets out uniformly without leaving brush strokes. Working time is 10 minutes and cure time is about 4 hours (depending on mass and temperature). XTC-3D™ cures to a hard, impact resistant coating that can be sanded, primed and painted. Adding colors and metal effects is easy.