Tech Spec Overview Charts
What's the Pot Life? Cure Time? Shore Hardness? Interactive, sortable reference charts let you see 'at a glance' technical data about silicones, urethanes, epoxies and other materials.
Printable versions optimized for 11" x 17" (A3) paper can be displayed in your shop for quick reference.
See Disclaimer
Select a Category Below to View Chart
Silicone Rubber – Tin Cure ›
Product Name |
Mixed Viscosity |
Mix Ratio By Volume |
Mix Ratio By Weight |
Pot Life |
Thin Film Recoat Time |
Cure Time |
Shore A Hardness |
Specific Gravity |
Specific Volume |
Color |
Die B Tear Strength |
Tensile Strength |
Elongation @ Break |
100% Modulus |
Shrinkage |
Useful Temperature (min) |
Useful Temperature (max) |
Volume Resistance |
Volume Resistivity |
Dielectric Constant, 100Hz |
Dielectric Strength |
Dissipation Factor, 100Hz |
Thermal Conductivity |
|
›Mold Max™ 10
|
15,000 cps |
– |
100A:10B |
45 minutes |
– |
24 hours |
10 |
1.15 g/cc |
24.1 cu. in./lb. |
Light Pink |
100 pli |
473 psi |
529 % |
35 psi |
0.001 in. / in. |
-65 °F |
400 °F |
8.29E+11 ohm |
5.83E+13 ohm/cm |
3.29 |
330 volts/mil |
0.005 |
– |
|
›Mold Max™ 10T
|
14,000 cps |
– |
100A:10B |
45 minutes |
– |
24 hours |
10 |
1.09 g/cc |
25.4 cu. in./lb. |
Translucent |
87 pli |
405 psi |
586 % |
29 psi |
0.0025 in. / in. |
-65 °F |
400 °F |
– |
– |
– |
– |
– |
– |
|
›Mold Max™ 14NV
|
7,500 cps |
– |
100A:10B |
40 minutes |
– |
4 hours |
14 |
1.12 g/cc |
24.7 cu. in./lb. |
White |
87 pli |
490 psi |
600 % |
35 psi |
0.002 in. / in. |
-65 °F |
400 °F |
8.29E+11 ohm |
5.83E+13 ohm/cm |
3.29 |
330 volts/mil |
0.005 |
0.21 W/M*K |
|
›Mold Max™ 15T
|
20,000 cps |
– |
100A:10B |
45 minutes |
– |
24 hours |
15 |
1.08 g/cc |
25.6 cu. in./lb. |
Translucent |
94 pli |
490 psi |
600 % |
35 psi |
0.002 in. / in. |
-65 °F |
400 °F |
– |
– |
– |
– |
– |
– |
|
›Mold Max™ 20
|
25,000 cps |
– |
100A:10B |
45 minutes |
– |
24 hours |
20 |
1.18 g/cc |
23.5 cu. in./lb. |
Light Pink |
110 pli |
555 psi |
512 % |
49 psi |
0.001 in. / in. |
-65 °F |
400 °F |
8.29E+11 ohm |
5.83E+13 ohm/cm |
3.29 |
330 volts/mil |
0.005 |
– |
|
›Mold Max™ 25
|
25,000 cps |
– |
100A:5B |
60 minutes |
– |
24 hours |
25 |
1.18 g/cc |
23.5 cu. in./lb. |
Purple |
130 pli |
577 psi |
375 % |
80 psi |
0.001 in. / in. |
-65 °F |
400 °F |
8.29E+11 ohm |
5.83E+13 ohm/cm |
3.29 |
330 volts/mil |
0.005 |
– |
|
›Mold Max™ 27T
|
30,000 cps |
– |
100A:10B |
45 minutes |
– |
24 hours |
27 |
1.11 g/cc |
25.0 cu. in./lb. |
Translucent |
110 pli |
575 psi |
400 % |
65 psi |
0.002 in. / in. |
-65 °F |
400 °F |
– |
– |
– |
– |
– |
– |
|
›Mold Max™ 29NV
|
10,000 cps |
– |
100A:10B |
40 minutes |
– |
6 hours |
29 |
1.17 g/cc |
23.7 cu. in./lb. |
Yellow |
96 pli |
417 psi |
361 % |
54 psi |
0.002 in. / in. |
-65 °F |
400 °F |
8.29E+11 ohm |
5.83E+13 ohm/cm |
3.29 |
330 volts/mil |
0.005 |
0.21 W/M*K |
|
›Mold Max™ 30
|
25,000 cps |
– |
100A:10B |
45 minutes |
– |
24 hours |
30 |
1.18 g/cc |
23.5 cu. in./lb. |
Pink |
125 pli |
577 psi |
300 % |
110 psi |
0.002 in. / in. |
-65 °F |
400 °F |
8.29E+11 ohm |
5.83E+13 ohm/cm |
3.29 |
330 volts/mil |
0.005 |
– |
|
›Mold Max™ 40
|
45,000 cps |
– |
100A:10B |
45 minutes |
– |
24 hours |
40 |
1.14 g/cc |
24.3 cu. in./lb. |
Mint Green |
120 pli |
550 psi |
250 % |
190 psi |
0.004 in. / in. |
-65 °F |
400 °F |
8.29E+11 ohm |
5.83E+13 ohm/cm |
3.29 |
330 volts/mil |
0.005 |
– |
|
›Mold Max™ 60
|
20,000 cps |
– |
100A:3B |
40 minutes |
– |
24 hours |
60 |
1.45 g/cc |
19.1 cu. in./lb. |
Red |
63 pli |
398 psi |
132 % |
331 psi |
0.0015 in. / in. |
-65 °F |
560 °F |
– |
9.000000E+14 ohm/cm |
3.4 |
>500 volts/mil |
0.02 |
0.347 W/M*K |
|
›Mold Max™ STROKE
|
Brushable |
– |
100A:10B |
30 minutes |
60 minutes |
16 hours |
30 |
1.18 g/cc |
23.5 cu. in./lb. |
White |
125 pli |
577 psi |
300 % |
– |
0.002 in. / in. |
-65 °F |
400 °F |
– |
– |
– |
– |
– |
– |
|
›Mold Max™ XLS™ II
|
30,000 cps |
– |
100A:10B |
40 minutes |
– |
24 hours |
30 |
1.22 g/cc |
22.7 cu. in./lb. |
Blue |
110 pli |
550 psi |
375 % |
95 psi |
0.001 in. / in. |
-65 °F |
400 °F |
– |
9.000000E+15 ohm/cm |
3.4 |
>360 volts/mil |
0.002 |
0.24 W/M*K |
|
›OOMOO™ 25
|
4,250 cps |
1A:1B |
100A:130B |
15 minutes |
– |
75 minutes |
25 |
1.34 g/cc |
20.6 cu. in./lb. |
Light Blue |
40 pli |
240 psi |
250 % |
100 psi |
0.0025 in. / in. |
-65 °F |
400 °F |
– |
– |
– |
– |
– |
– |
|
›OOMOO™ 30
|
4,250 cps |
1A:1B |
100A:130B |
30 minutes |
– |
6 hours |
30 |
1.34 g/cc |
20.6 cu. in./lb. |
Lavender |
40 pli |
240 psi |
250 % |
100 psi |
0.0025 in. / in. |
-65 °F |
400 °F |
– |
– |
– |
– |
– |
– |
|
›PoYo™ Putty 40
|
Putty |
20A:1B |
100A:6B |
3 minutes |
– |
30 minutes |
40 |
1.30 g/cc |
21.31 cu. in./lb. |
Light Pink |
85 pli |
450 psi |
250 % |
– |
0.003 in. / in. |
-65 °F |
400 °F |
– |
– |
– |
– |
– |
– |
Silicone Rubber – Platinum Cure ›
Product Name |
Mixed Viscosity |
Mix Ratio By Volume |
Mix Ratio By Weight |
Pot Life |
Cure Time |
Shore A Hardness |
Specific Gravity |
Specific Volume |
Color |
Die B Tear Strength |
Die C Tear Strength |
Tensile Strength |
Elongation @ Break |
100% Modulus |
Shrinkage |
Useful Temperature (min) |
Useful Temperature (max) |
Dielectric Strength |
Refractive Index |
Dielectric Constant, 100Hz |
Thermal Conductivity |
Dissipation Factor, 100Hz |
Volume Resistivity |
|
›Body Double™ Fast Set
|
Brushable |
1A:1B |
1A:1B |
90 seconds |
7 minutes |
25 |
1.17 g/cc |
23.7 cu. in./lb. |
Aqua, Green |
– |
40 pli |
450 psi |
500 % |
– |
<.001 in. / in. |
– |
– |
– |
– |
– |
– |
– |
– |
|
›Body Double™ SILK
|
Brushable |
1A:1B |
1A:1B |
6 minutes |
20 minutes |
25 |
0.91 g/cc |
30.4 cu. in./lb. |
Green |
– |
– |
– |
– |
– |
<.001 in. / in. |
– |
– |
– |
– |
– |
– |
– |
– |
|
›Body Double™ Standard Set
|
Brushable |
1A:1B |
1A:1B |
5 minutes |
20 minutes |
25 |
1.17 g/cc |
23.7 cu. in./lb. |
Purple |
– |
40 pli |
525 psi |
500 % |
– |
<.001 in. / in. |
– |
– |
– |
– |
– |
– |
– |
– |
|
›Dragon Skin™ 10 AF Anti Fungal
|
23,000 cps |
1A:1B |
1A:1B |
20 minutes |
5 hours |
10 |
1.07 g/cc |
25.8 cu. in./lb. |
Translucent |
102 pli |
– |
475 psi |
1,000 % |
22 psi |
<.001 in. / in. |
-65 °F |
450 °F |
>350 volts/mil |
– |
– |
– |
– |
– |
|
›Dragon Skin™ 10 FAST
|
23,000 cps |
1A:1B |
1A:1B |
8 minutes |
75 minutes |
10 |
1.07 g/cc |
25.8 cu. in./lb. |
Translucent |
102 pli |
– |
475 psi |
1,000 % |
22 psi |
<.001 in. / in. |
-65 °F |
450 °F |
>350 volts/mil |
– |
– |
– |
– |
– |
|
›Dragon Skin™ 10 MEDIUM
|
23,000 cps |
1A:1B |
1A:1B |
20 minutes |
5 hours |
10 |
1.07 g/cc |
25.8 cu. in./lb. |
Translucent |
102 pli |
– |
475 psi |
1,000 % |
22 psi |
<.001 in. / in. |
-65 °F |
450 °F |
>350 volts/mil |
– |
– |
– |
– |
– |
|
›Dragon Skin™ 10 NV
|
6,000 cps |
1A:1B |
1A:1B |
15 minutes |
75 minutes |
10 |
1.07 g/cc |
25.8 cu. in./lb. |
Translucent |
90 pli |
– |
400 psi |
663 % |
27 psi |
<.001 in. / in. |
– |
– |
– |
– |
– |
– |
– |
– |
|
›Dragon Skin™ 10 SLOW
|
23,000 cps |
1A:1B |
1A:1B |
45 minutes |
7 hours |
10 |
1.07 g/cc |
25.8 cu. in./lb. |
Translucent |
102 pli |
– |
475 psi |
1,000 % |
22 psi |
<.001 in. / in. |
-65 °F |
450 °F |
>350 volts/mil |
– |
– |
– |
– |
– |
|
›Dragon Skin™ 10 VERY FAST
|
23,000 cps |
1A:1B |
1A:1B |
4 minutes |
30 minutes |
10 |
1.07 g/cc |
25.8 cu. in./lb. |
Translucent |
102 pli |
– |
475 psi |
1,000 % |
22 psi |
<.001 in. / in. |
-65 °F |
450 °F |
>350 volts/mil |
– |
– |
– |
– |
– |
|
›Dragon Skin™ 15
|
21,000 cps |
1A:1B |
1A:1B |
40 minutes |
7 hours |
15 |
1.07 g/cc |
25.8 cu. in./lb. |
Translucent |
112 pli |
– |
537 psi |
771 % |
40 psi |
<.001 in. / in. |
-65 °F |
450 °F |
>350 volts/mil |
– |
– |
– |
– |
– |
|
›Dragon Skin™ 20
|
20,000 cps |
1A:1B |
1A:1B |
25 minutes |
4 hours |
20 |
1.08 g/cc |
25.6 cu. in./lb. |
Translucent |
120 pli |
– |
550 psi |
620 % |
49 psi |
<.001 in. / in. |
-65 °F |
450 °F |
>350 volts/mil |
– |
– |
– |
– |
– |
|
›Dragon Skin™ 20 NV
|
4,000 cps |
1A:1B |
1A:1B |
6 minutes |
30 minutes |
20 |
1.09 g/cc |
25.4 cu. in./lb. |
Translucent |
138 pli |
– |
440 psi |
672 % |
41 psi |
<.001 in. / in. |
-65 °F |
450 °F |
– |
– |
– |
– |
– |
– |
|
›Dragon Skin™ 30
|
20,000 cps |
1A:1B |
1A:1B |
45 minutes |
16 hours |
30 |
1.08 g/cc |
25.7 cu. in./lb. |
Translucent |
108 pli |
– |
500 psi |
364 % |
86 psi |
<.001 in. / in. |
– |
– |
>350 volts/mil |
– |
– |
– |
– |
– |
|
›Dragon Skin™ FX‑ Pro™
|
18,000 cps |
1A:1B |
1A:1B |
12 minutes |
40 minutes |
2 |
1.062 g/cc |
25.0 cu. in./lb. |
Translucent |
61 pli |
– |
288 psi |
763 % |
37.8 psi |
<.001 in. / in. |
– |
– |
– |
– |
– |
– |
– |
– |
|
›Ecoflex™ 00-20
|
3,000 cps |
1A:1B |
1A:1B |
30 minutes |
4 hours |
00-20 |
1.07 g/cc |
26.0 cu. in./lb. |
Translucent |
30 pli |
– |
160 psi |
845 % |
8 psi |
<.001 in. / in. |
-65 °F |
450 °F |
– |
– |
– |
– |
– |
– |
|
›Ecoflex™ 00-20 FAST
|
3,000 cps |
1A:1B |
1A:1B |
20 minutes |
1 hour |
00-20 |
1.07 g/cc |
26 cu. in./lb. |
Translucent |
30 pli |
– |
160 psi |
845 % |
8 psi |
<.001 in. / in. |
-65 °F |
450 °F |
350 volts/mil |
– |
– |
– |
– |
– |
|
›Ecoflex™ 00-35 FAST
|
3,500 cps |
1A:1B |
– |
2.5 minutes |
5 minutes |
00-35 |
1.07 g/cc |
26.0 cu. in./lb. |
Off-White Translucent |
38 pli |
– |
200 psi |
900 % |
10 psi |
<0.001 in. / in. |
-65 °F |
450 °F |
– |
– |
– |
– |
– |
– |
|
›Ecoflex™ 00-10
|
14,000 cps |
1A:1B |
1A:1B |
30 minutes |
4 hours |
00-10 |
1.04 g/cc |
26.6 cu. in./lb. |
Translucent |
22 pli |
– |
120 psi |
800 % |
8 psi |
<.001 in. / in. |
-65 °F |
450 °F |
– |
– |
– |
– |
– |
– |
|
›Ecoflex™ 00-30
|
3,000 cps |
1A:1B |
1A:1B |
45 minutes |
4 hours |
00-30 |
1.07 g/cc |
26.0 cu. in./lb. |
Translucent |
38 pli |
– |
200 psi |
900 % |
10 psi |
<.001 in. / in. |
-65 °F |
450 °F |
– |
– |
– |
– |
– |
– |
|
›Ecoflex™ 00-31 Near Clear™
|
3,000 cps |
1A:1B |
– |
40 minutes |
4 hours |
00-31 |
1.07 g/cc |
26 cu. in./lb. |
Water Clear Translucent |
38 pli |
– |
200 psi |
900 % |
10 psi |
<.001 in. / in. |
-65 °F |
450 °F |
– |
– |
– |
– |
– |
– |
|
›Ecoflex™ 00-33AF Anti Fungal
|
3,000 cps |
1A:1B |
1A:1B |
45 minutes |
4 hours |
00-33 |
1.07 g/cc |
26.0 cu. in./lb. |
Off-White Translucent |
38 pli |
– |
200 psi |
900 % |
10 psi |
<.001 in. / in. |
-65 °F |
450 °F |
– |
– |
– |
– |
– |
– |
|
›Ecoflex™ 00-45 Near Clear™
|
2,000 cps |
1A:1B |
– |
45 minutes |
4 hours |
00-45 |
1.06 g/cc |
26.2 cu. in./lb. |
Water Clear Translucent |
50 pli |
– |
315 psi |
980 % |
12 psi |
<.001 in. / in. |
-65 °F |
450 °F |
– |
– |
– |
– |
– |
– |
|
›Ecoflex™ 00-50
|
8,000 cps |
1A:1B |
1A:1B |
18 minutes |
3 hours |
00-50 |
1.07 g/cc |
25.9 cu. in./lb. |
Translucent |
50 pli |
– |
315 psi |
980 % |
12 psi |
<.001 in. / in. |
-65 °F |
450 °F |
– |
– |
– |
– |
– |
– |
|
›Ecoflex™ 5
|
13,000 cps |
1A:1B |
1A:1B |
1 minute |
5 minutes |
5 |
1.07 g/cc |
25.8 cu. in./lb. |
Translucent |
75 pli |
– |
350 psi |
1,000 % |
15 psi |
<.001 in. / in. |
-65 °F |
450 °F |
– |
– |
– |
– |
– |
– |
|
›Ecoflex™ GEL
|
9,300 cps |
1A:1B |
1A:1B |
15 minutes |
2 hours |
000-35 |
0.98 g/cc |
28 cu. in./lb. |
Translucent |
– |
– |
– |
>1000 % |
– |
<.001 in. / in. |
– |
– |
– |
1.40451 nm |
– |
– |
– |
– |
|
›Ecoflex™ GEL 2
|
5,000 cps |
1A:1B |
1A:1B |
20 minutes |
50 minutes |
000-34 |
0.98 g/cc |
26.4 cu. in./lb. |
Translucent |
– |
– |
– |
>1000 % |
– |
<.001 in. / in. |
– |
– |
– |
– |
– |
– |
– |
– |
|
›Encapso™ K
|
150 cps |
1A:1B |
1A:1B |
120 minutes |
16 hours |
33 |
0.97 g/cc |
28.6 cu. in./lb. |
Clear |
– |
– |
– |
– |
– |
0.001 in. / in. |
– |
– |
319 volts/mil |
– |
3.17 |
– |
– |
– |
|
›Equinox™ 35 FAST
|
Putty |
1A:1B |
1A:1B |
1 minute |
7 minutes |
35 |
1.25 g/cc |
22.2 cu. in./lb. |
Light Purple |
140 pli |
– |
520 psi |
430 % |
119 psi |
0.001 in. / in. |
– |
– |
– |
– |
– |
– |
– |
– |
|
›Equinox™ 38 MEDIUM
|
Putty |
1A:1B |
1A:1B |
4 minutes |
30 minutes |
38 |
1.25 g/cc |
22.2 cu. in./lb. |
Light Purple |
140 pli |
– |
520 psi |
430 % |
119 psi |
0.001 in. / in. |
– |
– |
– |
– |
– |
– |
– |
– |
|
›Equinox™ 40 SLOW
|
Putty |
1A:1B |
1A:1B |
30 minutes |
5 hours |
40 |
1.25 g/cc |
22.2 cu. in./lb. |
Light Purple |
140 pli |
– |
520 psi |
430 % |
119 psi |
0.001 in. / in. |
– |
– |
– |
– |
– |
– |
– |
– |
|
›EZ-Brush™ Vac Bag Silicone
|
20,000 cps |
1A:1B |
1A:1B |
30 minutes |
3.5 hours |
20 |
1.08 g/cc |
25.7 cu. in./lb. |
Translucent Green |
120 pli |
– |
550 psi |
364 % |
46 psi |
<.001 in. / in. |
– |
– |
– |
– |
– |
– |
– |
– |
|
›EZ-Spray™ 35
|
Sprayable |
1A:1B |
– |
1.5 minutes |
1 hour |
35 |
1.15 g/cc |
24.1 cu. in./lb. |
Purple |
92 pli |
– |
490 psi |
415 % |
– |
<.001 in. / in. |
– |
– |
– |
– |
– |
– |
– |
– |
|
›EZ-Spray™ Silicone 20
|
11,000 cps |
1A:1B |
– |
3 minutes |
20 minutes |
20 |
1.08 g/cc |
25.6 cu. in./lb. |
Translucent Green |
100 pli |
– |
495 psi |
470 % |
47 psi |
<.001 in. / in. |
-65 °F |
500 °F |
– |
– |
– |
– |
– |
– |
|
›EZ-Spray™ Silicone 22
|
11,000 cps |
1A:1B |
– |
5 minutes |
45 minutes |
22 |
1.08 g/cc |
25.6 cu. in./lb. |
Translucent Green |
102 pli |
– |
490 psi |
450 % |
49 psi |
<.001 in. / in. |
-65 °F |
500 °F |
– |
– |
– |
– |
– |
– |
|
›Mold Star™ 15 SLOW
|
12,500 cps |
1A:1B |
1A:1B |
50 minutes |
4 hours |
15 |
1.18 g/cc |
23.5 cu. in./lb. |
Green |
88 pli |
– |
400 psi |
440 % |
55 psi |
<.001 in. / in. |
-65 °F |
450 °F |
– |
– |
– |
– |
– |
– |
|
›Mold Star™ 16 FAST
|
12,500 cps |
1A:1B |
1A:1B |
6 minutes |
30 minutes |
16 |
1.18 g/cc |
23.5 cu. in./lb. |
Blue-Green |
88 pli |
– |
400 psi |
440 % |
55 psi |
<.001 in. / in. |
-65 °F |
450 °F |
– |
– |
– |
– |
– |
– |
|
›Mold Star™ 20T
|
11,000 cps |
1A:1B |
1A:1B |
6 minutes |
30 minutes |
20 |
1.08 g/cc |
25.6 cu. in./lb. |
Translucent |
90 pli |
– |
420 psi |
470 % |
47 psi |
<.001 in. / in. |
-65 °F |
450 °F |
– |
– |
– |
– |
– |
– |
|
›Mold Star™ 30
|
12,500 cps |
1A:1B |
100A:96B |
45 minutes |
6 hours |
30 |
1.12 g/cc |
24.7 cu. in./lb. |
Blue |
88 pli |
– |
420 psi |
339 % |
96 psi |
<.001 in. / in. |
-65 °F |
450 °F |
– |
– |
– |
– |
– |
– |
|
›Mold Star™ 31T
|
11,000 cps |
1A:1B |
1A:1B |
5 minutes |
23 minutes |
30 |
1.08 g/cc |
25.6 cu. in./lb. |
Translucent |
90 pli |
– |
423 psi |
400 % |
47 psi |
< .001 in. / in. |
-65 °F |
450 °F |
– |
– |
– |
– |
– |
– |
|
›Mold Star™ 14T
|
11,000 cps |
1A:1B |
1A:1B |
3 minutes |
9 minutes |
14 |
1.08 g/cc |
25.6 cu. in./lb. |
Translucent |
90 pli |
– |
420 psi |
490 % |
47 psi |
<.001 in. / in. |
-65 °F |
450 °F |
– |
– |
– |
– |
– |
– |
|
›Mold Star™ 19T
|
11,000 cps |
1A:1B |
1A:1B |
3 minutes |
12 minutes |
19 |
1.08 g/cc |
25.6 cu. in./lb. |
Translucent |
90 pli |
– |
420 psi |
470 % |
– |
0.001 in. / in. |
-65 °F |
450 °F |
– |
– |
– |
– |
– |
– |
|
›Rebound™ 25
|
Brushable |
1A:1B |
1A:1B |
20 minutes |
6 hours |
25 |
1.14 g/cc |
23.5 cu. in./lb. |
Orange |
102 pli |
– |
515 psi |
690 % |
– |
<.001 in. / in. |
– |
– |
– |
– |
– |
– |
– |
– |
|
›Rebound™ 40
|
Brushable |
1A:1B |
1A:1B |
20 minutes |
6 hours |
40 |
1.14 g/cc |
23.5 cu. in./lb. |
Green |
106 pli |
– |
486 psi |
324 % |
– |
<.001 in. / in. |
– |
– |
– |
– |
– |
– |
– |
– |
|
›Rubber Glass™
|
150 cps |
1A:1B |
1A:1B |
120 minutes |
16 hours |
33 |
0.97 g/cc |
28.6 cu. in./lb. |
Clear |
– |
– |
– |
– |
– |
<.001 in. / in. |
– |
– |
319 volts/mil |
– |
3.17 |
– |
– |
– |
|
›Smooth‑Sil™ 933 Flame Out
|
40,000 cps |
1A:1B |
1A:1B |
45 minutes |
6 hours |
33 |
1.42 g/cc |
19.5 cu. in./lb. |
White |
50 pli |
– |
222 psi |
433 % |
71 psi |
<0.001 in. / in. |
-65 °F |
450 °F |
– |
– |
– |
– |
– |
– |
|
›Smooth‑Sil™ 936
|
21,000 cps |
– |
100A:10B |
60 minutes |
24 hours |
36 |
1.21 g/cc |
22.9 cu. in./lb. |
Blue |
110 pli |
– |
550 psi |
500 % |
180 psi |
<0.001 in. / in. |
-65 °F |
450 °F |
– |
– |
– |
– |
– |
– |
|
›Smooth‑Sil™ 940
|
35,000 cps |
– |
100A:10B |
30 minutes |
24 hours |
40 |
1.18 g/cc |
23.4 cu. in./lb. |
Pink |
100 pli |
– |
600 psi |
300 % |
200 psi |
<.001 in. / in. |
-65 °F |
450 °F |
– |
– |
– |
– |
– |
– |
|
›Smooth‑Sil™ 945
|
30,000 cps |
1A:1B |
1A:1B |
25 minutes |
6 hours |
45 |
1.24 g/cc |
22.3 cu. in./lb. |
Purple |
120 pli |
– |
700 psi |
320 % |
260 psi |
<.001 in. / in. |
-65 °F |
450 °F |
– |
– |
– |
– |
– |
– |
|
›Smooth‑Sil™ 950
|
35,000 cps |
– |
100A:10B |
45 minutes |
18 hours |
50 |
1.24 g/cc |
22.3 cu. in./lb. |
Blue |
155 pli |
– |
725 psi |
320 % |
272 psi |
<.001 in. / in. |
-65 °F |
450 °F |
– |
– |
– |
0.261 W/M*K |
– |
– |
|
›Smooth‑Sil™ 960
|
30,000 cps |
– |
100A:10B |
45 minutes |
16 hours |
60 |
1.25 g/cc |
22.2 cu. in./lb. |
Green |
110 pli |
– |
650 psi |
270 % |
280 psi |
<.001 in. / in. |
-65 °F |
450 °F |
– |
– |
– |
– |
– |
– |
|
›Solaris™
|
1,200 cps |
1A:1B |
1A:1B |
240 minutes |
24 hours |
15 |
0.99 g/cc |
28.1 cu. in./lb. |
Clear |
– |
– |
180 psi |
290 % |
25 psi |
<.001 in. / in. |
-149 °F |
400 °F |
366 volts/mil |
1.41 nm |
2.78 |
0.18 W/M*K |
0.00 |
3.16E+15 ohm/cm |
|
›SORTA-Clear™ 12
|
6,000 cps |
1A:1B |
1A:1B |
40 minutes |
12 hours |
12 |
1.07 g/cc |
25.9 cu. in./lb. |
Water Clear Translucent |
80 pli |
– |
320 psi |
590 % |
23 psi |
<.001 in. / in. |
– |
– |
– |
– |
– |
– |
– |
– |
|
›SORTA-Clear™ 18
|
21,000 cps |
– |
100A:10B |
60 minutes |
24 hours |
18 |
1.08 g/cc |
25.6 cu. in./lb. |
Water Clear Translucent |
80 pli |
– |
425 psi |
545 % |
35 psi |
<.001 in. / in. |
-65 °F |
450 °F |
– |
– |
– |
– |
– |
– |
|
›SORTA-Clear™ 37
|
35,000 cps |
1A:1B |
1A:1B |
25 minutes |
4 hours |
37 |
1.08 g/cc |
25.6 cu. in./lb. |
Water Clear Translucent |
105 pli |
– |
600 psi |
400 % |
90 psi |
<.001 in. / in. |
– |
– |
– |
– |
– |
– |
– |
– |
|
›SORTA-Clear™ 40
|
35,000 cps |
– |
100A:10B |
60 minutes |
16 hours |
40 |
1.08 g/cc |
25.6 cu. in./lb. |
Water Clear Translucent |
120 pli |
– |
800 psi |
400 % |
90 psi |
<.001 in. / in. |
-65 °F |
450 °F |
– |
– |
– |
– |
– |
– |
Urethane Rubber ›
Product Name |
Mixed Viscosity |
Mix Ratio By Volume |
Mix Ratio By Weight |
Pot Life |
Thin Film Recoat Time |
Tack Free Time |
Handling Time |
Cure Time |
Shore A Hardness |
Specific Gravity |
Specific Volume |
Color |
Die C Tear Strength |
Tensile Strength |
Elongation @ Break |
100% Modulus |
Shrinkage |
Volume Resistance |
Volume Resistivity |
Dielectric Constant, 100Hz |
Dissipation Factor, 100Hz |
Dielectric Strength |
|
›Brush-On™ 35
|
Brushable |
1A:1B |
100A:67B |
20 minutes |
– |
– |
– |
16 hours |
35 |
1.29 g/cc |
21.5 cu. in./lb. |
Grey-Green |
57 pli |
335 psi |
1,000 % |
– |
<.001 in. / in. |
– |
– |
– |
– |
– |
|
›Brush-On™ 40
|
Brushable |
1A:1B |
100A:125B |
20 minutes |
– |
– |
– |
16 hours |
40 |
1.17 g/cc |
23.7 cu. in./lb. |
Off White |
60 pli |
300 psi |
1,000 % |
– |
<.001 in. / in. |
– |
– |
– |
– |
– |
|
›Brush-On™ 50
|
Brushable |
1A:1B |
100A:125B |
20 minutes |
– |
– |
– |
16 hours |
50 |
1.17 g/cc |
23.7 cu. in./lb. |
Off White |
80 pli |
500 psi |
400 % |
– |
<.001 in. / in. |
– |
– |
– |
– |
– |
|
›Brush-On™ 60
|
Brushable |
1A:1B |
100A:125B |
20 minutes |
– |
– |
– |
16 hours |
60 |
1.18 g/cc |
23.5 cu. in./lb. |
Off White |
80 pli |
630 psi |
400 % |
– |
<.001 in. / in. |
– |
– |
– |
– |
– |
|
›Clear Flex™ 30
|
750 cps |
1A:1B |
100A:94B |
15 minutes |
– |
– |
– |
16 hours |
30 |
1.03 g/cc |
26.9 cu. in./lb. |
Clear |
54 pli |
725 psi |
675 % |
– |
0.002 in. / in. |
– |
– |
– |
– |
– |
|
›Clear Flex™ 50
|
250 cps |
– |
1A:2B |
25 minutes |
– |
– |
– |
16 hours |
50 |
1.04 g/cc |
26.8 cu. in./lb. |
Clear |
25 pli |
250 psi |
500 % |
– |
0.0015 in. / in. |
– |
– |
– |
– |
– |
|
›Clear Flex™ 95
|
250 cps |
– |
1A:1.5B |
25 minutes |
– |
– |
– |
16 hours |
95 |
1.04 g/cc |
26.8 cu. in./lb. |
Clear |
200 pli |
2,500 psi |
175 % |
– |
0.0028 in. / in. |
>7.646E+13 ohm |
>6.014E+15 ohm/cm |
6.62 |
0.103 |
474 volts/mil |
|
›Compat™ 45
|
2,600 cps |
1A:1B |
85A:100B |
25 minutes |
– |
– |
– |
16 hours |
45 |
1.12 g/cc |
24.7 cu. in./lb. |
Brown |
101 pli |
629 psi |
772 % |
137 psi |
<0.001 in. / in. |
– |
– |
– |
– |
– |
|
›Econ™ 60
|
1,400 cps |
1A:1B |
1A:1B |
6 minutes |
– |
– |
4 hours |
16 hours |
60 |
1.04 g/cc |
26.7 cu. in./lb. |
Translucent Amber |
85 pli |
350 psi |
500 % |
82 psi |
<0.001 in. / in. |
– |
– |
– |
– |
– |
|
›Econ™ 80
|
1,200 cps |
1A:1B |
100A:90B |
13 minutes |
– |
– |
6 hours |
24 hours |
80 |
1.06 g/cc |
26.16 cu. in./lb. |
Translucent |
77 pli |
955 psi |
127 % |
670 psi |
0.0014 in. / in. |
– |
– |
– |
– |
– |
|
›EZ-Mix™ 40
|
Brushable |
1A:1B |
100A:95B |
18 minutes |
60 minutes |
– |
– |
16 hours |
40 |
1.025 g/cc |
27 cu. in./lb. |
Grey |
67 pli |
420 psi |
577 % |
– |
<.001 in. / in. |
– |
– |
– |
– |
– |
|
›EZ-Spray™ 45
|
Sprayable |
1A:1B |
– |
20 minutes |
10 minutes |
– |
– |
16 hours |
45 |
1.025 g/cc |
27 cu. in./lb. |
Light Blue |
100 pli |
510 psi |
375 % |
– |
<.001 in. / in. |
– |
– |
– |
– |
– |
|
›Formlastic™ 48
|
3,000 cps |
1A:1B |
100A:118B |
25 minutes |
– |
– |
– |
24 hours |
48 |
1.14 g/cc |
24.3 cu. in./lb. |
Off White |
98 pli |
700 psi |
1,250 % |
111 psi |
<0.001 in. / in. |
– |
– |
– |
– |
– |
|
›Formlastic™ 60
|
3,000 cps |
1A:1B |
100A:118B |
40 minutes |
– |
– |
– |
24 hours |
60 |
1.14 g/cc |
24.3 cu. in./lb. |
Off White |
146 pli |
1,025 psi |
1,000 % |
230 psi |
<0.001 in. / in. |
– |
– |
– |
– |
– |
|
›KX Flex™ 40
|
800 cps |
1A:1B |
1A:1B |
2.5 minutes |
– |
– |
30 minutes |
24 hours |
40 |
1.07 g/cc |
25.9 cu. in./lb. |
Translucent White |
– |
457 psi |
400 % |
– |
0.002 in. / in. |
– |
– |
– |
– |
– |
|
›KX Flex™ 60
|
800 cps |
1A:1B |
1A:1B |
2.5 minutes |
– |
– |
30 minutes |
24 hours |
60 |
1.15 g/cc |
24.1 cu. in./lb. |
Off-White |
– |
1,800 psi |
125 % |
– |
0.005 in. / in. |
– |
– |
– |
– |
– |
|
›KX Flex™ 90
|
800 cps |
– |
100A:120B |
2.5 minutes |
– |
– |
30 minutes |
24 hours |
90 |
1.15 g/cc |
24.1 cu. in./lb. |
Off-White |
– |
1,800 psi |
125 % |
– |
0.005 in. / in. |
– |
– |
– |
– |
– |
|
›PMC™-121 30/DRY
|
1,800 cps |
1A:1B |
1A:1B |
30 minutes |
– |
– |
– |
16 hours |
30 |
1.04 g/cc |
26.7 cu. in./lb. |
Clear Amber |
75 pli |
400 psi |
1,000 % |
82 psi |
< .001 in. / in. |
– |
– |
– |
– |
– |
|
›PMC™-121 30/WET
|
1,800 cps |
1A:1B |
1A:1B |
30 minutes |
– |
– |
– |
16 hours |
30 |
1.04 g/cc |
26.7 cu. in./lb. |
Clear Amber |
75 pli |
400 psi |
1,000 % |
82 psi |
< .001 in. / in. |
– |
– |
– |
– |
– |
|
›PMC™-121 50/WET
|
1,400 cps |
1A:1B |
1A:1B |
30 minutes |
– |
– |
– |
16 hours |
50 |
1.04 g/cc |
26.7 cu. in./lb. |
Clear Amber |
85 pli |
350 psi |
500 % |
82 psi |
< .001 in. / in. |
– |
– |
– |
– |
– |
|
›PMC™-724
|
4,000 cps |
– |
10A:100B |
20 minutes |
– |
– |
– |
16 hours |
40 |
1.38 g/cc |
20.1 cu. in./lb. |
Off-White |
90 pli |
600 psi |
>700 % |
80 psi |
<.001 in. / in. |
– |
– |
– |
– |
– |
|
›PMC™-744
|
3,400 cps |
2A:1B |
2A:1B |
15 minutes |
– |
– |
– |
16 hours |
44 |
1.01 g/cc |
27.5 cu. in./lb. |
Beige |
90 pli |
300 psi |
400 % |
90 psi |
< .001 in. / in. |
– |
– |
– |
– |
– |
|
›PMC™-746
|
1,200 cps |
2A:1B |
2A:1B |
15 minutes |
– |
– |
– |
16 hours |
60 |
1.03 g/cc |
26.9 cu. in./lb. |
Ranges From Amber To Blue |
100 pli |
700 psi |
650 % |
220 psi |
< .001 in. / in. |
– |
– |
– |
– |
– |
|
›PMC™-746 Clear Amber
|
1,200 cps |
2A:1B |
2A:1B |
15 minutes |
– |
– |
– |
16 hours |
60 |
1.03 g/cc |
26.9 cu. in./lb. |
Clear Amber |
100 pli |
700 psi |
650 % |
220 psi |
< .001 in. / in. |
– |
– |
– |
– |
– |
|
›PMC™-770
|
3,000 cps |
– |
2A:1B |
30 minutes |
– |
– |
– |
16 hours |
70 |
1.04 g/cc |
26.5 cu. in./lb. |
Light Amber |
200 pli |
750 psi |
750 % |
250 psi |
<.001 in. / in. |
– |
– |
– |
– |
– |
|
›PMC™-780 DRY
|
2,000 cps |
2A:1B |
2A:1B |
25 minutes |
– |
– |
– |
48 hours |
80 |
1.02 g/cc |
27.2 cu. in./lb. |
Light Amber |
200 pli |
900 psi |
750 % |
400 psi |
<.001 in. / in. |
– |
– |
– |
– |
– |
|
›PMC™-780 WET
|
2,000 cps |
2A:1B |
2A:1B |
25 minutes |
– |
– |
– |
48 hours |
80 |
1.02 g/cc |
27.2 cu. in./lb. |
Light Amber |
200 pli |
900 psi |
750 % |
400 psi |
<.001 in. / in. |
– |
– |
– |
– |
– |
|
›PMC™-790
|
3,000 cps |
2A:1B |
2A:1B |
20 minutes |
– |
– |
– |
48 hours |
90 |
1.07 g/cc |
25.9 cu. in./lb. |
Clear Amber |
300 pli |
2,000 psi |
550 % |
640 psi |
<.001 in. / in. |
– |
– |
– |
– |
– |
|
›ReoFlex™ 20
|
1,800 cps |
1A:1B |
1A:1B |
30 minutes |
– |
– |
– |
16 hours |
20 |
1.01 g/cc |
27.3 cu. in./lb. |
Off White |
60 pli |
200 psi |
1,000 % |
27 psi |
<.001 in. / in. |
– |
– |
– |
– |
– |
|
›ReoFlex™ 30
|
1,500 cps |
1A:1B |
1A:1B |
30 minutes |
– |
– |
– |
16 hours |
30 |
1.01 g/cc |
27.5 cu. in./lb. |
Off White |
82 pli |
450 psi |
1,000 % |
67 psi |
<.001 in. / in. |
– |
– |
– |
– |
– |
|
›ReoFlex™ 40
|
1,500 cps |
1A:1B |
1A:1B |
30 minutes |
– |
– |
– |
16 hours |
40 |
1.02 g/cc |
27.2 cu. in./lb. |
Off White |
85 pli |
490 psi |
1,000 % |
73 psi |
<.001 in. / in. |
– |
– |
– |
– |
– |
|
›ReoFlex™ 50
|
2,000 cps |
1A:1B |
1A:1B |
50 minutes |
– |
– |
– |
16 hours |
50 |
1.01 g/cc |
27.4 cu. in./lb. |
Off White |
120 pli |
580 psi |
435 % |
152 psi |
<.001 in. / in. |
– |
– |
– |
– |
– |
|
›ReoFlex™ 60
|
1,800 cps |
1A:1B |
1A:1B |
50 minutes |
– |
– |
– |
16 hours |
60 |
1.04 g/cc |
26.7 cu. in./lb. |
Off White |
132 pli |
782 psi |
581 % |
256 psi |
<.001 in. / in. |
– |
– |
– |
– |
– |
|
›Simpact™ 60A
|
1,100 cps |
1A:1B |
100A:94B |
4 minutes |
– |
– |
2 hours |
48 hours |
60 |
1.08 g/cc |
25.7 cu. in./lb. |
White |
142 pli |
990 psi |
400 % |
312 psi |
<.007 in. / in. |
– |
– |
– |
– |
– |
|
›Simpact™ 80A
|
2,000 cps |
– |
100A:60B |
15 minutes |
– |
– |
4 hours |
48 hours |
80 |
1.09 g/cc |
25.4 cu. in./lb. |
Amber |
182 pli |
2,295 psi |
164 % |
1,213 psi |
<.007 in. / in. |
– |
– |
– |
– |
– |
|
›Simpact™ 85A
|
1,100 cps |
– |
85A:100B |
4 minutes |
– |
– |
2 hours |
48 hours |
85 |
1.09 g/cc |
25.4 cu. in./lb. |
Off White |
182 pli |
1,573 psi |
164 % |
1,213 psi |
<.007 in. / in. |
– |
– |
– |
– |
– |
|
›UreCoat™
|
3,800 cps |
– |
100A:10B |
8 minutes |
30 minutes |
2 hours |
– |
16 hours |
70 |
1.05 g/cc |
26.4 cu. in./lb. |
Translucent Amber |
256 pli |
1,360 psi |
876 % |
503 psi |
– |
– |
– |
– |
– |
– |
|
›VytaFlex™ 10
|
3,100 cps |
1A:1B |
1A:1B |
30 minutes |
– |
– |
– |
24 hours |
10 |
1.00 g/cc |
27.9 cu. in./lb. |
Off-White |
38 pli |
200 psi |
1,000 % |
25 psi |
<.001 in. / in. |
– |
– |
– |
– |
– |
|
›VytaFlex™ 20
|
1,000 cps |
1A:1B |
1A:1B |
30 minutes |
– |
– |
– |
16 hours |
20 |
1.00 g/cc |
27.7 cu. in./lb. |
Clear Amber |
60 pli |
200 psi |
1,000 % |
50 psi |
<.001 in. / in. |
– |
– |
– |
– |
– |
|
›VytaFlex™ 30
|
1,800 cps |
1A:1B |
1A:1B |
30 minutes |
– |
– |
– |
16 hours |
30 |
1.02 g/cc |
27.3 cu. in./lb. |
Off-White |
78 pli |
500 psi |
1,000 % |
65 psi |
<.001 in. / in. |
– |
– |
– |
– |
– |
|
›VytaFlex™ 40
|
2,000 cps |
1A:1B |
1A:1B |
30 minutes |
– |
– |
– |
16 hours |
40 |
1.03 g/cc |
26.9 cu. in./lb. |
Off-White |
82 pli |
522 psi |
660 % |
100 psi |
<.001 in. / in. |
– |
– |
– |
– |
– |
|
›VytaFlex™ 45
|
2,000 cps |
1A:1B |
1A:1B |
30 minutes |
– |
– |
– |
16 hours |
45 |
1.04 g/cc |
26.4 cu. in./lb. |
Off White |
100 pli |
886 psi |
900 % |
116 psi |
<.001 in. / in. |
– |
– |
– |
– |
– |
|
›VytaFlex™ 50
|
2,000 cps |
1A:1B |
1A:1B |
60 minutes |
– |
– |
– |
16 hours |
50 |
1.04 g/cc |
26.7 cu. in./lb. |
Off-White |
102 pli |
588 psi |
400 % |
215 psi |
<.001 in. / in. |
– |
– |
– |
– |
– |
|
›VytaFlex™ 60
|
2,000 cps |
1A:1B |
1A:1B |
60 minutes |
– |
– |
– |
16 hours |
60 |
1.04 g/cc |
26.6 cu. in./lb. |
Off-White |
136 pli |
880 psi |
480 % |
300 psi |
<0.001 in. / in. |
– |
– |
– |
– |
– |
Urethane Resins and Coatings ›
Product Name |
Mixed Viscosity |
Mix Ratio By Volume |
Mix Ratio By Weight |
Pot Life |
Handling Time |
Cure Time |
Shore D Hardness |
Shore A Hardness |
Specific Gravity |
Specific Volume |
Color |
Die C Tear Strength |
Tensile Strength |
Tensile Modulus |
Ultimate Tensile |
Elongation @ Break |
100% Modulus |
Compressive Strength |
Compressive Modulus |
Flexural Strength |
Flexural Modulus |
Shrinkage |
Heat Deflection Temp |
Heat Deflection With Post Cure |
|
›Crystal Clear™ 200
|
600 cps |
– |
100A:90B |
20 minutes |
– |
16 hours |
80 |
– |
1.036 g/cc |
26.7 cu. in./lb. |
Clear |
– |
2,500 psi |
73,200 psi |
– |
10 % |
– |
6,385 psi |
40,000 psi |
10,650 psi |
200,000 psi |
0.001 in. / in. |
120 °F |
– |
|
›Crystal Clear™ 202
|
600 cps |
– |
100A:90B |
9 minutes |
– |
90 minutes |
80 |
– |
1.036 g/cc |
26.7 cu. in./lb. |
Clear |
– |
3,500 psi |
86,240 psi |
– |
10 % |
– |
4,200 psi |
44,000 psi |
5,390 psi |
183,200 psi |
0.0125 in. / in. |
120 °F |
– |
|
›Crystal Clear™ 204
|
600 cps |
– |
100A:90B |
2 hours |
– |
48 hours |
80 |
– |
1.036 g/cc |
26.7 cu. in./lb. |
Clear |
– |
3,500 psi |
86,240 psi |
– |
10 % |
– |
4,200 psi |
44,000 psi |
5,390 psi |
183,200 psi |
0.002 in. / in. |
120 °F |
– |
|
›Crystal Clear™ 206
|
600 cps |
– |
100A:90B |
4.5 hours |
– |
7 days |
80 |
– |
1.036 g/cc |
26.7 cu. in./lb. |
Clear |
– |
2,500 psi |
73,200 psi |
– |
10 % |
– |
6,385 psi |
40,000 psi |
10,650 psi |
200,000 psi |
0.002 in. / in. |
120 °F |
– |
|
›Crystal Clear™ 220
|
675 cps |
– |
100A:75B |
22 minutes |
– |
Overnight Followed By Post Cure |
85 |
– |
1.07 g/cc |
25.9 cu. in./lb. |
Clear |
– |
– |
286,000 psi |
8,190 psi |
12 % |
– |
10,100 psi |
87,000 psi |
11,400 psi |
305,000 psi |
0.0173 in. / in. |
176 °F |
– |
|
›Crystal Clear™ 221
|
675 cps |
– |
100A:75B |
75 minutes |
– |
Overnight Followed By Post Cure |
85 |
– |
1.07 g/cc |
25.9 cu. in./lb. |
Clear |
– |
– |
286,000 psi |
8,190 psi |
12 % |
– |
10,100 psi |
87,000 psi |
11,400 psi |
305,000 psi |
0.0173 in. / in. |
176 °F |
– |
|
›Crystal Clear™ 222 - Mercury Free
|
800 cps |
– |
100A:75B |
20 minutes |
– |
16 hours |
83 |
– |
1.07 g/cc |
25.9 cu. in./lb. |
Clear |
– |
– |
358,000 psi |
8,990 psi |
6.3% % |
– |
10,830 psi |
115,000 psi |
11,300 psi |
292,000 psi |
0.0135 in. / in. |
181 °F |
– |
|
›EZ-Spray™ Plastic
|
Variable |
1A:1B |
– |
2 seconds |
– |
3 hours |
75 |
– |
1.11 g/cc |
25 cu. in./lb. |
Off White |
– |
– |
100,000 psi |
2,650 psi |
10 % |
– |
5,000 psi |
45,000 psi |
5,000 psi |
153,000 psi |
0.016 in. / in. |
130 °F |
– |
|
›EZ-Spray™ StyroCoat™
|
Variable |
1A:1B |
– |
2 seconds |
– |
60 minutes |
80 |
– |
1.12 g/cc |
24.7 cu. in./lb. |
Off White |
– |
– |
131,000 psi |
3,170 psi |
20 % |
– |
5,000 psi |
47,600 psi |
6,400 psi |
205,000 psi |
0.015 in. / in. |
130 °F |
– |
|
›Feather Lite™
|
410 cps |
1A:1B |
– |
8.5 minutes |
– |
2 hours |
58 |
– |
0.67 g/cc |
41.3 cu. in./lb. |
Beige |
– |
– |
156,000 psi |
2,160 psi |
1.6 % |
– |
3,070 psi |
53,700 psi |
3,440 psi |
164,300 psi |
0.003 in. / in. |
140 °F |
– |
|
›KX Flex™ 40
|
800 cps |
1A:1B |
1A:1B |
2.5 minutes |
30 minutes |
24 hours |
– |
40 |
1.07 g/cc |
25.9 cu. in./lb. |
Translucent White |
– |
457 psi |
– |
– |
400 % |
– |
– |
– |
– |
– |
0.002 in. / in. |
– |
– |
|
›KX Flex™ 60
|
800 cps |
1A:1B |
1A:1B |
2.5 minutes |
30 minutes |
24 hours |
– |
60 |
1.15 g/cc |
24.1 cu. in./lb. |
Off-White |
– |
1,800 psi |
– |
– |
125 % |
– |
– |
– |
– |
– |
0.005 in. / in. |
– |
– |
|
›KX Flex™ 90
|
800 cps |
– |
100A:120B |
2.5 minutes |
30 minutes |
24 hours |
– |
90 |
1.15 g/cc |
24.1 cu. in./lb. |
Off-White |
– |
1,800 psi |
– |
– |
125 % |
– |
– |
– |
– |
– |
0.005 in. / in. |
– |
– |
|
›Plasti-Paste™
|
Paste |
1A:3B |
41A:100B |
10 minutes |
90 minutes |
24 hours |
70 |
– |
1.16 g/cc |
23.9 cu. in./lb. |
Off White |
– |
– |
168,100 psi |
1,600 psi |
1.5 % |
– |
3,420 psi |
48,800 psi |
3,410 psi |
150,000 psi |
0.005 in. / in. |
130 °F |
– |
|
›Plasti-Paste™ II
|
Paste |
1A:2B |
62A:100B |
10 minutes |
90 minutes |
24 hours |
70 |
– |
1.0 g/cc |
27.73 cu. in./lb. |
Off White |
– |
– |
235,000 psi |
2,150 psi |
1.14 % |
– |
4,980 psi |
62,700 psi |
3,840 psi |
203,000 psi |
0.005 in. / in. |
130 °F |
– |
|
›Shell Shock™ FAST
|
3,000 cps |
1A:4B |
1A:5B |
3 minutes |
– |
60 minutes |
85 |
– |
1.60 g/cc |
17.3 cu. in./lb. |
Beige |
– |
3,100 psi |
435,000 psi |
– |
0.4 % |
– |
9,000 psi |
500,000 psi |
7,150 psi |
980,000 psi |
0.0006 in. / in. |
135 °F |
– |
|
›Shell Shock™ SLOW
|
3,000 cps |
1A:4B |
1A:5B |
8 minutes |
– |
5 hours |
85 |
– |
1.60 g/cc |
17.3 cu. in./lb. |
Beige |
– |
3,100 psi |
435,000 psi |
– |
0.4 % |
– |
9,000 psi |
500,000 psi |
7,150 psi |
980,000 psi |
0.0006 in. / in. |
135 °F |
– |
|
›Simpact™ 60A
|
1,100 cps |
1A:1B |
100A:94B |
4 minutes |
2 hours |
48 hours |
– |
60 |
1.08 g/cc |
25.7 cu. in./lb. |
White |
142 pli |
990 psi |
– |
– |
400 % |
312 psi |
– |
– |
– |
– |
<.007 in. / in. |
– |
– |
|
›Simpact™ 80A
|
2,000 cps |
– |
100A:60B |
15 minutes |
4 hours |
48 hours |
– |
80 |
1.09 g/cc |
25.4 cu. in./lb. |
Amber |
182 pli |
2,295 psi |
– |
– |
164 % |
1,213 psi |
– |
– |
– |
– |
<.007 in. / in. |
– |
– |
|
›Simpact™ 85A
|
1,100 cps |
– |
85A:100B |
4 minutes |
2 hours |
48 hours |
– |
85 |
1.09 g/cc |
25.4 cu. in./lb. |
Off White |
182 pli |
1,573 psi |
– |
– |
164 % |
1,213 psi |
– |
– |
– |
– |
<.007 in. / in. |
– |
– |
|
›SMASH! Plastic™
|
900 cps |
1A:1B |
– |
5 minutes |
90 minutes |
16 hours |
80 |
– |
1.036 g/cc |
26.7 cu. in./lb. |
Clear |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
0.0001 in. / in. |
– |
– |
|
›Smooth-Cast™ 300
|
80 cps |
1A:1B |
100A:90B |
3 minutes |
– |
10 minutes |
70 |
– |
1.05 g/cc |
26.4 cu. in./lb. |
White |
– |
3,000 psi |
139,500 psi |
– |
5 % |
– |
4,000 psi |
45,800 psi |
4,510 psi |
128,000 psi |
0.01 in. / in. |
120 °F |
– |
|
›Smooth-Cast™ 300Q
|
80 cps |
1A:1B |
100A:90B |
30 seconds |
– |
5 minutes |
70 |
– |
1.05 g/cc |
26.4 cu. in./lb. |
White |
– |
3,000 psi |
139,500 psi |
– |
5 % |
– |
4,000 psi |
45,800 psi |
4,510 psi |
128,000 psi |
0.01 in. / in. |
120 °F |
– |
|
›Smooth-Cast™ 305
|
80 cps |
1A:1B |
100A:90B |
7 minutes |
– |
30 minutes |
70 |
– |
1.05 g/cc |
26.4 cu. in./lb. |
White |
– |
3,000 psi |
134,000 psi |
– |
7.5 % |
– |
3,800 psi |
44,900 psi |
4,000 psi |
118,000 psi |
0.0065 in. / in. |
120 °F |
– |
|
›Smooth-Cast™ 310
|
80 cps |
1A:1B |
100A:90B |
20 minutes |
– |
4 hours |
70 |
– |
1.05 g/cc |
26.4 cu. in./lb. |
White |
– |
3,000 psi |
134,000 psi |
– |
7.5 % |
– |
3,800 psi |
44,900 psi |
4,000 psi |
118,000 psi |
0.0065 in. / in. |
120 °F |
– |
|
›Smooth-Cast™ 320
|
80 cps |
1A:1B |
100A:90B |
3 minutes |
– |
10 minutes |
70 |
– |
1.05 g/cc |
26.4 cu. in./lb. |
Off White |
– |
3,000 psi |
138,000 psi |
– |
10 % |
– |
3,650 psi |
45,800 psi |
4,500 psi |
132,000 psi |
0.01 in. / in. |
140 °F |
– |
|
›Smooth-Cast™ 321
|
80 cps |
1A:1B |
100A:90B |
9 minutes |
– |
30 minutes |
70 |
– |
1.05 g/cc |
26.4 cu. in./lb. |
Off White |
– |
3,000 psi |
138,000 psi |
– |
8 % |
– |
3,550 psi |
40,300 psi |
3,500 psi |
110,000 psi |
0.007 in. / in. |
140 °F |
– |
|
›Smooth-Cast™ 322
|
80 cps |
1A:1B |
100A:90B |
20 minutes |
– |
4 hours |
70 |
– |
1.05 g/cc |
26.4 cu. in./lb. |
Off White |
– |
3,000 psi |
134,000 psi |
– |
8 % |
– |
3,550 psi |
40,300 psi |
3,500 psi |
110,000 psi |
0.007 in. / in. |
140 °F |
– |
|
›Smooth-Cast™ 325
|
100 cps |
1A:1B |
115A:100B |
2.5 minutes |
– |
10 minutes |
72 |
– |
1.07 g/cc |
25.9 cu. in./lb. |
Clear Amber |
– |
3,170 psi |
140,000 psi |
– |
10 % |
– |
3,500 psi |
36,500 psi |
3,690 psi |
101,000 psi |
0.01 in. / in. |
120 °F |
– |
|
›Smooth-Cast™ 326
|
100 cps |
1A:1B |
115A:100B |
9 minutes |
– |
60 minutes |
72 |
– |
1.07 g/cc |
25.9 cu. in./lb. |
Clear Amber |
– |
3,170 psi |
140,000 psi |
– |
10 % |
– |
3,080 psi |
32,200 psi |
3,100 psi |
95,700 psi |
0.0075 in. / in. |
120 °F |
– |
|
›Smooth-Cast™ 327
|
100 cps |
1A:1B |
115A:100B |
20 minutes |
– |
4 hours |
72 |
– |
1.07 g/cc |
25.9 cu. in./lb. |
Clear Amber |
– |
3,170 psi |
140,000 psi |
– |
10 % |
– |
3,080 psi |
32,200 psi |
3,100 psi |
95,700 psi |
0.0075 in. / in. |
120 °F |
– |
|
›Smooth-Cast™ 380
|
1,140 cps |
1A:1B |
1A:1B |
6 minutes |
– |
60 minutes |
82 |
– |
1.74 g/cc |
15.9 cu. in./lb. |
Tan |
– |
3,550 psi |
490,000 psi |
– |
1.43 % |
– |
7,860 psi |
126,000 psi |
4,870 psi |
315,000 psi |
0.0025 in. / in. |
125 °F |
– |
|
›Smooth-Cast™ 385
|
3,000 cps |
– |
1A:5B |
20 minutes |
– |
2 hours |
85 |
– |
1.60 g/cc |
17.3 cu. in./lb. |
Beige |
– |
3,100 psi |
400,000 psi |
– |
1 % |
– |
8,500 psi |
400,000 psi |
5,900 psi |
433,000 psi |
0.0006 in. / in. |
135 °F |
– |
|
›Smooth-Cast™ 45D
|
250 cps |
1A:1B |
100A:93B |
5 minutes |
– |
30 minutes |
45 |
– |
1.10 g/cc |
25.2 cu. in./lb. |
Translucent White |
– |
1,560 psi |
– |
– |
100 % |
– |
– |
– |
– |
– |
0.007 in. / in. |
– |
– |
|
›Smooth-Cast™ 57D
|
300 cps |
1A:1B |
100A:93B |
3 minutes |
– |
30 minutes |
57 |
– |
1.05 g/cc |
26.4 cu. in./lb. |
Translucent White |
– |
2,420 psi |
– |
– |
100 % |
– |
– |
– |
– |
– |
0.012 in. / in. |
– |
– |
|
›Smooth-Cast™ 60D
|
430 cps |
1A:1B |
100A:93B |
5 minutes |
– |
30 minutes |
60 |
– |
1.05 g/cc |
26.4 cu. in./lb. |
Translucent White |
– |
2,420 psi |
– |
– |
100 % |
– |
– |
– |
– |
– |
0.012 in. / in. |
– |
– |
|
›Smooth-Cast™ 61D
|
430 cps |
1A:1B |
100A:93B |
7 minutes |
– |
60 minutes |
61 |
– |
1.05 g/cc |
26.4 cu. in./lb. |
Translucent White |
– |
2,420 psi |
– |
– |
100 % |
– |
– |
– |
– |
– |
0.012 in. / in. |
– |
– |
|
›Smooth-Cast™ 65D
|
120 cps |
1A:1B |
100A:93B |
2.5 minutes |
– |
15 minutes |
65 |
– |
1.05 g/cc |
26.4 cu. in./lb. |
White |
– |
2,400 psi |
– |
– |
20 % |
– |
– |
– |
– |
– |
0.01 in. / in. |
– |
– |
|
›Smooth-Cast™ 66D
|
120 cps |
1A:1B |
100A:93B |
7 minutes |
– |
60 minutes |
66 |
– |
1.05 g/cc |
26.4 cu. in./lb. |
Grey |
– |
2,400 psi |
– |
– |
20 % |
– |
– |
– |
– |
– |
0.01 in. / in. |
– |
– |
|
›Smooth-Cast™ ONYX™ FAST
|
100 cps |
100A:100B |
120A:100B |
2.5 minutes |
– |
15 minutes |
80 |
– |
1.09 g/cc |
27.7 cu. in./lb. |
Black |
– |
5,840 psi |
246,000 psi |
– |
4 % |
– |
8,760 psi |
77,400 psi |
8,280 psi |
246,000 psi |
0.010 in. / in. |
– |
250 °F |
|
›Smooth-Cast™ ONYX™ SLOW
|
100 cps |
100A:100B |
120A:100B |
5 minutes |
– |
90 minutes |
80 |
– |
1.09 g/cc |
27.7 cu. in./lb. |
Black |
– |
7,660 psi |
374,000 psi |
– |
3 % |
– |
11,400 psi |
97,900 psi |
10,230 psi |
286,000 psi |
0.012 in. / in. |
– |
212 °F |
|
›TASK™ 11
|
2,000 cps |
– |
100A:100B |
20 minutes |
– |
16 hours |
60 |
– |
1.12 g/cc |
24.7 cu. in./lb. |
Translucent White |
– |
2,500 psi |
– |
– |
100 % |
– |
– |
– |
– |
– |
0.0024 in. / in. |
– |
– |
|
›TASK™ 12
|
2,400 cps |
– |
100A:44B |
20 minutes |
– |
16 hours |
60 |
– |
1.08 g/cc |
26 cu. in./lb. |
Clear Amber |
– |
2,700 psi |
– |
– |
300 % |
– |
– |
– |
– |
– |
0.001 in. / in. |
– |
– |
|
›TASK™ 13
|
800 cps |
– |
100A:120B |
3 minutes |
– |
20 minutes |
50 |
– |
1.15 g/cc |
24.1 cu. in./lb. |
Black |
– |
1,800 psi |
– |
– |
125 % |
– |
– |
– |
– |
– |
0.005 in. / in. |
– |
– |
|
›TASK™ 14
|
800 cps |
– |
100A:120B |
10 minutes |
– |
45 minutes |
50 |
– |
1.15 g/cc |
24.1 cu. in./lb. |
Black |
– |
1,800 psi |
– |
– |
125 % |
– |
– |
– |
– |
– |
0.0035 in. / in. |
– |
– |
|
›TASK™ 15
|
600 cps |
– |
75A:100B |
6 minutes |
– |
1 hour |
75 |
– |
1.12 g/cc |
24.7 cu. in./lb. |
Opaque White |
– |
2,720 psi |
126,000 psi |
– |
20 % |
– |
5,450 psi |
60,000 psi |
5,450 psi |
170,000 psi |
0.0042 in. / in. |
117 °F |
– |
|
›TASK™ 16
|
1,400 cps |
– |
1A:2B |
6 minutes |
90 minutes |
24 hours |
30 |
80 |
1.08 g/cc |
25.64 cu. in./lb. |
Light Yellow |
197 pli |
2,264 psi |
– |
– |
233 % |
855 psi |
– |
– |
– |
– |
0.0025 in. / in. |
– |
– |
|
›TASK™ 18
|
4,400 cps |
– |
26A:100B |
20 minutes |
– |
16 hours |
88 |
– |
1.57 g/cc |
17.6 cu. in./lb. |
Metal Gray |
– |
3,250 psi |
514,000 psi |
– |
1 % |
– |
8,420 psi |
97,300 psi |
10,700 psi |
86,000 psi |
0.0006 in. / in. |
149 °F |
– |
|
›TASK™ 2
|
150 cps |
1A:1B |
115A:100B |
7 minutes |
– |
60 minutes |
80 |
– |
1.12 g/cc |
24.7 cu. in./lb. |
White |
– |
6,650 psi |
290,000 psi |
– |
6 % |
– |
8,300 psi |
78,000 psi |
9,500 psi |
288,000 psi |
0.005 in. / in. |
134 °F |
– |
|
›TASK™ 21
|
500 cps |
2A:1B |
2A:1B |
6 minutes |
– |
1 hour |
75 |
– |
1.07 g/cc |
25.9 cu. in./lb. |
White |
– |
5,500 psi |
270,000 psi |
– |
7.5 % |
– |
7,100 psi |
78,500 psi |
7,100 psi |
250,000 psi |
0.0058 in. / in. |
144 °F |
– |
|
›TASK™ 3
|
150 cps |
1A:1B |
115A:100B |
20 minutes |
– |
90 minutes |
80 |
– |
1.12 g/cc |
24.7 cu. in./lb. |
White |
– |
6,650 psi |
290,000 psi |
– |
6 % |
– |
8,300 psi |
78,000 psi |
9,500 psi |
288,000 psi |
0.0025 in. / in. |
134 °F |
– |
|
›TASK™ 4
|
250 cps |
– |
100A:100B |
20 minutes |
– |
16 hours |
83 |
– |
1.167 g/cc |
23.9 cu. in./lb. |
Ivory |
– |
6,500 psi |
130,000 psi |
– |
4 % |
– |
7,400 psi |
75,000 psi |
9,000 psi |
204,000 psi |
0.0035 in. / in. |
110 °F |
– |
|
›TASK™ 5
|
600 cps |
1A:1B |
1A:1B |
3 minutes |
15 minutes |
24 hours |
77 |
– |
1.1 g/cc |
25.2 cu. in./lb. |
Tan |
– |
4,530 psi |
200,000 psi |
– |
5 % |
– |
6,700 psi |
83,000 psi |
6,480 psi |
216,000 psi |
0.007 in. / in. |
145 °F |
– |
|
›TASK™ 6
|
800 cps |
1A:1B |
1A:1B |
7 minutes |
75 minutes |
24 hours |
75 |
– |
1.07 g/cc |
25.9 cu. in./lb. |
Tan |
– |
5,200 psi |
146,000 psi |
– |
4 % |
– |
5,570 psi |
65,000 psi |
6,200 psi |
182,500 psi |
0.0031 in. / in. |
162 °F |
– |
|
›TASK™ 7
|
200 cps |
1A:1B |
104A:100B |
2.5 minutes |
– |
10 minutes |
73 |
– |
1.2 g/cc |
23.1 cu. in./lb. |
Off-White |
– |
3,390 psi |
150,700 psi |
– |
15.1 % |
– |
5,140 psi |
57,600 psi |
5,450 psi |
148,900 psi |
0.0111 in. / in. |
131 °F |
– |
|
›TASK™ 8
|
100 cps |
1A:1B |
120A:100B |
2.5 minutes |
– |
15 minutes |
80 |
– |
1.09 g/cc |
25.4 cu. in./lb. |
Off-White |
– |
5,840 psi |
246,000 psi |
– |
4 % |
– |
8,760 psi |
77,400 psi |
8,280 psi |
271,000 psi |
0.01 in. / in. |
194 °F |
263 °F |
|
›TASK™ 9
|
300 cps |
1A:1B |
115A:100B |
7 minutes |
– |
1 hour |
85 |
– |
1.14 g/cc |
24.3 cu. in./lb. |
Clear Amber |
– |
7,800 psi |
370,000 psi |
– |
6 % |
– |
11,000 psi |
98,000 psi |
11,850 psi |
350,000 psi |
0.009 in. / in. |
131 °F |
– |
Epoxy Casting, Coating and Laminating Resins ›
Product Name |
Mixed Viscosity |
Mix Ratio By Volume |
Mix Ratio By Weight |
Pot Life |
Thin Film Working Time |
Thin Film Recoat Time |
Tack Free Time |
Cure Time |
Barcol 935 Hardness |
Shore D Hardness |
Shore A Hardness |
Specific Gravity |
Specific Volume |
Color |
Die C Tear Strength |
Tensile Strength |
Tensile Modulus |
Ultimate Tensile |
Tensile Elongation |
Elongation @ Break |
100% Modulus |
Compressive Strength |
Compressive Modulus |
Flexural Strength |
Flexural Modulus |
Shrinkage |
Heat Deflection Temp |
Flexural Strength on 6 ply / 10 oz. Laminate |
Tensile Modulus on 6 ply / 10 oz. Laminate |
Flexural Modulus on 6 ply / 10 oz. Laminate |
Ultimate Tensile on 6 ply / 10 oz. Laminate |
Buoyant Force |
Thermal Conductivity |
Refractive Index |
Heat Deflection With Post Cure |
|
›EpoxAcast™ 655 + 101 Hardener
|
23,000 cps |
– |
100A:10B |
30 minutes |
– |
– |
– |
3 hours |
– |
90 |
– |
1.66 g/cc |
16.7 cu. in./lb. |
Grey |
– |
– |
2,040,000 psi |
4,810 psi |
0.54 % |
– |
– |
12,500 psi |
125,500 psi |
7,660 psi |
1,403,000 psi |
0.0006 in. / in. |
135 °F |
– |
– |
– |
– |
– |
0.675 W/M*K |
– |
– |
|
›EpoxAcast™ 650 + 101 Hardener
|
7,000 cps |
– |
100A:12B |
20 minutes |
– |
– |
– |
1 hour |
93 |
– |
– |
1.52 g/cc |
18.22 cu. in./lb. |
Off White |
– |
– |
1,503,000 psi |
6,000 psi |
0.42 % |
– |
– |
16,350 psi |
142,600 psi |
5,890 psi |
710,000 psi |
0.001 in. / in. |
129 °F |
– |
– |
– |
– |
– |
– |
– |
– |
|
›EpoxAcast™ 650 + 102 Hardener
|
7,000 cps |
– |
100A:13B |
90 minutes |
– |
– |
– |
4 hours |
93 |
– |
– |
1.52 g/cc |
18.22 cu. in./lb. |
Off White |
– |
– |
1,503,000 psi |
6,000 psi |
0.42 % |
– |
– |
16,350 psi |
142,600 psi |
5,890 psi |
710,000 psi |
0.001 in. / in. |
129 °F |
– |
– |
– |
– |
– |
– |
– |
– |
|
›EpoxAcast™ 650 + 103 Hardener
|
7,000 cps |
– |
100A:14B |
3.5 hours |
– |
– |
– |
24 hours |
93 |
– |
– |
1.52 g/cc |
18.22 cu. in./lb. |
Off White |
– |
– |
– |
6,000 psi |
0.42 % |
– |
– |
16,350 psi |
142,600 psi |
5,890 psi |
710,000 psi |
0.001 in. / in. |
129 °F |
– |
– |
– |
– |
– |
– |
– |
– |
|
›EpoxAcast™ 650 + HT Hardener
|
5,000 cps |
– |
100A:10B |
3 hours |
– |
– |
– |
Twenty Four Hours Followed By Post Cure |
93 |
– |
– |
1.52 g/cc |
18.22 cu. in./lb. |
Off White |
– |
– |
1,079,000 psi |
6,900 psi |
0.82 % |
– |
– |
15,980 psi |
134,400 psi |
10,850 psi |
775,000 psi |
0.007 in. / in. |
187 °F |
– |
– |
– |
– |
– |
– |
– |
– |
|
›EpoxAcast™ 650 BLACK + 101 Hardener
|
7,000 cps |
– |
100A:12B |
20 minutes |
– |
– |
– |
1 hour |
93 |
– |
– |
1.52 g/cc |
18.22 cu. in./lb. |
Black |
– |
– |
1,503,000 psi |
6,000 psi |
0.42 % |
– |
– |
16,350 psi |
142,600 psi |
5,890 psi |
710,000 psi |
0.001 in. / in. |
129 °F |
– |
– |
– |
– |
– |
– |
– |
– |
|
›EpoxAcast™ 650 BLACK + 102 Hardener
|
7,000 cps |
– |
100A:13B |
90 minutes |
– |
– |
– |
4 hours |
93 |
– |
– |
1.52 g/cc |
18.22 cu. in./lb. |
Black |
– |
– |
1,503,000 psi |
6,000 psi |
0.42 % |
– |
– |
16,350 psi |
142,600 psi |
5,890 psi |
710,000 psi |
0.001 in. / in. |
129 °F |
– |
– |
– |
– |
– |
– |
– |
– |
|
›EpoxAcast™ 650 BLACK + 103 Hardener
|
7,000 cps |
– |
100A:14B |
3.5 hours |
– |
– |
– |
24 hours |
93 |
– |
– |
1.52 g/cc |
18.22 cu. in./lb. |
Black |
– |
– |
1,503,000 psi |
6,000 psi |
0.42 % |
– |
– |
16,350 psi |
142,600 psi |
5,890 psi |
710,000 psi |
0.001 in. / in. |
129 °F |
– |
– |
– |
– |
– |
– |
– |
– |
|
›EpoxAcast™ 650 BLACK + HT Hardener
|
5,000 cps |
– |
100A:10B |
3 hours |
– |
– |
– |
Twenty Four Hours Followed By Post Cure |
93 |
– |
– |
1.52 g/cc |
18.22 cu. in./lb. |
Black |
– |
– |
1,079,000 psi |
6,900 psi |
0.82 % |
– |
– |
15,980 psi |
134,000 psi |
10,850 psi |
775,000 psi |
0.007 in. / in. |
187 °F |
– |
– |
– |
– |
– |
– |
– |
– |
|
›EpoxAcast™ 655 + 102 Hardener
|
23,000 cps |
– |
100A:11B |
75 minutes |
– |
– |
– |
9 hours |
– |
90 |
– |
1.66 g/cc |
16.7 cu. in./lb. |
Grey |
– |
– |
2,040,000 psi |
4,810 psi |
0.54 % |
– |
– |
12,500 psi |
125,500 psi |
7,660 psi |
1,403,000 psi |
0.0006 in. / in. |
135 °F |
– |
– |
– |
– |
– |
0.675 W/M*K |
– |
– |
|
›EpoxAcast™ 655 + 103 Hardener
|
23,000 cps |
– |
100A:12B |
3.5 hours |
– |
– |
– |
24 hours |
– |
90 |
– |
1.66 g/cc |
16.7 cu. in./lb. |
Grey |
– |
– |
2,040,000 psi |
4,810 psi |
0.54 % |
– |
– |
12,500 psi |
125,500 psi |
7,660 psi |
1,403,000 psi |
0.0006 in. / in. |
135 °F |
– |
– |
– |
– |
– |
0.675 W/M*K |
– |
– |
|
›EpoxAcast™ 655 + HT Hardener
|
12,000 cps |
– |
100A:8B |
4 hours |
– |
– |
– |
Twenty Four Hours Followed By Post Cure |
– |
90 |
– |
1.64 g/cc |
16.5 cu. in./lb. |
Grey |
– |
– |
7,200,000 psi |
6,000 psi |
0.50 % |
– |
– |
15,700 psi |
270,000 psi |
– |
– |
0.001 in. / in. |
225 °F |
– |
– |
– |
– |
– |
0.675 W/M*K |
– |
– |
|
›EpoxAcast™ 670 HT
|
6,000 cps |
– |
100A:16B |
3 hours |
– |
– |
– |
Twenty Four Hours Followed By Post Cure |
– |
90 |
– |
1.15 g/cc |
20.51 cu. in./lb. |
Beige |
– |
4,500 psi |
332,000 psi |
– |
0.65 % |
– |
– |
13,000 psi |
101,400 psi |
11,000 psi |
254,000 psi |
0.002 in. / in. |
350 °F |
– |
– |
– |
– |
– |
– |
– |
– |
|
›EpoxAcast™ 690
|
280 cps |
– |
100A:30B |
5 hours |
– |
– |
– |
24 hours |
– |
80 |
– |
1.10 g/cc |
25 cu. in./lb. |
Clear |
– |
6,630 psi |
572,000 psi |
– |
1.8 % |
– |
– |
9,610 psi |
91,300 psi |
10,980 psi |
410,000 psi |
0.002 in. / in. |
115 °F |
– |
– |
– |
– |
– |
– |
1.565 nm |
– |
|
›EpoxAcast™ 692 Deep Pour
|
370 cps |
– |
100A:40B |
12 hours |
– |
– |
– |
– |
– |
80 |
– |
1.08 g/cc |
25.7 cu. in./lb. |
Clear |
– |
– |
378,000 psi |
4,585 psi |
3.1 % |
– |
– |
5,777 psi |
82,000 psi |
6,780 psi |
203,000 psi |
0.007 in. / in. |
100 °F |
– |
– |
– |
– |
– |
– |
1.5372 nm |
– |
|
›EpoxAcoat™ NEUTRAL
|
Light Paste |
5A:1B |
100A:15B |
20 minutes |
40 minutes |
60 minutes |
4 hours |
16 hours |
87 |
85 |
– |
1.43 g/cc |
19.4 cu. in./lb. |
Neutral |
– |
– |
– |
26,000 psi |
– |
– |
– |
24,000 psi |
– |
30,000 psi |
– |
0.00015 in. / in. |
133 °F |
– |
– |
– |
– |
– |
– |
– |
– |
|
›EpoxAcoat™ GREY
|
Light Paste |
5A:1B |
100A:15B |
20 minutes |
40 minutes |
60 minutes |
4 hours |
16 hours |
87 |
85 |
– |
1.43 g/cc |
19.4 cu. in./lb. |
Grey |
– |
– |
– |
26,000 psi |
– |
– |
– |
24,000 psi |
– |
30,000 psi |
– |
0.00015 in. / in. |
133 °F |
– |
– |
– |
– |
– |
– |
– |
– |
|
›EpoxAcoat™ HT
|
Light Paste |
– |
100A:18B |
40 minutes |
75 minutes |
4 hours |
– |
24 hours |
– |
85 |
– |
– |
– |
Dark Red |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
133 °F |
– |
– |
– |
– |
– |
– |
– |
284 °F |
|
›EpoxAcoat™ RED
|
Light Paste |
5A:1B |
100A:15B |
20 minutes |
40 minutes |
60 minutes |
4 hours |
16 hours |
87 |
85 |
– |
1.43 g/cc |
19.4 cu. in./lb. |
Red |
– |
– |
– |
26,000 psi |
– |
– |
– |
24,000 psi |
– |
30,000 psi |
– |
0.00015 in. / in. |
133 °F |
– |
– |
– |
– |
– |
– |
– |
– |
|
›EpoxAcoat™ WHITE
|
Light Paste |
5A:1B |
100A:15B |
20 minutes |
40 minutes |
60 minutes |
4 hours |
16 hours |
87 |
85 |
– |
1.43 g/cc |
19.4 cu. in./lb. |
White |
– |
– |
– |
26,000 psi |
– |
– |
– |
24,000 psi |
– |
30,000 psi |
– |
0.00015 in. / in. |
133 °F |
– |
– |
– |
– |
– |
– |
– |
– |
|
›EpoxAmite™ 101
|
1,000 cps |
4A:1B |
100A:24B |
11 minutes |
30 minutes |
– |
– |
8 hours |
– |
84 |
– |
1.13 g/cc |
24.5 cu. in./lb. |
Clear Yellow |
– |
– |
445,000 psi |
7,930 psi |
2.45 % |
– |
– |
11,550 psi |
121,400 psi |
13,660 psi |
468,000 psi |
– |
133 °F |
30,700 psi |
– |
– |
35,100 psi |
– |
– |
– |
– |
|
›EpoxAmite™ 102
|
650 cps |
3A:1B |
100A:29B |
22 minutes |
90 minutes |
– |
– |
15 hours |
– |
80 |
– |
1.11 g/cc |
25 cu. in./lb. |
Clear Yellow |
– |
– |
450,000 psi |
8,180 psi |
3.15 % |
– |
– |
10,970 psi |
122,000 psi |
12,220 psi |
423,000 psi |
– |
120 °F |
28,500 psi |
– |
– |
26,800 psi |
– |
– |
– |
– |
|
›EpoxAmite™ 103
|
650 cps |
3A:1B |
100A:28.4B |
55 minutes |
180 minutes |
– |
– |
24 hours |
– |
80 |
– |
1.10 g/cc |
25.2 cu. in./lb. |
Clear Yellow |
– |
– |
452,000 psi |
7,910 psi |
2.63 % |
– |
– |
10,500 psi |
104,000 psi |
12,300 psi |
429,000 psi |
– |
127 °F |
20,700 psi |
– |
– |
27,000 psi |
– |
– |
– |
– |
|
›EpoxAmite™ HT
|
650 cps |
– |
100A:33B |
60 minutes |
180 minutes |
– |
– |
24 hours |
– |
80 |
– |
1.10 g/cc |
25.2 cu. in./lb. |
Clear |
– |
– |
342,000 psi |
6,500 psi |
2.3 % |
– |
– |
16,600 psi |
168,000 psi |
12,325 psi |
429,000 psi |
– |
– |
20,700 psi |
2,150,000 psi |
2,216,000 psi |
32,100 psi |
– |
– |
– |
300 °F |
|
›EpoxAmite™ WHITE 101
|
3,400 cps |
– |
100A:20B |
20 minutes |
45 minutes |
– |
– |
15 hours |
– |
83 |
– |
1.25 g/cc |
22.2 cu. in./lb. |
White |
– |
– |
627,000 psi |
5,130 psi |
0.8 % |
– |
– |
16,290 psi |
116,000 psi |
8,770 psi |
465,000 psi |
– |
136 °F |
29,000 psi |
– |
– |
24,700 psi |
– |
– |
– |
– |
|
›EpoxAmite™ WHITE 102
|
2,800 cps |
– |
100A:23B |
62 minutes |
120 minutes |
– |
– |
24 hours |
– |
85 |
– |
1.23 g/cc |
22.5 cu. in./lb. |
White |
– |
– |
557,000 psi |
5,600 psi |
1.2 % |
– |
– |
11,960 psi |
114,000 psi |
8,350 psi |
446,000 psi |
– |
133 °F |
31,600 psi |
– |
– |
30,700 psi |
– |
– |
– |
– |
|
›EPSILON™ + 101 Hardener
|
Variable |
– |
100A:20B |
15 minutes |
45 minutes |
60 minutes |
2 hours |
16 hours |
– |
75 |
– |
1.16 g/cc |
23.9 cu. in./lb. |
Beige |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
|
›Epsilon™ PRO
|
4,000 cps |
2A:1B |
100A:44B |
22 minutes |
35 minutes |
3 hours |
4 hours |
16 hours |
– |
65 |
– |
1.11 g/cc |
25.0 cu. in./lb. |
Clear Amber |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
|
›EPSILON™ + 102 Hardener
|
Variable |
– |
100A:25B |
30 minutes |
120 minutes |
180 minutes |
5 hours |
24 hours |
– |
75 |
– |
1.14 g/cc |
24.3 cu. in./lb. |
Beige |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
|
›EZ-Spray™ StyroCoat™
|
Variable |
1A:1B |
– |
2 seconds |
– |
– |
– |
60 minutes |
– |
80 |
– |
1.12 g/cc |
24.7 cu. in./lb. |
Off White |
– |
– |
131,000 psi |
3,170 psi |
– |
20 % |
– |
5,000 psi |
47,600 psi |
6,400 psi |
205,000 psi |
0.015 in. / in. |
130 °F |
– |
– |
– |
– |
– |
– |
– |
– |
|
›Free Form™ AIR FAST
|
Dough |
1A:1B |
1A:1B |
– |
– |
– |
– |
– |
– |
60 |
– |
0.45 g/cc |
61.6 cu. in./lb. |
Grey |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
145 °F |
– |
– |
– |
– |
10.4 lb/ft³ |
– |
– |
– |
|
›Free Form™ AIR
|
Dough |
1A:1B |
1A:1B |
– |
– |
– |
– |
– |
– |
50 |
– |
0.45 g/cc |
61.6 cu. in./lb. |
Grey |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
140 °F |
– |
– |
– |
– |
10.4 lb/ft³ |
– |
– |
– |
|
›Free Form™ AIR Fire Safe
|
Dough |
1A:1B |
– |
– |
– |
– |
– |
– |
– |
73 |
– |
0.8 g/cc |
34.6 cu. in./lb. |
Grey |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
140 °F |
– |
– |
– |
– |
– |
– |
– |
– |
|
›Free Form™ AIR HT
|
Dough |
2A:1B |
2A:1B |
150 minutes |
– |
– |
– |
16 hours |
– |
55 |
– |
0.51 g/cc |
54.31 cu. in./lb. |
Grey |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
300 °F |
– |
– |
– |
– |
– |
– |
– |
400 °F |
|
›Free Form™ Habitat™ Black
|
Dough |
1A:1B |
1A:1B |
60 minutes |
– |
– |
– |
16 hours |
– |
85 |
– |
1.6 g/cc |
17.3 cu. in./lb. |
Black |
– |
3,480 psi |
– |
– |
– |
– |
– |
14,390 psi |
– |
– |
– |
– |
160 °F |
– |
– |
– |
– |
– |
– |
– |
212 °F |
|
›Free Form™ Habitat™ Fire Safe™
|
Dough |
1A:1B |
1A:1B |
90 minutes |
– |
– |
– |
16 hours |
– |
85 |
– |
1.44 g/cc |
17.3 cu. in./lb. |
Grey |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
160 °F |
– |
– |
– |
– |
– |
– |
– |
212 °F |
|
›Free Form™ Habitat™ Flex FR
|
Dough |
1A:1B |
1A:1B |
90 minutes |
– |
– |
– |
24 hours |
– |
– |
90 |
1.55 g/cc |
17.9 cu. in./lb. |
Light Brown |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
|
›Free Form™ SCULPT
|
Putty |
1A:1B |
– |
1.5 hours |
– |
– |
– |
24 hours |
– |
80 |
– |
1.33 g/cc |
20.73 cu. in./lb. |
Grey |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
<.001 in. / in. |
150 °F |
– |
– |
– |
– |
– |
– |
– |
– |
|
›Habitat Cast N Coat™
|
13,500 cps |
1A:1B |
1A:1B |
85 minutes |
– |
– |
– |
16 hours |
– |
85 |
– |
1.51 g/cc |
18.35 cu. in./lb. |
Tan |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
131 °F |
– |
– |
– |
– |
– |
– |
– |
– |
|
›Habitat™ Folding Powder
|
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
|
›Plasti-Paste™ EPOXY
|
Paste |
2A:1B |
2A:1B |
40 minutes |
– |
60 minutes |
– |
16 hours |
– |
80 |
– |
1.0 g/cc |
27.73 cu. in./lb. |
Off-White |
– |
– |
470,000 psi |
3,320 psi |
– |
0.83 % |
– |
7,700 psi |
138,000 psi |
9,186 psi |
2,273,000 psi |
0.001 in. / in. |
160 °F |
– |
– |
– |
– |
– |
– |
– |
– |
|
›Tarbender™
|
1,100 cps |
2A:1B |
100A:41B |
45 minutes |
2 hours |
6 hours |
8 hours |
16 hours |
– |
75 |
– |
1.09 g/cc |
25.4 cu. in./lb. |
Clear |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
|
›UreCoat™
|
3,800 cps |
– |
100A:10B |
8 minutes |
– |
30 minutes |
2 hours |
16 hours |
– |
– |
70 |
1.05 g/cc |
26.4 cu. in./lb. |
Translucent Amber |
256 pli |
1,360 psi |
– |
– |
– |
876 % |
503 psi |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
|
›UreCoat™ Matting Powder
|
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
|
›XTC-3D™
|
350 cps |
2A:1B |
100A:42B |
10 minutes |
20 minutes |
90 minutes |
2 hours |
3.5 hours |
– |
80 |
– |
1.09 g/cc |
25.1 cu. in./lb. |
Clear (Slightly Yellow In Thick Sections) |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
Epoxy Putties ›
Product Name |
Mixed Viscosity |
Mix Ratio By Volume |
Mix Ratio By Weight |
Pot Life |
Cure Time |
Shore D Hardness |
Shore A Hardness |
Specific Gravity |
Specific Volume |
Color |
Tensile Strength |
Compressive Strength |
Shrinkage |
Heat Deflection Temp |
Heat Deflection With Post Cure |
Buoyant Force |
|
›Free Form™ AIR FAST
|
Dough |
1A:1B |
1A:1B |
– |
– |
60 |
– |
0.45 g/cc |
61.6 cu. in./lb. |
Grey |
– |
– |
– |
145 °F |
– |
10.4 lb/ft³ |
|
›Free Form™ AIR
|
Dough |
1A:1B |
1A:1B |
– |
– |
50 |
– |
0.45 g/cc |
61.6 cu. in./lb. |
Grey |
– |
– |
– |
140 °F |
– |
10.4 lb/ft³ |
|
›Free Form™ AIR Fire Safe
|
Dough |
1A:1B |
– |
– |
– |
73 |
– |
0.8 g/cc |
34.6 cu. in./lb. |
Grey |
– |
– |
– |
140 °F |
– |
– |
|
›Free Form™ AIR HT
|
Dough |
2A:1B |
2A:1B |
150 minutes |
16 hours |
55 |
– |
0.51 g/cc |
54.31 cu. in./lb. |
Grey |
– |
– |
– |
300 °F |
400 °F |
– |
|
›Free Form™ Habitat™ Black
|
Dough |
1A:1B |
1A:1B |
60 minutes |
16 hours |
85 |
– |
1.6 g/cc |
17.3 cu. in./lb. |
Black |
3,480 psi |
14,390 psi |
– |
160 °F |
212 °F |
– |
|
›Free Form™ Habitat™ Fire Safe™
|
Dough |
1A:1B |
1A:1B |
90 minutes |
16 hours |
85 |
– |
1.44 g/cc |
17.3 cu. in./lb. |
Grey |
– |
– |
– |
160 °F |
212 °F |
– |
|
›Free Form™ Habitat™ Flex FR
|
Dough |
1A:1B |
1A:1B |
90 minutes |
24 hours |
– |
90 |
1.55 g/cc |
17.9 cu. in./lb. |
Light Brown |
– |
– |
– |
– |
– |
– |
|
›Free Form™ SCULPT
|
Putty |
1A:1B |
– |
1.5 hours |
24 hours |
80 |
– |
1.33 g/cc |
20.73 cu. in./lb. |
Grey |
– |
– |
<.001 in. / in. |
150 °F |
– |
– |
|
›Habitat™ Folding Powder
|
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
Mix and Pour Expanding Foams ›
Product Name |
Mixed Viscosity |
Mix Ratio By Volume |
Mix Ratio By Weight |
Pot Life |
Tack Free Time |
Handling Time |
Cure Time |
Expansion (approximate) |
Foam Density |
Specific Gravity |
Specific Volume |
Color |
Density |
|
›EZ-Spray™ FlexFoam
|
1,000 cps |
1A:1B |
– |
10 seconds |
2 minutes |
– |
15 minutes |
7 times |
7 lb/ft³ |
0.11 g/cc |
– |
White |
– |
|
›EZ-Spray™ Foam
|
400 cps |
1A:1B |
– |
13 seconds |
2 minutes |
– |
10 minutes |
7 times |
– |
0.128 g/cc |
– |
Tan |
8 lb/ft³ |
|
›FlexFoam-iT!™ 14
|
1,000 cps |
1A:2B |
100A:190B |
60 seconds |
– |
45 minutes |
2 hours |
4 times |
14 lb/ft³ |
0.22 g/cc |
114 cu. in./lb. |
White |
– |
|
›FlexFoam-iT!™ 15 Tuff Stuff
|
1,000 cps |
1A:2B |
100A:185B |
2 minutes |
– |
90 minutes |
4 hours |
4 times |
15 lb/ft³ |
0.24 g/cc |
115 cu. in./lb. |
White |
– |
|
›FlexFoam-iT!™ 17
|
1,000 cps |
1A:2B |
100A:185B |
60 seconds |
– |
30 minutes |
2 hours |
3.5 times |
17 lb/ft³ |
0.27 g/cc |
93 cu. in./lb. |
White |
– |
|
›FlexFoam-iT!™ 23 FR
|
1,000 cps |
– |
85A:100B |
90 seconds |
– |
60 minutes |
2 hours |
2 times |
23 lb/ft³ |
0.37 g/cc |
68 cu. in./lb. |
White |
– |
|
›FlexFoam-iT!™ 25
|
1,000 cps |
– |
1A:2B |
90 seconds |
– |
25 minutes |
2 hours |
2 times |
25 lb/ft³ |
0.4 g/cc |
63 cu. in./lb. |
White |
– |
|
›FlexFoam-iT!™ 6 Pillow Soft
|
1,000 cps |
1A:1B |
105A:100B |
35 seconds |
– |
60 minutes |
2 hours |
10 times |
6 lb/ft³ |
0.09 g/cc |
280 cu. in./lb. |
White |
– |
|
›FlexFoam-iT!™ 7 FR
|
1,000 cps |
1A:1B |
100A:88B |
35 seconds |
– |
60 minutes |
2 hours |
8 times |
7 lb/ft³ |
0.11 g/cc |
229 cu. in./lb. |
White |
– |
|
›FlexFoam-iT!™ III
|
1,000 cps |
1A:2B |
57.5A:100B |
35 seconds |
– |
25 minutes |
2 hours |
15 times |
3 lb/ft³ |
0.05 g/cc |
504 cu. in./lb. |
White |
– |
|
›FlexFoam-iT!™ IV Tuff Stuff
|
1,000 cps |
– |
80A:100B |
30 seconds |
– |
45 minutes |
2 hours |
13 times |
4 lb/ft³ |
0.06 g/cc |
420 cu. in./lb. |
White |
– |
|
›FlexFoam-iT!™ V
|
1,000 cps |
1A:1B |
105A:100B |
50 seconds |
– |
45 minutes |
2 hours |
11 times |
5 lb/ft³ |
0.08 g/cc |
315 cu. in./lb. |
White |
– |
|
›FlexFoam-iT!™ VIII Pillow Soft
|
1,000 cps |
1A:2B |
52.6A:100B |
35 seconds |
– |
25 minutes |
2 hours |
7 times |
8 lb/ft³ |
0.13 g/cc |
194 cu. in./lb. |
White |
– |
|
›FlexFoam-iT!™ X
|
1,000 cps |
1A:1B |
105A:100B |
50 seconds |
– |
45 minutes |
2 hours |
6 times |
10 lb/ft³ |
0.16 g/cc |
157 cu. in./lb. |
White |
– |
|
›FOAM-iT!™ 10
|
400 cps |
1A:1B |
100A:87B |
1.5 minutes |
20 minutes |
– |
2 hours |
6 times |
10 lb/ft³ |
0.16 g/cc |
157 cu. in./lb. |
Beige |
– |
|
›FOAM-iT!™ 10 SLOW
|
400 cps |
1A:1B |
100A:87B |
3.5 minutes |
1 hour |
– |
4 hours |
6 times |
10 lb/ft³ |
0.16 g/cc |
157 cu. in./lb. |
Beige |
– |
|
›FOAM-iT!™ 15
|
500 cps |
1A:1B |
100A:87B |
1.5 minutes |
20 minutes |
– |
2 hours |
4 times |
15 lb/ft³ |
0.24 g/cc |
105 cu. in./lb. |
Beige |
– |
|
›FOAM-iT!™ 26
|
500 cps |
1A:1B |
100A:90B |
1.5 minutes |
20 minutes |
– |
2 hours |
2 times |
26 lb/ft³ |
0.42 g/cc |
60 cu. in./lb. |
White |
– |
|
›FOAM-iT!™ 3
|
200 cps |
1A:1B |
100A:87B |
1 minute |
20 minutes |
– |
2 hours |
18 times |
3 lb/ft³ |
0.05 g/cc |
504 cu. in./lb. |
Beige |
– |
|
›FOAM-iT!™ 4
|
300 cps |
1A:1B |
100A:87B |
1.5 minutes |
20 minutes |
– |
2 hours |
14 times |
4 lb/ft³ |
0.06 g/cc |
420 cu. in./lb. |
Beige |
– |
|
›FOAM-iT!™ 4 BLACK
|
300 cps |
1A:1B |
100A:87B |
1.5 minutes |
20 minutes |
– |
2 hours |
14 times |
4 lb/ft³ |
0.06 g/cc |
420 cu. in./lb. |
Black |
– |
|
›FOAM-iT!™ 5
|
300 cps |
1A:1B |
100A:87B |
1.5 minutes |
20 minutes |
– |
2 hours |
10 times |
5 lb/ft³ |
0.08 g/cc |
315 cu. in./lb. |
Beige |
– |
|
›FOAM-iT!™ 8
|
300 cps |
– |
2A:1B |
1.5 minutes |
20 minutes |
– |
2 hours |
8 times |
8 lb/ft³ |
0.13 g/cc |
194 cu. in./lb. |
Off White |
– |
|
›Soma Foama™ 15
|
10,000 cps |
2A:1B |
100A:47B |
30 seconds |
– |
20 minutes |
1 hour |
4 times |
15 lb/ft³ |
0.24 g/cc |
115 cu. in./lb. |
White |
– |
|
›Soma Foama™ 25
|
10,000 cps |
1A:1B |
1A:1B |
90 seconds |
– |
20 minutes |
1 hour |
2-3 times |
25 lb/ft³ |
0.40 g/cc |
69 cu. in./lb. |
White |
– |
Adhesives ›
Product Name |
Mixed Viscosity |
Mix Ratio By Volume |
Mix Ratio By Weight |
Pot Life |
Handling Time |
Cure Time |
Barcol 935 Hardness |
Shore D Hardness |
Shore A Hardness |
Specific Gravity |
Specific Volume |
Color |
Die C Tear Strength |
Tensile Strength |
Tensile Modulus |
Elongation @ Break |
Compressive Strength |
Compressive Modulus |
Flexural Strength |
Shrinkage |
Heat Deflection Temp |
Modulus of Elasticity in Tension |
Sag Resistance |
Thermal Conductivity |
Compressive Yield Strength |
Modulus of Elasticity in Compression |
|
›Black Panther™ 85
|
5,400 cps |
1A:1B |
100A:92B |
3.5 minutes |
– |
2.5 hours |
– |
– |
85 |
1.11 g/cc |
25 cu. in./lb. |
Black |
175 pli |
3,400 psi |
– |
121 % |
– |
– |
– |
0.0038 in. / in. |
– |
700 psi |
– |
– |
– |
– |
|
›EA-40™
|
Light Paste |
1A:1B |
– |
2 hours |
– |
24 hours |
66 |
– |
– |
1.10 g/cc |
– |
Clear Amber |
– |
3,400 psi |
– |
1.0 % |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
|
›Metalset™ A4
|
Paste |
1A:1B |
1A:1B |
22 minutes |
– |
16 hours |
71 |
– |
– |
1.43 g/cc |
19.5 cu. in./lb. |
Metallic |
– |
3,600 psi |
165,000 psi |
1.2 % |
7,500 psi |
160,000 psi |
– |
– |
180 °F |
– |
1/4 in. |
0.418 W/M*K |
– |
– |
|
›MT-13™
|
Light Paste |
1A:1B |
100A:123B |
35 minutes |
– |
16 hours |
72 |
– |
– |
1.37 g/cc |
– |
White |
– |
4,300 psi |
285,000 psi |
0.8 % |
8,700 psi |
165,000 psi |
– |
– |
– |
– |
1/16 in. |
– |
– |
– |
|
›PC-3™
|
Paste |
1A:1B |
1A:1B |
20 minutes |
2 hours |
24 hours |
75 |
– |
– |
1.4 g/cc |
20 cu. in./lb. |
Black |
– |
3,000 psi |
– |
– |
– |
– |
5,000 psi |
0.003 in. / in. |
– |
– |
– |
– |
5,000 psi |
– |
|
›Si-Tac™
|
80,000 cps |
1A:1B |
1A:1B |
2.5 hours |
– |
6 hours |
– |
– |
30 |
1.08 g/cc |
– |
Translucent |
– |
– |
– |
550 % |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
|
›Super Instant™
|
Light Paste |
1A:1B |
– |
2.5 minutes |
10 minutes |
16 hours |
60 |
– |
– |
1.17 g/cc |
– |
Clear Amber |
– |
1,100 psi |
– |
10+ % |
– |
– |
– |
– |
– |
27,000 psi |
– |
– |
4,500 psi |
115,000 psi |
|
›URE-BOND™ 90
|
6,500 cps |
1A:1B |
100A:88B |
8 minutes |
4 hours |
16 hours |
– |
90 |
– |
1.11 g/cc |
25 cu. in./lb. |
Amber |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
Polymer Modifiers for Concrete and Gypsum ›
Product Name |
Mixed Viscosity |
Mix Ratio By Volume |
Mix Ratio By Weight |
Pot Life |
Cure Time |
Specific Volume |
Color |
Tensile Strength |
Ultimate Tensile |
Compressive Strength |
Flexural Strength |
Useful Temperature (max) |
Density |
Ultimate Flexural |
Impact Resistance |
Coefficient of Thermal Expansion |
Water Vapor Diffusion Coefficient |
Freeze / Thaw Resistance |
Water Absorption |
Flexural Strength on 6 ply / 10 oz. Laminate |
|
›duoMatrix™ NEO
|
Variable |
100A:50B |
100A:50B |
30 minutes |
90 minutes |
17.45 cu. in./lb. |
White |
3300-5500 psi |
– |
6500-9500 psi |
7500-9800 psi |
200 °F |
– |
– |
– |
– |
– |
– |
– |
– |
|
›duoMatrix™-C
|
Variable |
– |
– |
90 minutes |
16 hours |
1.06 cu. in./lb. |
– |
900 psi |
– |
13,000 psi |
5,000 psi |
– |
– |
– |
– |
– |
– |
– |
– |
– |
|
›duoMatrix™-G
|
Variable |
– |
100 Parts Gypsum + 50 Parts C-1 Latex + 10 Parts C-2 Resin + 0.5 Parts C-3 Hardener |
60 minutes |
120 minutes |
17.45 cu. in./lb. |
Bright White |
3300-5500 psi |
– |
6500-9500 psi |
7500-9800 psi |
200 °F |
– |
– |
– |
– |
– |
– |
– |
– |
|
›Forton™ VF-774
|
100,300 cps |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
|
›Forton™ MG
|
Variable |
– |
– |
30 minutes |
90 minutes |
– |
Bright White |
– |
3500 - 5100 psi |
6000 - 9000 psi |
– |
200 °F |
95 - 100 lb/ft³ |
3500 - 9400 psi |
170 in lb / in² |
11.1x10-6 in/in/℉ |
250 mµ |
300 cycles |
0.8 ‰ after 24 hour water soak |
– |
|
›Forton™ MG Sculptor Kit
|
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
|
›Forton™ VF-812
|
Variable |
– |
– |
– |
90 minutes |
– |
Bright White |
– |
5,100 psi |
9,000 psi |
– |
200 °F |
– |
– |
– |
– |
– |
– |
– |
– |
|
›Matrix Dryve™
|
Variable |
3 Parts Powder : 1 Part Water By Volume |
100 Parts Powder : 27 Parts Water by Weight |
20 minutes |
90 minutes |
17.45 cu. in./lb. |
White |
3300 - 5500 psi |
– |
6500 - 9500 psi |
– |
200 °F |
99 lbs lb/ft³ |
– |
175 in lb / in² |
– |
– |
300 cycles |
0.5 ‰ after 24 hour water soak |
7500 - 9800 psi |
|
›Matrix™ Chopped Glass
|
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
|
›Matrix™ Accelerator
|
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
|
›Matrix™ Retarder
|
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
|
›Matrix™ Thickener
|
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
– |
Polysulfide Rubber ›
Product Name |
Mixed Viscosity |
Mix Ratio By Weight |
Pot Life |
Cure Time |
Shore A Hardness |
Specific Gravity |
Specific Volume |
Color |
Tensile Strength |
Elongation @ Break |
100% Modulus |
Shrinkage |
|
›FMC™ 200
|
6,000 cps |
100A:12B |
50 minutes |
16 hours |
20 |
1.35 g/cc |
20.5 cu. in./lb. |
Black |
157 psi |
700 % |
29 psi |
negligible in. / in. |
|
›FMC™ 201
|
6,000 cps |
100A:12B |
50 minutes |
16 hours |
15 |
1.35 g/cc |
20.5 cu. in./lb. |
Black |
150 psi |
700 % |
29 psi |
negligible in. / in. |
|
›FMC™ 205
|
6,000 cps |
100A:12B |
90 minutes |
16 hours |
12 |
1.38 g/cc |
20.1 cu. in./lb. |
Black |
60 psi |
550 % |
15 psi |
Negligible in. / in. |
Lifecasting Materials ›
Product Name |
Mixed Viscosity |
Mix Ratio By Volume |
Mix Ratio By Weight |
Pot Life |
Cure Time |
Shore A Hardness |
Specific Gravity |
Specific Volume |
Color |
Die C Tear Strength |
Tensile Strength |
Elongation @ Break |
Shrinkage |
|
›Alja-Safe™
|
Variable |
1 Part Warm Water (80° F / 27° C) to 1 Part Alja-Safe Powder |
4 Parts Warm Water (80° F / 27° C) to 1 Part Alja-Safe Powder |
5 minutes |
8 minutes |
– |
– |
26 cu. in./lb. |
Light Purple |
– |
– |
– |
– |
|
›Alja-Safe™ Acrobat
|
Variable |
1 Part warm water (80° F / 27° C) to 1 Part Alja-Safe Acrobat® powder |
3 parts water to 1 part Acrobat® by weight |
5 minutes |
8 minutes |
– |
– |
26 cu. in./lb. |
Off White |
– |
– |
– |
– |
|
›Alja-Safe™ Breeze
|
Variable |
5 Parts Warm Water (80° F / 27° C) to 1 Part Alja-Safe Breeze liquid |
– |
3 minutes |
8 minutes |
– |
– |
26 cu. in./lb. |
Blue |
– |
– |
– |
– |
|
›Body Double™ Fast Set
|
Brushable |
1A:1B |
1A:1B |
90 seconds |
7 minutes |
25 |
1.17 g/cc |
23.7 cu. in./lb. |
Aqua, Green |
40 pli |
450 psi |
500 % |
<.001 in. / in. |
|
›Body Double™ SILK
|
Brushable |
1A:1B |
1A:1B |
6 minutes |
20 minutes |
25 |
0.91 g/cc |
30.4 cu. in./lb. |
Green |
– |
– |
– |
<.001 in. / in. |
|
›Body Double™ Standard Set
|
Brushable |
1A:1B |
1A:1B |
5 minutes |
20 minutes |
25 |
1.17 g/cc |
23.7 cu. in./lb. |
Purple |
40 pli |
525 psi |
500 % |
<.001 in. / in. |
Disclaimer
Although we do our best to ensure accuracy, Smooth-On offers no warranties, promises, and/or representations of any kind, either expressed or implied, as to the accuracy, completeness, or reliability of the information contained in these sortable charts, nor suitability of the information contained herein to your particular circumstances. Smooth-On assumes no liability for losses or damages of whatever nature (direct, indirect, consequential or other) associated with your use, or inability to use, the sortable charts, or from your use (or failure to use) the information contained herein. Other useful tools include
product technical bulletins and our
extensive FAQ section. You can also
contact our technical support team.